Organic-inorganic antibacterial and antifouling interior wall paint and preparation method thereof

An inorganic antibacterial and interior wall coating technology, applied in the field of coatings, can solve the problems of inorganic coatings that do not have crack resistance and adhesion, and achieve super strong adhesion, not easy to pulverize, and good scrub resistance

Active Publication Date: 2021-10-29
ZIBO VOCATIONAL INST
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This patent uses modified fluorocarbon emulsion and pure acrylic emulsion as film-formers, which belong to organic coatings and have the self-cleaning and antifouling properties of organic coatings, but do not have the anti-cracking, super-adhesive, and non-easy properties of inorganic coatings. Powdering, not easy to generate static electricity, long service life and other excellent characteristics; in addition, the patent uses antibacterial additives and antifungal agents to make the coating antifungal, and does not take slow release measures

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Organic-inorganic antibacterial and antifouling interior wall paint and preparation method thereof
  • Organic-inorganic antibacterial and antifouling interior wall paint and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] Organic-inorganic antibacterial antifouling interior wall paint is prepared according to the following steps:

[0041] 1. Inorganic hybrid perfluorocarbon modified acrylate self-emulsifying emulsion, the number of parts by mass is 80 parts, and the preparation steps are as follows:

[0042] (1) Add 40 parts of perfluoro-n-propyl vinyl ether SF-000360, 80 parts of butyl acrylate, and 4 parts of acrylic acid into the reaction kettle, stir and mix to obtain a mixed monomer;

[0043] (2) Add 600 parts of deionized water, 3 parts of acrylic polyether phosphate APE-2005, 3 parts of polyether nonionic emulsifier ONIST AE-100 containing double bonds, and 3 parts of sodium persulfate-sodium bisulfite Into the reaction kettle, feed nitrogen, turn on the electric mixer to stir, pre-emulsify for 0.5 hours, and raise the temperature to 60°C to obtain a pre-emulsion;

[0044] (3) Keep the pre-emulsion at 60°C, add the mixed monomer obtained in step (1) dropwise to the pre-emulsion o...

Embodiment 2

[0060] Organic-inorganic antibacterial antifouling interior wall paint is prepared according to the following steps:

[0061] 1. Inorganic hybrid perfluorocarbon modified acrylate self-emulsifying emulsion, the number of parts by mass is 50 parts, and the preparation steps are as follows:

[0062] (1) Add 10 parts of perfluoro-n-propyl vinyl ether SF-000360, 60 parts of butyl acrylate, and 2 parts of acrylic acid into the reaction kettle, stir and mix to obtain a mixed monomer;

[0063] (2) Add 200 parts of deionized water, 1 part of acrylic polyether phosphate APE-2005, 1 part of polyether nonionic emulsifier ONIST AE-100 containing double bonds, and 1 part of sodium persulfate-sodium bisulfite Into the reaction kettle, feed nitrogen, turn on the electric mixer to stir, pre-emulsify for 0.5 hours, and raise the temperature to 40°C to obtain a pre-emulsion;

[0064] (3) Keep the pre-emulsion at 40°C, add the mixed monomer obtained in step (1) dropwise to the pre-emulsion obta...

Embodiment 3

[0080] Organic-inorganic antibacterial antifouling interior wall paint is prepared according to the following steps:

[0081] 1. Inorganic hybrid perfluorocarbon modified acrylate self-emulsifying emulsion, the number of parts by mass is 60 parts, and the preparation steps are as follows:

[0082] (1) Add 20 parts of perfluoro-n-propyl vinyl ether SF-000360, 60 parts of butyl acrylate, and 5 parts of acrylic acid into the reaction kettle, stir and mix to obtain a mixed monomer;

[0083] (2) Add 200 parts of deionized water, 1 part of acrylic polyether phosphate APE-2005, 2 parts of polyether nonionic emulsifier ONIST AE-100 containing double bonds, and 1 part of sodium persulfate-sodium bisulfite Into the reaction kettle, feed nitrogen, turn on the electric mixer to stir, pre-emulsify for 0.8 hours, and raise the temperature to 50°C to obtain a pre-emulsion;

[0084] (3) Keep the pre-emulsion at 50°C, add the mixed monomer obtained in step (1) dropwise to the pre-emulsion obt...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of coatings, in particular to an organic-inorganic antibacterial and antifouling interior wall coating and a preparation method thereof. Inorganic hybrid perfluorocarbon modified acrylate self-emulsifying emulsion, zeolite-loaded silver, silica gel-loaded silver, functional filler, calcined kaolin, wollastonite powder, lime calcium powder, Tuyile HD‑20 dispersant, Tuyile inorganic powder DS‑ 195 dispersant, 2,4,7,9-tetramethyl-5-decyne-4,7-diol, deionized water. The invention uses inorganic hybrid perfluorocarbon modified acrylate self-emulsifying emulsion as the base material, and uses zeolite silver-loaded and silica gel-loaded silver as composite inorganic antifungal agents, so that the coating has the chemical corrosion resistance, flame retardancy and fire prevention of inorganic coatings , green and environmental protection characteristics and the advantages of strong adhesion and good scrub resistance of organic coatings ensure that the coatings are safe and non-toxic, have excellent anti-mildew properties, and have a long effective period of anti-mildew.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to an organic-inorganic antibacterial and antifouling interior wall coating and a preparation method thereof. Background technique [0002] In recent years, with the high-level development of my country's economy, people's quality of life has improved significantly, and people have paid more and more attention to a safe, healthy and comfortable indoor environment. Interior wall coatings have been recognized by the public due to their advantages such as convenient construction and environmental friendliness. With the refinement of coating functions, more and more people have higher requirements for interior wall coatings: [0003] One is environmental friendliness. At the present stage, my country has entered a critical period of providing more high-quality ecological products to meet the people's growing needs for a beautiful ecological environment. It is imperative to develop an...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D133/08C09D5/08C09D5/18C09D5/14C09D7/61C09D7/63C09D1/04C09D1/00
CPCC08K2003/2241C08K2201/011C09D1/00C09D1/04C09D5/08C09D5/14C09D5/18C09D133/064C09D7/61C09D7/63C08K13/06C08K9/12C08K3/346C08K3/34C08K3/22C08K5/053C08K7/26
Inventor 曲园园
Owner ZIBO VOCATIONAL INST
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com