Composite 3D printing material containing coffee grounds as well as preparation method and application of composite 3D printing material

A 3D printing and coffee grounds technology, applied in the field of additive manufacturing, can solve problems such as clogged nozzle printing, materials that cannot be printed, failures, etc.

Active Publication Date: 2021-08-31
张晓军
View PDF12 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition, the melt index, impurities, and crystallization points of the material may cause the material to be unable to print. Therefore, when there are other solid particles such as wood, coffee grounds, copper powder, and aluminum powder in the 3D composite printing material, uniform dispersion is the most critical and difficult. One of the problems to be solved; if the above solid particles cannot be dispersed evenly to form an agglomeration reaction, the agglomeration position of the solid material will form the followi

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Composite 3D printing material containing coffee grounds as well as preparation method and application of composite 3D printing material
  • Composite 3D printing material containing coffee grounds as well as preparation method and application of composite 3D printing material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] The composite 3D printing material of this embodiment is made of the following raw materials in parts by weight: 20 parts of modified coffee grounds, 80 parts of polylactic acid, 3 parts of polycaprolactone, 20 parts of polyhydroxyalkanoate and 2 parts of plasticizer ; Wherein, the modified coffee grounds is obtained by modifying the coffee grounds raw material with a mixed solution containing water-soluble polyester and coupling agent, and the water-soluble polyester includes the first water-soluble polyester (purchased from Henan Xingguang Resin Co., Ltd. ) and the second water-soluble polyester (Korean water-soluble polyester SK375), the coupling agent is a titanate coupling agent, and the plasticizer is DOP.

[0036] The preparation steps of the above composite 3D printing materials are as follows:

[0037] 1. Coffee grounds pretreatment

[0038]Screen the collected coffee grounds to remove impurities such as non-coffee grounds, and then use vacuum equipment for pr...

Embodiment 2

[0046] The composite 3D printing material of this embodiment is made of the following raw materials in parts by weight: 35 parts of modified coffee grounds, 65 parts of polylactic acid, 2 parts of polycaprolactone, 15 parts of polyhydroxyalkanoate and 1 part of plasticizer Among them, the modified coffee grounds are obtained by modifying the raw material of coffee grounds with a mixed solution containing water-soluble polyester and a coupling agent, the water-soluble polyester is water-soluble polyester SK375, and the coupling agent is titanate coupling agent, the plasticizer is DOP.

[0047] The preparation steps of the above composite 3D printing materials are as follows:

[0048] 1. Coffee grounds pretreatment

[0049] Screen the collected coffee grounds to remove impurities such as non-coffee grounds, and then use vacuum equipment for preliminary drying; mix the dried coffee grounds evenly, and then use a grinder to grind the coffee grounds into powder, with a particle si...

Embodiment 3

[0057] The composite 3D printing material of this embodiment is made of the following raw materials in parts by weight: 45 parts of modified coffee grounds, 55 parts of polylactic acid, 4 parts of polycaprolactone, 25 parts of polyhydroxyalkanoate and 3 parts of plasticizer Among them, the modified coffee grounds are obtained by modifying the raw material of coffee grounds with a mixed solution containing water-soluble polyester and coupling agent. The water-soluble polyester is purchased from Henan Xingguang Resin Co., Ltd., and the coupling agent is silane coupling Agent KH570, the plasticizer is epoxy soybean oil.

[0058] The preparation steps of the above composite 3D printing materials are as follows:

[0059] 1. Coffee grounds pretreatment

[0060] Screen the collected coffee grounds to remove impurities such as non-coffee grounds, and then use vacuum equipment for preliminary drying; mix the dried coffee grounds evenly, and then use a grinder to grind the coffee groun...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Login to view more

Abstract

The invention provides a composite 3D printing material containing coffee grounds as well as a preparation method and application of the composite 3D printing material. The composite 3D printing material is prepared from the following raw materials in parts by weight: 10 to 55 parts of modified coffee grounds, 45 to 90 parts of polylactic acid, 1 to 5 parts of polycaprolactone, 10 to 30 parts of polyhydroxyalkanoate and 1 to 3 parts of plasticizer, wherein the modified coffee grounds are obtained by modifying coffee grounds raw materials with a mixed solution containing water-soluble polyester and a coupling agent. According to the method, high-value utilization of the waste coffee grounds can be achieved, environment protection is facilitated, meanwhile, the cost of consumables is greatly reduced, and remarkable social benefits and economic benefits are achieved; and in addition, the composite 3D printing material containing the coffee grounds can well meet the functional requirements of daily 3D printing, the comprehensive performance of printed products is excellent, and the application range is wide.

Description

technical field [0001] The invention relates to the technical field of additive manufacturing, in particular to a composite 3D printing material containing coffee grounds and its preparation method and application. Background technique [0002] Coffee is a drink made from roasted and ground coffee beans, and it is the main drink popular in the world along with cocoa and tea. The world consumes at least 400 billion cups of coffee every year. If a cup of freshly ground coffee of 350 ml produces about 20 grams of coffee grounds, it will produce 8 million tons of coffee grounds a year; taking a bag of rice of 25 kg as an example, The world produces at least 320 million bags of waste coffee grounds a year. At present, most of the coffee grounds in the world are discarded, landfilled or incinerated together with other wastes. This cost-increasing treatment method will not only produce more greenhouse gases such as carbon dioxide and nitric oxide, but will also be The combustion ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L67/04C08L99/00C08L91/00C08K5/12C08H99/00B33Y70/10B33Y80/00
CPCC08L67/04C08H99/00B33Y70/10B33Y80/00C08L99/00C08K5/12C08L91/00Y02W90/10
Inventor 张晓军韩民峰贾玲玉何督督傅文军
Owner 张晓军
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap