A kind of mica composite material and preparation process of internally shortened fiber for new energy vehicles

A technology of new energy vehicles and composite materials, which is applied in the field of mica composite materials and preparation technology of internally shortened fibers for new energy vehicles, can solve the problems of low electrical strength of mica boards, and achieve high consistency of structural strength and electrical strength Effect of reducing dosage and improving thermal insulation performance

Active Publication Date: 2022-06-28
浙江荣泰电工器材股份有限公司
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In order to solve the problem of low electrical strength of the mica board existing in the related technical problems, the application provides a mica composite material and a preparation process of internally shortened fibers for new energy vehicles

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of mica composite material and preparation process of internally shortened fiber for new energy vehicles

Examples

Experimental program
Comparison scheme
Effect test

preparation example 1

[0051] Preparation example 1, preparing modified mica powder, modified mica powder is prepared from the following raw materials in parts by weight:

[0052] 0.60kg coarse grade mica, 1.80kg fine grade mica, 0.2kg tris hydrochloride, 0.04kg sodium hydroxide, 0.1kg dopamine hydrochloride.

[0053] The preparation of modified mica powder comprises the following steps:

[0054] b1, rinse the mica powder with deionized water, dry, and use a ball mill to grind the mica powder into coarse-grained mica of 250-550um and fine-grained mica of 74-150um;

[0055] b2, with 0.04kg sodium hydroxide and 0.2kg tris hydrochloride configuration pH is the tris hydrochloride buffer solution of 8.5, adds 0.1kg dopamine hydrochloride, is configured as dopamine solution, and 0.60 Pour kg of coarse-grained mica and 1.80 kg of fine-grained mica into the dopamine solution, stir with a high-speed mixer for 7 hours to prepare modified mica, take out the prepared modified mica, and dry.

preparation example 2

[0056] Preparation example 2, preparing unmodified mica powder, the difference between preparation example 2 and preparation example 1 is: the mica powder is rinsed with deionized water, dried, and the mica powder is ground into 250-550um coarse-grained mica and For 74-150um fine-grained mica, select 0.60kg of coarse-grained mica and 1.80kg of fine-grained mica.

preparation example 3

[0057] Preparation example 3, preparing modified aramid fiber, the modified aramid fiber is prepared from the following raw materials in parts by weight:

[0058] 0.8kg aramid fiber, 0.2kg sodium hydroxide, 0.05kg polyethylene oxide, 0.03kg sodium dodecylbenzenesulfonate.

[0059] The preparation of modified aramid fiber includes the following steps: cutting 0.8kg of aramid fiber to 3-5mm, putting 0.8kg of aramid fiber into 0.2kg of sodium hydroxide solution, adding 0.03kg of sodium dodecylbenzenesulfonate and 0.05kg polyethylene oxide, stir evenly with a mixer, the stirring speed is 100r / min, take it out after reacting for 30min, and dry it.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The application relates to the field of mica insulating materials, and specifically discloses a mica composite material and a preparation process of internal shortening fibers for new energy vehicles. The mica composite material includes 18-26 parts of modified mica powder, 6-12 parts of adhesive, 2-8 parts of modified ceramic powder, and 3-5 parts of modified aramid fiber; its preparation method is: to the modified mica powder, modified The adhesive is added to the permanent ceramic powder and the modified aramid fiber, mixed evenly, poured into the three-dimensional mold, stirred, and heated for molding. The mica composite material with internally shortened fibers for new energy vehicles of the present application can be used for battery protection of new energy vehicles, and it has the advantages of good compatibility between mica and reinforcing materials and high mechanical strength; in addition, the preparation method of the present application The invention has the advantages of integral molding of the prepared special-shaped three-dimensional mica, consistent electrical insulation effect of each point of the prepared special-shaped three-dimensional mica, and high electric strength.

Description

technical field [0001] This application relates to the field of mica composite materials, more specifically, it relates to a kind of mica composite material and preparation process of internally shortened fibers for new energy vehicles. Background technique [0002] Insulating material is the material that isolates the charged body from other parts in electrical equipment. It is an important guarantee for the long-term safe operation of electrical products, and it is also a key material that directly affects the advanced level of technical indicators of electrical products. Mica is a special sheet silicate mineral. Its crystal structure is a lamellar structure composed of two layers of silicon-oxygen tetrahedron sandwiching a layer of aluminum-oxygen octahedron. This structure determines its It has extremely high electrical insulation, and at the same time, it also has the characteristics of good peelability, chemical stability, reducibility and the ability to maintain the a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L63/00C08L51/10C08L77/10C08L61/32C08K9/08C08K3/34
CPCC08L63/00C08L2205/16C08K2201/014C08K2201/005C08L51/10C08L77/10C08L61/32C08K9/08C08K3/34