Preparation method of high-moisture-retention dry-state essence mask with temperature-sensitive absorption-promoting function

A technology to promote absorption and function, applied in the field of preparation of high moisturizing dry essence mask, can solve the problems of shedding, loss, loss of function, etc., and achieve the effect of preventing oxidation failure, increasing porosity, and promoting absorption

Pending Publication Date: 2022-04-01
贺文祯
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Yet the dry facial film that above-mentioned method obtains also has several defectives, for example:
[0005] (1) The essence substances attached to the surface of the mask base fabric through post-finishing methods do not have high bonding fastness with the mask base fabric, and are easy to fall off during processing, causing losses
[0006] (2) The essence is directly exposed on the surface of the mask, and it is easily oxidized by the air during storage and becomes invalid
Therefore, vacuum or air-filled packaging must be used to isolate the

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of high-moisture-retention dry-state essence mask with temperature-sensitive absorption-promoting function

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0037] Example 1

[0038] (A) Polypropylene fiber containing 25 wt% alkali-soluble polyester (PTA, amphimetaric acid-5-sulfate, EG and PEG600) containing 25 ml (The alkali-soluble polyester and polypropylene are often obtained) immersed in a 3 wt% aqueous sodium hydroxide solution, alkali reduction treatment at 70 ° C, after 2 hours, deionized water cleaning, 80 ° C Dry, obtain polypropylene fibers having porous structures (an average diameter 100 microns).

[0039] (B) The plasma treatment of a polypropylene fiber having a porous structure was taken for a plasma treatment for 10 min to obtain a surface hydroxy-modified polypropylene fiber under an oxygen atmosphere.

[0040] (C) The bath ratio is 1: 30 mL to impregnate the surface hydroxy-modified polypropylene fibers in the essence containing 6 wt% hyaluronic acid, after 1.5 h, remove excess liquid surface of the fiber, dried at 80 ° C, obtained Polypropylene fibers are loaded with essential substances.

[0041] (D) Shot treatment...

Example Embodiment

[0043] Example 2

[0044] (A) Polypropylene fibers containing 10 wt% alkali-soluble polyester (PTA, amphimic acid-5-sulfonate, EG and PEG600) containing 10% by weight In the 2 wt% aqueous sodium hydroxide aqueous solution, alkali reduction treatment was performed at 60 ° C, and after 0.5 h, the deionized water was cleaned, and the polypropylene fibers having a porous structure were obtained (an average diameter 150 microns). .

[0045] (B) Planted a polypropylene fiber having a porous structure under an oxygen atmosphere for 5 min to obtain a surface hydroxy-modified polypropylene fiber.

[0046] (C) Puzzle is immersed in a bath ratio of 1: 20 mL to impregnate the surface hydroxy-modified polypropylene fiber in the essence containing 5 wt% essence (2 wt% nicotinamide, 2 wt% hyaluronic acid, 1 wt% Snowstone). After 1 hours, the excess liquid of the fiber surface is removed, and the polypropylene fibers loaded with the essential substance is obtained at 80 ° C.

[0047] (D) Shot tre...

Example Embodiment

[0049] Example 3

[0050] (A) Polypropylene fiber containing 40 wt% alkali-soluble polyester (PTA, amphimethel terephthalic acid-5-sulfate, EG and PEG600) containing 40 wt% alkali-5-sulfate, EG and PEG600) In the 4 wt% aqueous sodium hydroxide aqueous solution, base reduction treatment was carried out at 80 ° C, after 3 hours, the deionized water was cleaned, and the polypropylene fibers having a porous structure were obtained at 80 ° C to obtain a polypropylene fiber having a porous structure (200 microns).

[0051] (B) A plasma treatment of polypropylene fibers having a porous structure for 15 min under the oxygen atmosphere, and obtains a surface hydroxy-modified polypropylene fiber.

[0052] (C) Puzzle-modified polypropylene fibers containing surface hydroxy-modified polypropylene fibers (2 wt% nicotinamide, 4 wt% hyaluronic acid, 2 wt% alternant sugar) In the essence, it is taken after 2 hours, and the excess liquid of the fiber surface is removed, and the polypropylene fiber...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Diameteraaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention relates to the field of cosmetics, and discloses a preparation method of a high-moisture-retention dry-state essence mask with a temperature-sensitive absorption-promoting function, and the preparation method comprises the following steps: (A) carrying out alkali decrement treatment on polypropylene fibers containing alkali-soluble polyester; (B) carrying out plasma treatment on the polypropylene fiber in an oxygen atmosphere; (C) dipping the polypropylene fiber into the essence; (D) spraying the finishing liquid on the polypropylene fiber, and carrying out heating crosslinking treatment to obtain the mask fiber with a skin-core structure; and (E) preparing the high-moisture-retention dry-state essence mask by taking the mask fiber as a raw material. The interior of the fiber in the mask is of a porous structure and can load essence substances, and meanwhile the surface of the fiber is provided with a temperature-sensitive gel skin layer. When the mask is stored in a dry state, the quality guarantee period can be effectively prolonged, and when warm water is added into the mask, the mask can quickly absorb water and promote release of essence substances after being applied to the skin surface.

Description

Technical field [0001] The present invention relates to the field of cosmetics, and more particularly to a method of preparing a high moisturizing dummy sequester mask having a warm-sensitive absorption function. Background technique [0002] Most of the mask on the existing market is mostly a wet mask containing extractive liquid, in a wet rich water environment, in order to avoid the essence of essence or oxidation in the essence, it is often necessary to add some preservatives or antibacterial agents. The anticorrosive and the biotechnic bioethic is poor, so it is easy to cause negative effects such as skin allergy after frequent use of the mask. The stem mask which is obtained on the mask base fabric in a donor form can solve the above problems. Since the dummy mask can be stored under dry conditions, the shelf life is also superior to the wet mask even if a preservative or acetactic agent is not added. [0003] At present, the preparation of the current dry mask is to prep...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): A61K8/85A61K8/81A61K8/73A61K8/67A61K8/63A61K8/60A61K8/64A61K8/02A61Q19/00D06M15/03D06M10/02D06M15/263D06M15/13D06M15/15D06M101/20
Inventor 贺文祯
Owner 贺文祯
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka