High-silicon content shell-core structured silicon/acrylic emulsion and method for preparing same

A core-shell structure and silicon-acrylic emulsion technology, which is applied in the field of high-silicon content core-shell structure silicon-acrylic emulsion and its preparation, can solve the problems of paint stain resistance, water resistance and weather resistance, and poor compatibility. Achieve good mechanical properties, good water resistance, and prevent hydrolysis

Inactive Publication Date: 2007-08-15
TONGJI UNIV
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] However, due to the hydrolyzability of organosiloxane monomers in the preparation of silicone-acrylic emulsions, the compatibility of organosilicon monomers and acrylate monomers is poor. The silicon content is usually less than 10%, which does not significantly improve the stain resistance, water resistance and weather resistance of the coating

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] The preparation of high-silicon-content core-shell structure silicon-acrylic emulsion refers to Table 2 (preparation formula of high-silicon content core-shell structure silicon-acrylic emulsion of the present invention). First, the seed emulsion was prepared according to the seed emulsion polymerization formula 1 in Table 2. Pre-emulsify the mixed monomers (methyl methacrylate, butyl acrylate, acrylic acid, vinyltrialkoxysilane), emulsifier OS and deionized water under strong stirring in a one-necked flask to obtain a pre-emulsion. Add deionized water, protective gel and hydrolysis inhibitor into the three-necked flask, stir and raise the temperature to 85°C. Put the emulsion in the dropping funnel, put the aqueous solution containing the pH adjuster and the initiator in another dropping funnel, and slowly drop the two liquids into the three-necked flask under the condition of stirring, and the dripping will be completed in about two hours. Then keep warm for one hour...

Embodiment 2

[0032] According to the formula in Table 2, high-silicon content core-shell structure silicon-acrylic emulsion 2 was prepared. The preparation method is the same as in Example 1.

Embodiment 3

[0034] According to the formula in Table 2, high-silicon-content core-shell structure silicon-acrylic emulsion 3 was prepared. The preparation method is the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
degree of polymerizationaaaaaaaaaa
Login to View More

Abstract

The invention relates to a high-silicon content shell-core structured silicon / acrylic emulsion and method for preparation by using ethyltrimethoxysilane, acrylic acid and acrylic acid ester as monomer, peroxodisulfate as initiating agent, octyl phenol polyoxyethylene ether maleic ester sodium (OS) as emulsifying agent, sodium methacrylic acid as protection rubber, binary alcohol such as propylene glycol, or 1.4-butylene glycol or low-molecular-weight polyethylene glycol as organosilicon hydrolysis depressant, first carrying out seed (core) emulsion polymerization, then using the emulsion as seed, vinyl trialkoxy silicane and acrylic acid ester as monomer, ammonium persulphate as initiating agent, divinyl benzene as crosslinking agent, binary alcohol such as propylene glycol, or 1.4-butylene glycol or low-molecular-weight polyethylene glycol as organosilicon hydrolysis depressant, and carrying out emulsion polymerization.

Description

technical field [0001] The invention relates to a high-silicon-content core-shell structure silicon-acrylic emulsion and a preparation method thereof. Background technique [0002] In recent years, there have been many studies on silicone-modified polyacrylate emulsions (silicon-acrylic emulsions for short). Silicone acrylic emulsion is the raw material for preparing high-quality architectural exterior wall coatings. The purpose of the research is to improve the stain resistance, water resistance and weather resistance of polyacrylate emulsion coatings. [0003] There are two modification methods of blending and copolymerization for modifying polyacrylate with silicone. The blending method is to mix the two emulsions of organopolysiloxane and polyacrylate in a certain ratio evenly. This method has a simple process and has been applied in actual production; but in the blending modification, there is no chemical bond between the two polymer molecular chains. Due to the lar...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08F220/10C08F4/40C08F2/44C08F2/22
Inventor 王国建陈峰刘琳许乾慰
Owner TONGJI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com