Preparation of high-purity titanium biboride ceramic micropowder by using self-spreading high-temp. reduction synthesis process

A self-propagating high-temperature, titanium diboride technology, applied in the field of refractory compounds and their solid-phase synthesis, can solve the problems of long time, coarse product particle size, large powder particle size, etc., achieve low energy consumption and time consumption, and simple process , the effect of fine grain

Inactive Publication Date: 2002-03-27
WUHAN UNIV OF TECH
View PDF1 Cites 32 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The main disadvantages of this method: complex production equipment, high reaction temperature, long time, huge energy consumption, coarse grains of titanium diboride obtained, low boron content, poor product purity
Chinese patent CN105533A reports a carbon thermal reduction synthesis method of titanium diboride ceramic powder based on activated carbon as a reducing agent, ammonium pentaborate as a

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0015] Example 1: 27 grams of TiO 2 Powder (≤80μm), 26g B 2 o 3 Mg powder (≤120μm), 47 grams of Mg powder (≤200μm) are fully mixed. The mixed sample is pressed into a block blank, put into a self-propagating high-temperature synthesis reactor, and under the protection of argon gas at normal temperature and pressure, the surface of the sample is ignited with a tungsten wire or an electric arc. The combustion wave spreads rapidly. At this time, the combustion temperature of the sample is 1800-2000°C, and the combustion reaction is completed within 1-2 minutes. After the sample was completely cooled, it was placed in a ball mill for ball milling for 2 hours. The obtained powder was put into a reaction kettle, 10 liters of hydrochloric acid with a concentration of 1 mol / l was added and stirred continuously, acid washed at 50° C. for 4 hours, filtered and dried. The composition of the obtained micropowder is: Ti68.2wt%, B30.1wt%, O0.5wt%, N0.1wt%, Mg0.1wt%, and the average part...

example 2

[0016] Example 2: 29 grams of TiO 2 Powder (≤80μm), 26g B 2 o 3 Mg powder (≤120μm), 45 grams of Mg powder (≤200μm) are fully mixed. The mixed sample is pressed into a block blank, put into a self-propagating high-temperature synthesis reactor, and under the protection of argon gas at normal temperature and pressure, the surface of the sample is ignited with a tungsten wire or an electric arc. The combustion wave spreads rapidly. At this time, the combustion temperature of the sample is 2000-2200°C, and the combustion reaction is completed within 1-2 minutes. After the sample was completely cooled, it was placed in a ball mill for ball milling for 2 hours. The obtained powder was put into a reaction kettle, 20 liters of sulfuric acid with a concentration of 0.5 mol / l was added and stirred continuously, acid washed at 50° C. for 6 hours, filtered and dried. The composition of the obtained micropowder is: Ti68.8wt%, B30.35wt%, O0.7wt%, N0.1wt%, Mg0.05wt%, and the average part...

example 3

[0017] Example 3: 29 grams of TiO 2 Powder (≤80μm), 28g B 2 o 3 Mg powder (≤1200μm), 43 grams of Mg powder (≤200μm) are fully mixed. The mixed sample is pressed into a block blank, put into a self-propagating high-temperature synthesis reactor, and under the protection of argon gas at normal temperature and pressure, the surface of the sample is ignited with a tungsten wire or an electric arc. The combustion wave spreads rapidly. At this time, the combustion temperature of the sample is 1700-1900°C, and the combustion reaction is completed within 1-2 minutes. After the sample was completely cooled, it was placed in a ball mill for ball milling for 2 hours. The obtained powder was put into a reaction kettle, 10 liters of hydrochloric acid with a concentration of 1 mol / l was added and stirred continuously, acid washed at 50° C. for 4 hours, filtered and dried. The composition of the obtained micropowder is: Ti67.87wt%, B31.3wt%, O0.6wt%, N0.1wt%, Mg0.13wt%, and the average p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The preparation method of high-purity TiB2 ceramic micropowder uses active metal reducing agent and cleap oxide raw material, and adopts the following steps: uniformly mixing TiO2, B2O3 and metal Mg powder, die-pressing and forming, placing the above-mentioned obtained material in a self-spreading high-temp. synthesis equipment with argon protection at normal temp. and normal pressure, lighting to make combustion, breaking combustion product, pickling so as to obtain the invented high-purity TiB2 ceramic micropowder. As compared with traditional carbon thermal reduced TiB2 ceramic powder saidinvention possesses the advantages of high purity, fine crystal grain, simple process and low energy consumption and time consumption, and as compared with SHS simple substance synthetic TiB2 ceramicpowder it is low in production cost.

Description

technical field [0001] The invention relates to a refractory compound and a solid phase synthesis method thereof. Background technique [0002] Titanium diboride ceramic powder is an important new type of engineering ceramic raw material. Its important physical and chemical properties include: high melting point (>3000°C), high hardness (>30GPa), high chemical stability, and high thermal conductivity. (120W / mK), high modulus (>570GPa), excellent electrical conductivity. Mainly used in: hard tool materials, composite material additives, new heating elements (>1800°C), high-temperature inert electrodes (>1200°C), high-temperature wear-resistant electrodes, high-temperature corrosion-resistant electrodes, high-strength lead frames for large-scale integrated circuits materials etc. But high purity TiB 2 The high price of raw materials limits the large-scale development and application of such materials. The traditional synthesis process of titani...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B35/515C04B35/58C04B35/65
Inventor 傅正义王为民王皓
Owner WUHAN UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap