Cold construction adhesive for waterproof rolled sheet

A waterproof membrane and production method technology, applied in the direction of adhesive types, ester copolymer adhesives, hydrocarbon copolymer adhesives, etc., can solve the problem of weak construction bonding, heavy pollution, and non-aging resistance problems, achieve the effect of excellent chemical comprehensive performance index, convenient construction and strong adhesive force

Inactive Publication Date: 2007-06-06
XI NIU PI WATERPROOFING TECH CO LTD
View PDF1 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The construction methods are mostly hot-melt construction or oily ointment, oily base oil, and polymer glue bonding, which has high energy consumption, danger, large environmental pollution, and wet base surface construction is not firm; use polyvinyl alcohol latex cement Adhesives and other polymer latex cement adhesives bond waterproof membranes, which have a series of problems such as not being resistant to hydrolysis, not being resistant to aging, and being delaminated with the old base surface.
[0003] Chinese patent ZL 01109850.3 discloses a cold adhesive made of 30-40 parts by weight of asphalt, 2-5 parts by weight of ethylene-propylene copolymer, 20-56 parts by weight of 90# gasoline or 120# solvent oil, which contains a large amount of solvent , can only be used for the construction bonding of modified asphalt waterproofing membrane, and the wet base surface and uneven base surface cannot be constructed
The coiled material disclosed in US Patent SU 383724 is made by mixing melted ethylene propylene rubber particles with asphalt that has been preheated to 160-180°C and added with shale tar. High energy consumption, cumbersome operation and unsafe

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] Embodiment 1, weighing 375 kilograms of styrene-acrylic polymer water-based latex, 500 kilograms of pure acrylic polymer water-based latex, benzenesulfonate water reducer: 25 kilograms, 10% polyvinyl alcohol solution, 10% polyvinyl alcohol solution The preparation method is to add polyvinyl alcohol with a degree of polymerization of 2500 to 2600 into the reactor, add measured water, add a certain amount of powdered polyvinyl alcohol while heating up and stir, until boiling, then keep the temperature at 95 to 100°C for about 2 hours, and take out the material Observe that polyvinyl alcohol is completely dissolved in water to form a colorless transparent slurry, which can be cooled below 60°C and discharged for later use, and then the raw materials are water-based latex, water reducer, cellulose and 8-15% of the mass fraction according to the above formula. The polyvinyl alcohol aqueous solution is put into a stirring mixing tank according to the specified ratio, stirred f...

Embodiment 2

[0024] Embodiment 2, weighing 400 kilograms of styrene-acrylic polymer water-based latex, 455 kilograms of pure acrylic polymer water-based latex, benzenesulfonate water reducer: 25 kilograms, 8% polyvinyl alcohol solution: 8% polyvinyl alcohol solution The preparation method is to add polyvinyl alcohol with a degree of polymerization of 2500 to 2600 into the reactor, add measured water, add a certain amount of powdered polyvinyl alcohol while heating up and stir, until boiling, then keep the temperature at 95 to 100°C for about 2 hours, and take out the material Observe that polyvinyl alcohol is completely dissolved in water to form a colorless transparent slurry, which can be cooled below 60°C and discharged for later use, and then the raw materials are water-based latex, water reducer, cellulose and 8-15% of the mass fraction according to the above formula. The polyvinyl alcohol aqueous solution is put into a stirring mixing tank according to the specified ratio, stirred for...

Embodiment 3

[0025] Example 3, weighing 400 kilograms of styrene acrylate copolymerized water-based latex, 455 kilograms of pure acrylic polymer water-based latex, amide / imide type water reducing agent: 25 kilograms, 15% polyvinyl alcohol solution: 15% polyvinyl alcohol solution: The preparation method of vinyl alcohol solution is to add polyvinyl alcohol with a degree of polymerization of 2500-2600 into the reactor, add measured water, add a certain amount of powdered polyvinyl alcohol while heating up, stir, until boiling, and then keep the temperature at 95-100 ° C for about 2 hours , take the material and observe, the polyvinyl alcohol is completely dissolved in water to form a colorless transparent slurry liquid, then the material can be cooled below 60°C and discharged for later use, and then the raw materials water-based latex, water reducer, cellulose and mass fraction of 8- 15% polyvinyl alcohol aqueous solution is put into a stirring and mixing tank according to a specified ratio,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
flexural strengthaaaaaaaaaa
quality scoreaaaaaaaaaa
Login to View More

Abstract

The present invention discloses one kind of adhesive for composite waterproof rolled sheet product and its production process. The adhesive consists of water-thinned latex or water soluble glue powder, water reducing agent, cellulose and additive. It has high adhesion effect, wide use range, high strength, waterproof function, and may be used in the construction of modified waterproof asphalt rolled sheet and polymer sheet with fabric on the surface of new and old concrete and in the repair and waterproof sealing of concrete.

Description

technical field [0001] The invention relates to a building waterproof material, in particular to an adhesive glue used in the construction of a modified asphalt waterproof coiled material or a polymer sheet product with a fabric layer and a production method thereof. technical background [0002] At present, asphalt waterproof membrane or polymer sheet with fabric layer can be produced in a factory and is easy to use, so it is used more and more in construction, especially in roof construction. The modified asphalt membrane with adhesive One side of the adhesive is directly pasted to the concrete surface to achieve the purpose of waterproofing. However, it is not easy to achieve the effects of good waterproof performance, high bonding strength, aging resistance and motion deformation resistance of the adhesive. The waterproof membranes currently seen are mainly modified asphalt waterproof membranes and polymer sheets. The construction methods are mostly hot-melt constructi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J125/14C09J133/08C09J131/04
Inventor 卢桂才伍盛江
Owner XI NIU PI WATERPROOFING TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com