Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Method for making bamboo fiber

A bamboo fiber and bamboo fiber technology, applied in the field of bamboo fiber preparation, can solve the problems of high fiber lignin content, low extraction efficiency, and unsuitable large-scale production, and achieve high fiber strength, good toughness, good gloss and elastic effect

Inactive Publication Date: 2008-10-01
临安力源竹纤维技术开发有限公司
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing bamboo fiber preparation methods do not involve the spinnable bamboo fiber manufacturing process and method, and the made bamboo fiber is limited by the bamboo joints, and the fiber lignin content is high, and the fiber fineness, strength and toughness cannot reach the level of textile yarn. Line requirements, and special high-pressure equipment is required, the extraction efficiency is not high, and large-scale production cannot be formed

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for making bamboo fiber

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0010] Embodiment 1: choose 1-year-old Cizhu as raw material, cut off by bamboo joints, split into bamboo slices, put the bamboo slices on the heating furnace and bake for 3 minutes, and use the bamboo fiber separation equipment to make the baked bamboo slices under thermal stress And under the action of external mechanical force, large denaturation and large strain will occur, so that the "transverse stress" on the bamboo fiber is greater than the bonding force between the bamboo fibers, directly separate and extract the thick bamboo fiber, and then soak the thick bamboo fiber in 60 ℃ hot water Take it out for 8 hours to dry until 70% dry, then use mechanical methods to further soften and separate bamboo fibers and remove impurities. Then put it into the cooking tank, add 1% sodium hydroxide 5g / liter, sodium silicate 1%, sodium tripolyphosphate 0.5%, sodium sulfide 0.5%. # Softening solution, bath ratio 20, pressurized 1kg / cm 2 Cook under conditions, and keep the temperature...

Embodiment 2

[0011] Embodiment 2: Choose 1-year-old Cizhu as raw material, cut it into bamboo slices according to the standard bamboo joints, put about half of the bamboo slices on the heating furnace and bake until the green bamboo turns gray, and fix the baked bamboo slices on the workbench And at the 2cm place near the end of the bamboo, use a sharp knife to scratch the inner layer of the bamboo slice (just cut through the bamboo yellow layer), then use the bamboo hemp clamp to clamp the part of the bamboo slice and pull it back, and then separate the inner layer of the bamboo yellow. At the same time, the bamboo body is processed into fine and velvet fibers, and the clamping and pulling process is repeated. After one end of the whole bamboo chip is processed, the other half of the bamboo chip is put on the heating furnace to bake, and the separated bamboo fiber is wrapped around On the fixed column, pull the other end back with your hand. After the bamboo and hemp processing is complete...

Embodiment 3

[0012] Embodiment 3: select 1-2 year old green bamboo as raw material, saw off according to 3 standard bamboo joints, remove the green bamboo, put the bamboo tube on the heating furnace and bake for 3 minutes, and use the bamboo fiber separation and extraction equipment to make the baked bamboo tube Bamboo fiber is separated and crude bamboo fiber is extracted. Then soak the thick bamboo fiber in hot water at 60°C for 24 hours, take it out and let it dry until 70% dry, and use mechanical methods to further soften and separate the bamboo fiber and remove impurities. Then put it into the cooking tank, add sodium hydroxide 20g / liter, sodium carbonate 40g / liter, sodium silicate 3%, sodium tripolyphosphate 2%, sodium sulfide 2% 1 # The softening liquid has a bath ratio of 25, and the temperature is kept at 100°C, steamed and boiled under normal pressure for 5 hours, washed and dried, and then fermented with enzyme preparation for 7 days to be taken out. Put in 2% sodium hydroxide ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention is preparation process of bamboo fiber, including coarse bamboo fiber, refined bamboo fiber and spinnable bamboo fiber. The coarse bamboo fiber is prepared through cutting bamboo, separating bamboo fiber, steaming inside the No. 1 softening liquid and enzyme fermentation; the refined bamboo fiber is prepared through steaming inside the No. 2 softening liquid, enzyme fermentation, rinsing and bleaching, acid treatment, and oil soaking and drying; and the spinnable bamboo fiber is prepared through emulsifying, initial carding, combing and drawing. The bamboo fiber has lignin content lower than 5 %, and has the features of being natural and green, high in strength, high toughness, high brightness and high elasticity.

Description

technical field [0001] The invention relates to a method for preparing fibers, in particular to a method for preparing bamboo raw fibers. Background technique [0002] Bamboo is the second largest forest resource in the world. The bamboo forest area in the world is about 20 million hectares, and it is widely distributed, from tropical to subtropical, temperate and even frigid regions. Due to the rapid growth and high economic value of bamboo, a large number of artificial bamboo forests have appeared all over the world. my country is rich in bamboo plant resources, ranking first in the Asia-Pacific region in terms of both the type and area of ​​bamboo. There are about 40 genera and more than 400 species of bamboo in my country. The bamboo forest area is about 7 million hectares, accounting for about 35% of the world's bamboo forest area and 58% of the Asia-Pacific region. [0003] Bamboo fiber is made of natural bamboo, which is a real environmental protection fiber. The ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D01B1/10D01C1/02B27L11/08
Inventor 姚文斌张蔚倪进中
Owner 临安力源竹纤维技术开发有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com