Watersoluble fluor resin non-stick paint and manufacture method thereof

A non-stick coating, water-based fluorine technology, applied in coatings, devices for coating liquid on the surface, special surfaces, etc., can solve the problem of less products and achieve good temperature dispersion area, good fullness, and high hardness.

Inactive Publication Date: 2010-03-24
TIANJIN COLOROAD COATING & CHEM
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, non-stick coatings are only in the research and development stage in my country, and there are few products, especially water-based non-stick coatings are only in the exploration stage and are far from meeting domestic demand.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0070] (1) Synthetic acrylic water-based resin:

[0071] Process: Add xylene solvent and 20 parts of mixed monomers, pass nitrogen gas, heat up to 100°C, add various monomers and some initiator dibenzoyl peroxide (BPO) dropwise, keep warm for 1 hour, add dropwise Keep the remaining initiator at high temperature (130°C) for 3 hours, measure the conversion rate (99%), remove the solvent, remove the solvent under negative pressure, lower the temperature, add DC-3AD modified polysiloxane surfactant, and add deionized water , stir to disperse, control the solid content, filter and pack for later use. The ratio of the main raw material mixed monomers: 55 parts of methyl methacrylate, 25 parts of methacrylic acid, 5 parts of acrylic acid, 15 parts of 2-ethylhexyl acrylate, and 9 parts of methacrylamide.

[0072] (2) Modified polytetrafluoroethylene (PTFE) water-based resin

[0073] Process: Add 30 parts of polytetrafluoroethylene (PTFE) water-based resin, start stirring, add the de...

Embodiment 2

[0077] (1) Synthetic acrylic water-based resin:

[0078] Process: Add butyl acetate solvent and 30 parts of mixed monomers, blow nitrogen gas → raise the temperature to 100°C → add various monomers and part of the initiator di-tert-amyl peroxide (DTAP) dropwise → keep warm for 1h → Add the remaining initiator dropwise → keep high temperature (130°C) for 3 hours → measure the conversion rate (96%) → desolventize → negative pressure desolventize → lower the temperature → add DP-518 dispersant surfactant → add deionized water → stir Disperse → control solid content → filter and pack for later use. The proportion of the main raw material mixed monomer: 40 parts of methyl methacrylate, 15 parts of methacrylic acid, 3 parts of acrylic acid, 12 parts of 2-ethylhexyl acrylate, and 5 parts of methacrylamide.

[0079] (2) Modified polytetrafluoroethylene (PTFE) water-based resin

[0080] Process: Add 60 parts of polytetrafluoroethylene (PTFE) water-based resin → start stirring, add th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
hardnessaaaaaaaaaa
hardnessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a waterborne fluororesin nonstick coating, which is formed by 40 to 70 portions of modified polyte-trafluoroethylene (PTFE) water base resin, 10 to 30 portions of high temperature resistance pigment, 1 to 5 portions of fluororesin additive, 1 to 5 portions of surfactant and 20 to 40 portions of antiwear filler. The waterborne fluororesin nonstick coating uses synthesis propylene acid water base resin for modifying trafluoroethylene PTFE water base resin, adopts acrylic acid fat second polymerization method and does not use an addition agent, the entire fluorine caprylate compound which is harmful to human body in the modification process; the modified resin forms mosaic and perforating network structure, has good temperature dispersing region, solves the problem ofthe adhesiveness of the coating and the base material and the problems of baking and cracking, thus improving the hardness of nonstick coating. The NU aqueous fluorine resin of the invention does notstick to coating, can be coated on the surfaces of a microwave oven, an electric cooker, a nonstick pan and an electromagnetic pan, etc. to play the roles of protecting the surfaces from being stuckwith food, and causing food and aluminum and other metals to be isolated.

Description

technical field [0001] The invention belongs to the technical field of coatings and production techniques thereof, and relates to a non-stick coating of fluorine-containing resin, more specifically a NU water-based non-stick coating of fluororesin and a preparation method thereof. Background technique [0002] Non-stick coating is a special coating whose coating surface is not easily adhered by other sticky substances or easily removed after adhesion. This kind of coating is widely used in household appliances, cooking utensils, automobiles, machinery, chemical industry and other industries due to its anti-adhesive properties such as extremely low surface energy, small friction coefficient and easy sliding. Since DuPont of the United States successfully developed polytetrafluoroethylene (PTFE) non-stick coatings in 1938, it developed PVDF (polyvinylidene fluoride resin) resin construction fluorine coatings in the 1960s. Fluorine-containing resins with functional groups. Fl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D127/18C09D5/02C09D7/12B05D5/08C09D133/12
Inventor 田铁梁李华宁孙振瀛姚学民李建杰乔衡张展王玉锁刘平孟昭晖王春廷邓长福邢达
Owner TIANJIN COLOROAD COATING & CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com