Composite electrode of high purity polyaniline nanometer line and method for preparing the same

A composite electrode and polyaniline technology, applied in capacitor electrodes, electrode shape/type, circuits, etc., can solve the problems of low product purity, low yield, complicated steps of pure nanowires, etc., and achieve high purity and simple process.

Inactive Publication Date: 2010-03-24
TIANJIN UNIV
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The advantage of the template polymerization method is that the yield of the product is high when the template used is suitable, but the disadvantage is that the product purity is low and the steps to obtain pure nanowires are complicated.
When non-template methods (interfacial polymerization and rapid mixing) were used, the obtained polyaniline nanowires were of high purity, with controllable diameter and length of the nanowires, but with low yields
The electrochemical polymerization method has high yield and is environmentally friendly, but it is easy to form a layer of polyaniline particles on the surface of the electrode during the polymerization process, so that the purity of the obtained polyaniline nanowires is not high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Composite electrode of high purity polyaniline nanometer line and method for preparing the same
  • Composite electrode of high purity polyaniline nanometer line and method for preparing the same
  • Composite electrode of high purity polyaniline nanometer line and method for preparing the same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] 0.629 g of polysulfone was dissolved in 6 mL of N,N-dimethylacetamide to obtain a N,N-dimethylacetamide solution containing 10% polysulfone. Then coat a film on the surface of the stainless steel electrode to control the thickness of the liquid film to 5 μm. Afterwards, the stainless steel electrode coated with polysulfone N, N-dimethylacetamide solution was quickly immersed in a coagulation bath (water) to complete phase inversion, and a polysulfone / stainless steel composite electrode was obtained. The polysulfone / stainless steel composite electrode was used as the working electrode, and another piece of stainless steel was used as the counter electrode. -1 Aniline and 1.00mol·L -1 Sulfuric acid was used as the electrolyte, and a cell voltage of 1.80V was used for electrolytic polymerization for 40 minutes to obtain polyaniline nanowires, the purity of which was 100%.

Embodiment 2

[0015] 1.415 g of polysulfone was dissolved in 6 mL of N,N-dimethylacetamide to obtain a N,N-dimethylacetamide solution containing 20% ​​polysulfone. Then coat a film on the surface of the stainless steel electrode to control the thickness of the liquid film to 100 μm. Afterwards, the stainless steel electrode coated with polysulfone N, N-dimethylacetamide solution was quickly immersed in a coagulation bath (water) to complete phase inversion, and a polysulfone / stainless steel composite electrode was obtained. The polysulfone / stainless steel composite electrode was used as the working electrode, and another piece of stainless steel was used as the counter electrode. -1 Aniline and 1.00mol·L -1 Sulfuric acid was used as the electrolyte, and a cell voltage of 1.80V was used for electrolytic polymerization for 40 minutes to obtain polyaniline nanowires, the purity of which was 100%.

Embodiment 3

[0017] 2.425 g of polysulfone was dissolved in 6 mL of N,N-dimethylacetamide to obtain a N,N-dimethylacetamide solution containing 30% polysulfone. Then coat a film on the surface of the stainless steel electrode to control the thickness of the liquid film to 150 μm. Afterwards, the stainless steel electrode coated with polysulfone N, N-dimethylacetamide solution was quickly immersed in a coagulation bath (water) to complete phase inversion, and a polysulfone / stainless steel composite electrode was obtained. The polysulfone / stainless steel composite electrode was used as the working electrode, and another piece of stainless steel was used as the counter electrode. -1 Aniline and 1.00mol·L -1 Sulfuric acid was used as the electrolyte, and a cell voltage of 1.80V was used for electrolytic polymerization for 40 minutes to obtain polyaniline nanowires, the purity of which was 100%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
diameteraaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a composite electrode which prepares polyaniline nano-wires with high purity and a method for preparing the composite electrode, which belongs to the technique for preparing polyaniline nano-wire materials. A substrate of the composite electrode is stainless steel, titanium, nickel, cobalt, aluminum, iron, copper, graphite or glassy carbon, and thin film of polysulfone, polyether sulfone, polyimide or polyether imide is compounded on the substrate. The method for preparing the composite electrode comprises following steps: dissolving the polysulfone, the polyether sulfone, the polyimide or the polyether imide in N, N-dimethylacetamide, N, N-dimethylformamide, N-methyl pyrrolidone, dimethyl sulfoxide or m-cresol, preparing even and transparent casting solution, coating the casting solution on the surface of a substrate electrode, then, rapidly dipping the electrode in coagulation bath to finish phase inversion, and obtaining the composite electrode. The method ofthe invention has the advantages that the composite electrode is used as a working electrode to prepare the polyaniline nano-wires, which solves the problem that polyaniline particles exist in the polyaniline nano-wires and increases the purity of the polyaniline nano-wires.

Description

technical field [0001] The invention relates to a composite electrode for preparing high-purity polyaniline nanowires and a preparation method, belonging to the technology for preparing polyaniline nanowire materials. Background technique [0002] Polyaniline has the advantages of readily available raw materials, simple synthesis methods, unique protonic acid doping behavior, excellent electrochemical and optical properties, structural diversity, and good environmental stability. These excellent characteristics make the application of polyaniline in the fields of sensors, actuators, electromagnetic shielding, antistatic coatings, metal anticorrosion, gas separation membranes, super large capacity capacitors and optoelectronic devices have attracted extensive attention. One of the conductive polymers used in practice. In recent years, polyaniline nanowires have attracted great attention of researchers due to their large specific surface area and excellent physical and chemic...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C25B11/02H01G9/04H01G13/00
Inventor 王纪孝张海滨李寒露褚青献王志王世昌
Owner TIANJIN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com