Method for preparing of cerium oxide powder for chemical mechanical polishing and method for preparing of chemical mechanical polishing slurry using the same

A cerium dioxide, slurry technology, applied in chemical instruments and methods, cerium oxide/cerium hydroxide, nanotechnology for materials and surface science, etc., can solve problems such as low polishing speed and difficulty

Active Publication Date: 2007-09-19
LG CHEM LTD
View PDF1 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, when only this problem is considered and the strength of the polishing material is reduced, the problem of scratches on the polishing film can be solved, but the polishing speed will become lower, thereby causing an additional problem of difficulty in applying the polishing material to the actual process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing of cerium oxide powder for chemical mechanical polishing and method for preparing of chemical mechanical polishing slurry using the same

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0032] (1) Preparation steps of cerium precursor

[0033] This step is used for the preparation of cerium precursor.

[0034] The cerium precursor is not particularly limited, but is preferably selected from the group consisting of carbonates, hydroxide salts, chloride salts, oxalates and sulfates. Among them, it is more preferable to use CO containing 2 and H 2 Carbonate of O gas.

[0035] The raw material for the cerium precursor may be selected from the group comprising cerium nitrate, cerium acetate, cerium chloride and cerium sulfonate. It is preferable to use cerium nitrate or cerium acetate which can be used as a carbonate raw material.

[0036] Also, in the preparation of the cerium precursor, a precipitant for the preparation of a typical cerium precursor may be employed, and more specifically an ammonia compound, especially urea or ammonium carbonate is preferably used.

[0037] In the preparation of the above-mentioned cerium precursor, pores can be formed in t...

Embodiment 1

[0080] (Preparation of Ceria Powder)

[0081]0.5 mol of cerium nitrate was dissolved in 100 mL of distilled water, and itaconic acid as a pore-forming material was added in an amount of 0.3 wt % of cerium nitrate and stirred until it was completely dissolved. Then, 1.5 mol of urea as a precipitating agent was dissolved in 100 mL of distilled water, followed by mixing the two prepared solutions in a 500 mL precipitation reactor. While stirring at a speed of 200 rpm using a stirrer, a precipitation reaction was performed at 96° C. for 20 hours. The resulting powder was centrifuged and washed, then dried in an oven at 100 °C for 24 hours. Then, the powder was analyzed by XRD, and the result confirmed that it was orthorhombic cerium carbonate.

[0082] 1.5 kg of cerium carbonate powder was placed in an alumina crucible, and decomposed materials were removed by performing heat treatment at 350° C. for 24 hours under an oxygen atmosphere. 1.2 kg of oxide are obtained.

[0083] T...

Embodiment 2

[0091] (Preparation of Ceria Powder)

[0092] In addition to the use of ammonium sulfate ((NH 4 ) 2 SO 4 ) as a pore-forming material, ceria powder was prepared in the same manner as described in Example 1, and a crystal size of 26nm, 23m 2 Ceria powder with a specific surface area per g, a pore distribution of 3-10 nm pores distributed at a ratio of 42% of the total pores, and an average particle diameter of 65-473 nm.

[0093] (Preparation of Ceria Powder Dispersion Solution)

[0094] A ceria powder dispersion solution was obtained in the same manner as described in Example 1.

[0095] (Preparation of CMP slurry)

[0096] A CMP slurry was prepared in the same manner as described in Example 1 except for adjusting the average particle size to 152 nm.

[0097] The amount of abrasion of the prepared CMP slurry was measured, and as a result, the polishing rate of the oxide film was 3,406 Å / min and the polishing rate of the nitride film was 39 Å / min. Also, after observation...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
crystal sizeaaaaaaaaaa
crystal sizeaaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to view more

Abstract

The present invention relates to a method of preparing a cerium oxide powder for a CMP slurry and a method of preparing a CMP slurry using the same, and more particularly, to a method of preparing a cerium oxide powder for a CMP slurry and a method of preparing a CMP slurry using the same in which the specific surface area of the powder is increased by preparing a cerium precursor, and then decomposing and calcinating the prepared cerium precursor. The pore distribution is controlled to increase the chemical contact area between a polished film and a polishing material, thereby reducing polishing time while the physical strength of powder is decreased, which remarkably reduces scratches on a polished film.

Description

technical field [0001] The present invention relates to a method of preparing ceria powder for CMP (Chemical Mechanical Polishing) slurry and a method of using the powder to prepare CMP slurry, more particularly, to the preparation of ceria powder for CMP slurry A method and a method of preparing a CMP slurry using the powder, in which the specific surface area of ​​the powder is increased, and the pore size distribution is controlled to increase the chemical contact area between the film to be polished and the polishing material. Therefore, reducing the polishing time and at the same time reducing the physical hardness of the powder significantly reduces scratches on the film to be polished. Background technique [0002] Ceria powder is a high-function ceramic powder widely used as a raw material for polishing materials, catalysts, fluorescent bodies, etc., and has recently received attention as an inorganic polishing material. It is an important raw material for polishing...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C01F17/00C01F17/235
CPCC01F17/0043B82Y30/00C01P2002/60C01P2004/62C01P2004/64C01P2006/12C01P2006/17C09G1/02C09K3/1463C01F17/235
Inventor 吴明焕鲁埈硕金长烈金钟泌曹昇范高敏镇
Owner LG CHEM LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap