Method for preparing high water soluble Nano carbon tube grafted by super branched polymer

A technology of hyperbranched polymer and carbon nanotubes, applied in the field of nanomaterials, can solve the problems of low content of carbon nanotubes, poor solubility of products, materials that cannot reflect the characteristics of carbon nanotubes, etc. Achieving the effect of water solubility and excellent dispersibility

Inactive Publication Date: 2007-12-26
BEIJING UNIV OF CHEM TECH
View PDF0 Cites 38 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

For example, the content of carbon nanotubes is relatively small when polymers are grafted to modify carbon nanotubes, and the resulting materials cannot reflect the char

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing high water soluble Nano carbon tube grafted by super branched polymer

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] Using the multi-wall carbon nanotubes prepared by catalytic pyrolysis as the initial raw material, the carbon nanotubes are purified by strong oxidizing acid to remove impurities in the raw materials, and at the same time, the carbon nanotubes are chopped. Utilizing the action of active groups appearing on the surface of carbon nanotubes after chopping and polyamines, a certain hyperbranching initiating group is modified on the surface of carbon nanotubes. Then react with hyperbranched poly(amide-ester) (hyperbranched polymer generation number is five generations) synthesized by phenylic anhydride (benzene-1,2,4-tricarboxylic acid-1,2 anhydride) and diethanolamine to obtain hyperbranched Poly(amide-ester) grafted carbon nanotubes.

[0024] Step (a): Put 2 g of dry multi-walled carbon nanotubes and 40 mL of 60% concentrated nitric acid into a 100 mL flask equipped with a magnetic stirrer, and reflux for 24 h under magnetic stirring at 80 ° C; discard the upper layer liqu...

Embodiment 2

[0029] On the basis of Example 1, step (a) is the same as Example 1, and the input amount of diethanolamine is changed to 1.4g in step (b), and 10% metaphthalic anhydride (benzene-1,2,4- Tricarboxylic acid-1,2 anhydride) and diethanolamine synthesized hyperbranched poly(amide-ester) (hyperbranched polymer generation number is five generations) DMF solution input amount is changed into 40mL, other conditions are constant, obtained black powder The graft modification of hyperbranched poly(amide-ester) carbon nanotubes.

[0030] Compared with the product obtained in the examples, the content of N elements (8.1%) and O elements (0.62% becomes 14%) changes more obviously in the elemental analysis, and the peak values ​​of amido and carboxyl groups in the XPS analysis results are higher than those in Example 1. The map is larger, the result is clearer and more obvious, and the dispersion performance of the modified product in water is improved to a certain extent (20mg / mL)

Embodiment 3

[0032] On the basis of Example 1, step (a) is the same as Example 1, and the input amount of diethanolamine is changed to 2.1g in step (b), and 10% metaphthalic anhydride (benzene-1,2,4- Tricarboxylic acid-1,2 anhydride) and diethanolamine synthesized hyperbranched poly(amide-ester) (hyperbranched polymer generation number is five generations) DMF solution input amount is changed into 50mL, other conditions are constant, obtained black powder The graft modification of hyperbranched poly(amide-ester) carbon nanotubes.

[0033] The obtained result product has some changes in the content of N element (9.7%) and O element (0.62% becomes 14.3%) relative to the result of the product of Example 2 in elemental analysis, and the peaks of amido and carboxyl in the XPS analysis results are also different from the spectrum of the embodiment Greater increase, the result further proves the grafting effect of amine group and hyperbranched polymer, and the dispersion performance of the modifi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

This invention discloses a method for preparing highly water-soluble carbon nanotubes by grafting modification with hyper branched polymer. The method comprises: purifying carbon nanotubes with a highly oxidative acid to form active groups at the sidewalls and the ends, modifying with polyamine or polyol to form initiating groups at the surfaces, and then reacting between hyper branched polymer and the initiating groups for grafting to form large quantities of carboxyl or amine groups at the surfaces of carbon nanotubes so that carbon nanotubes have high solubility and dispersibility in aqueous solvents. The obtained highly water-soluble carbon nanotubes have improved processability, and can be used in composite materials, hydrogen storage materials, electronics, sensors and biomaterials.

Description

technical field [0001] The invention relates to a surface-modified carbon nanotube and a preparation method thereof, in particular to a super-high water-soluble carbon nanotube grafted by a hyperbranched polymer and a preparation method thereof, belonging to the field of nanomaterials. Background technique [0002] As human beings realize that nanotechnology will become the leading technology in the 21st century, it is more and more urgent for people to master and utilize nanotechnology, so as to realize all-round leapfrog development of society, economy and science and technology. Among them, the discovery of carbon nanotubes is a milestone in the history of the world. In the past ten years, carbon nanotubes have been the focus of scientific research in the world. Due to their unique internal structure (aspect ratio, chirality, etc.) New one-dimensional nanomaterials have important application prospects in many fields and are one of the most promising nanomaterials in the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C30B29/02C30B33/00C30B29/62C01B31/02B01J2/30
Inventor 程斌丁顶
Owner BEIJING UNIV OF CHEM TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap