Method for producing polybenzimidazole crosslinked membrane with epoxy compound

A technology of polybenzimidazole and epoxy compounds, which is applied in the field of epoxy compound cross-linked films, can solve the problems of easy volatilization and loss of cross-linking agents, difficulty in precise control of cross-linking density, etc., and achieve excellent mechanical properties, simple method and fast reaction The effect of mild conditions

Inactive Publication Date: 2008-07-16
SHANGHAI JIAO TONG UNIV
View PDF2 Cites 31 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The methods disclosed in the above patents all require high temperature (such as 300°C) cross-linking reaction. Because the cross-linking agent is easily volatile and lost at high temperature, it is difficult to accurately control the cross-linking density.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for producing polybenzimidazole crosslinked membrane with epoxy compound
  • Method for producing polybenzimidazole crosslinked membrane with epoxy compound
  • Method for producing polybenzimidazole crosslinked membrane with epoxy compound

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] Preparation of amino-containing polybenzimidazole homopolymers from 5-aminoisophthalic acid and 3,3',4,4'-tetraaminobiphenyl:

[0034] Add 5mmol (1.071g) of 3,3',4,4'-tetraaminobiphenyl and 5mmol (0.905g) of 5-aminoisophthalic acid into 20g of polyphosphoric acid containing 70-90wt% phosphorus pentoxide , Under the condition of mechanical stirring under the protection of nitrogen, first react at 150°C for 2 hours, then react at 190°C for 20 hours, and pour into water after cooling down. First neutralize to weak acidity with sodium hydroxide, then neutralize to neutral with sodium bicarbonate, filter, put the collected polymer in ammonia water at 80°C and stir for 12 hours, filter, wash the sample to neutral, 100 °C for 24 hours in vacuum to obtain a homopolymer of amino-containing polybenzimidazole.

[0035] Its intrinsic viscosity is 0.64dL / g, Fig. 1 is its nuclear magnetic resonance spectrum, Fig. 2 is its infrared spectrum.

[0036] Preparation of Polyethylene Glyc...

Embodiment 2

[0040] Prepare amino-containing polybenzimidazole copolymers by 5-aminoisophthalic acid, isophthalic acid and 3,3',4,4'-tetraaminobiphenyl:

[0041]6mmol (1.2856g) 3,3',4,4'-tetraaminobiphenyl, 3mmol (0.4984) isophthalic acid and 3mmol (0.543g) 5-aminoisophthalic acid were added to 20g containing 70-90wt% In the polyphosphoric acid of phosphorus pentoxide, under the condition of nitrogen protection and mechanical stirring, first react at 150°C for 2 hours, then react at 190°C for 20 hours, and pour it into water after cooling down. First neutralize to weak acidity with sodium hydroxide, then neutralize to neutral with sodium bicarbonate, filter, put the collected polymer in ammonia water at 80°C and stir for 12 hours, filter, wash the sample to neutral, 100 °C for 24 hours in vacuum to obtain a copolymer containing amino polybenzimidazole. Its intrinsic viscosity is 0.36dL / g.

[0042] Preparation of polybenzimidazole crosslinked film crosslinked by bisphenol A type epoxy res...

Embodiment 3

[0046] Prepare amino-containing polybenzimidazole copolymers by 5-aminoisophthalic acid, isophthalic acid and 3,3',4,4'-tetraaminobiphenyl:

[0047] 6mmol (1.2856g) 3,3',4,4'-tetraaminobiphenyl, 4mmol (0.6645) isophthalic acid and 2mmol (0.362g) 5-aminoisophthalic acid were added to 20g containing 70-90wt% In the polyphosphoric acid of phosphorus pentoxide, under the condition of nitrogen protection and mechanical stirring, first react at 150°C for 2 hours, then react at 190°C for 20 hours, and pour it into water after cooling down to room temperature. First neutralize to weak acidity with sodium hydroxide, then neutralize to neutral with sodium bicarbonate, filter, put the collected polymer in ammonia water at 80°C and stir for 12 hours, filter, wash the sample to neutral, 100 °C for 24 hours in vacuum to obtain a copolymer containing amino polybenzimidazole. Its intrinsic viscosity is 1.40dL / g.

[0048] Preparation of polybenzimidazole crosslinked film crosslinked by bisph...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to View More

Abstract

The invention relates to a method for preparing a polybenzimidazole crosslinking membrane by using epoxy compounds, which takes amino dibasic acid and aromatic tetraamine as monomer raw material and polyphosphoric acid as reaction medium and reaction is carried out for 5-30 hours at 150-220 DEG C under the nitrogen protection condition so as to obtain homopolymer containing amino polybenzimidazole, and takes the amino dibasic acid, nonaminonic dibasic acid and the aromatic tetraamine as the monomer raw materials to prepare copolymer containing amino polyphosphoric under the same conditions. The prepared homopolymer and the copolymer of the polybenzimidazole have good dissolvability in solvents of dimethyl sulphoxide, N, N- dimethylacetamide, phosphate, vitriol and methane-sulforic acid, etc. The bifunctionality or polyfunctional epoxy compounds are used as cross linking agent. The polybenzimidazole crosslinking membrane that has good property can be prepared through crosslinking reaction of the amido contained in the polybenzimidazole and epoxy functional groups contained in the bifunctionality or polyfunctional epoxy compounds.

Description

technical field [0001] The invention relates to a method for preparing a polybenzimidazole cross-linked film with an epoxy compound. A high-performance epoxy compound cross-linked film containing amino-soluble polybenzimidazole is prepared by using a di- or multi-functional epoxy compound. It belongs to the technical field of chemical materials. Background technique [0002] The polybenzimidazole with full aromatic structure is a kind of high-performance material, which has extremely high heat resistance, excellent mechanical properties, excellent chemical stability, good dielectric properties and spinning and film-forming properties. It has been widely used in aerospace, microelectronics and other fields. In the mid-1990s, it was discovered that polybenzimidazole doped with phosphoric acid has potential application prospects in the field of high-temperature proton exchange membrane fuel cells. Therefore, this type of material has received great attention in recent years. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08J5/18C08J3/24C08L79/04C08K5/15
Inventor 房建华徐楠张桂梅郭晓霞徐宏杰印杰
Owner SHANGHAI JIAO TONG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com