Water-soluble epoxy red ferric oxide primer and method of preparing same

A technology of epoxy iron red primer and iron oxide red, which is applied in the direction of epoxy resin coatings, coatings, anti-corrosion coatings, etc., can solve the problems of environmental pollution, resource waste, personnel injury, etc., and achieve convenient construction, easy emulsification, The effect of excellent chemical resistance

Inactive Publication Date: 2008-12-31
CNPC RES INST OF ENG TECH
View PDF0 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the anti-corrosion primers for the inner and outer walls of steel storage tanks in oil fields mostly use solvent-based anti-corrosion coatings. The organ...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] The manufacture method-1 of waterborne epoxy iron red primer of the present invention. In the stainless steel barrel, first add 1.6 parts by weight of deionized water, then add 1 part by weight of epoxy-modified water-based amine curing agent EU5073 (Shanghai Dekun Industrial Co., Ltd.), 0.01 parts by weight of wetting and dispersing agent H140 ( Shenzhen Haichuan Chemical Technology Co., Ltd.), after high-speed stirring and dispersion, add 0.3 parts by weight of iron oxide red, 0.5 parts by weight of precipitated barium sulfate, 0.4 parts by weight of sericite, 0.1 parts by weight of composite iron-titanium powder, and 0.2 parts by weight of Aluminum tripolyphosphate, 0.01 parts by weight polymethylalkylsiloxane solution, and then grind with a sand mill to prepare component A. Add 0.12 parts by weight of butyl glycidyl ether to 1 part by weight of bisphenol A liquid epoxy resin, and stir evenly to prepare component B. When in use, mix and stir 1 part by weight of comp...

Embodiment 2

[0021] In a stainless steel bucket, first add 1.4 parts by weight of deionized water, then add 1 part by weight of epoxy-modified water-based amine curing agent EU5073, and 0.01 parts by weight of wetting and dispersing agent H140. Add 0.5 parts by weight of iron oxide red, 0.2 parts by weight of precipitated barium sulfate, 0.3 parts by weight of sericite, 0.2 parts by weight of aluminum tripolyphosphate, and 0.01 parts by weight of polymethylalkylsiloxane solution, and then grind with a sand mill A component is prepared. Add 0.08 parts by weight of butyl glycidyl ether to 1 part by weight of liquid bisphenol A epoxy resin, and stir evenly to prepare component B. When in use, mix and stir 1 part by weight of component A and 0.25 part by weight of component B to obtain the water-based epoxy iron red primer. The raw materials used are all domestic commercial products.

[0022] Waterborne epoxy iron red primer performance test result of the present invention is shown in Table ...

Embodiment 3

[0024] In a stainless steel bucket, first add 2 parts by weight of deionized water, then add 1 part by weight of epoxy-modified water-based amine curing agent EU5073, and 0.01 part by weight of wetting and dispersing agent H140. Add 0.4 parts by weight of iron oxide red, 0.6 parts by weight of precipitated barium sulfate, 0.5 parts by weight of sericite, 0.2 parts by weight of composite iron-titanium powder, 0.1 parts by weight of aluminum tripolyphosphate, 0.01 parts by weight of polymethylalkylsiloxane solution, and then grind it with a sand mill to obtain component A. Add 0.12 parts by weight of butyl glycidyl ether to 1 part by weight of bisphenol A liquid epoxy resin, and stir evenly to prepare component B. When in use, mix and stir 1 part by weight of component A and 0.18 part by weight of component B to obtain a water-based epoxy iron red primer. The raw materials used are all domestic commercial products.

[0025] Waterborne epoxy iron red primer performance test res...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to waterborne epoxy iron red shop primer and a preparation method thereof. The waterborne epoxy iron red shop primer contains two compositions; A composition is prepared by the steps of dissolving epoxy-modified waterborne amine hardener in deionized water, then adding wetting dispersant, polymethyl siloxane, iron oxide red, precipitated barium sulfate, sericite, compound ferrotitanium powder, and aluminium triphosphate, and mixing, blending and grinding the mixture; B composition is prepared by mixing and blending bisphenol-a-type epoxy resin and butyl glycidyl ether. The waterborne epoxy iron red shop primer is safe and environment-friendly and can be used as anticorrosive shop primer for interior and exterior walls of steel oil storage tanks in oil fields.

Description

technical field [0001] The invention relates to a water-based epoxy iron red primer and a manufacturing method, which can be used as an anti-corrosion primer for the inner and outer walls of steel storage tanks in oil fields. Background technique [0002] At present, the anti-corrosion primers for the inner and outer walls of oilfield steel storage tanks mostly use solvent-based anti-corrosion coatings. The organic solvents contained in this coating volatilize in large quantities during production and construction, causing environmental pollution, personnel injury and waste of resources. . Contents of the invention [0003] The purpose of the present invention is to avoid the disadvantages of the above-mentioned prior art and provide a simple production process, convenient construction, excellent rust resistance, chemical resistance, salt spray resistance, water resistance, and salt water resistance. , oil-resistant, sewage-resistant water-based epoxy iron red primer and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D163/02C09D7/12C09D5/12
Inventor 徐翠竹林竹张莉范云鹏韩文礼
Owner CNPC RES INST OF ENG TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap