A water-based polyurethane and synthetic leather technology, applied in textiles, papermaking, fiber treatment, etc., can solve the problems of air permeability and waterproof, etc., and achieve the effect of plump hand feeling, reliable process and sufficient source

Active Publication Date: 2009-07-15
ENDIAN (GUANGDONG) LEATHER GOODS & FASHION TECH CORP
View PDF0 Cites 30 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Now polyurethane synthetic leather is close to natural leather in terms of microstructure and physical properties, and even some mechanical properties far exceed natural leather, but breathability and waterproof are a pair of contradictions, a

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0019] Example 1

[0020]Add 100 parts of toluene diisocyanate (TDI), 120 parts of polyoxypropylene glycol, 20 parts of 2,2-dimethylolpropionic acid (DMPA), and 2 parts of tert-butyldimethylchlorosilane under stirring at room temperature. In a reaction vessel filled with nitrogen, the temperature was controlled at 80°C and reacted for 5 hours to obtain a prepolymer; at 5°C, the above prepolymer was slowly added dropwise to 500 parts of deionized water dissolved in 10 parts of triethylamine at high speed. Stir and emulsify, then continue to add 100 parts of nano-silica and 20 parts of (3,3'-diethyl-4,4'-diaminodiphenylmethane) terminal amino chain extender under high-speed stirring to react at 20℃5 Within hours, an aqueous polyurethane emulsion with a solid content of 60 wt% was obtained.

Example Embodiment

[0021] Example 2

[0022] Put 70 parts of dicyclohexylmethane diisocyanate, 160 parts of polyoxypropylene triol, and 15 parts of 3-hydroxy-2-(hydroxymethyl)-2-methylpropionic acid in a reactor isolated from air. Control the reaction temperature at 80°C and react for 6 hours to obtain the prepolymer; at 0°C, slowly add the above prepolymer dropwise to 600 parts of deionized water dissolved in 10 parts of triethylamine, stir and emulsify at high speed, and then Continue to add 20 parts of nano silica under stirring, and react at 30° C. for 5 hours to obtain an aqueous polyurethane emulsion with a solid content of 55 wt%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Viscosityaaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of synthetic leather materials, in particular to an aqueous polyurethane emulsion for synthetic leather and a preparation method thereof. Environment-friendly aqueous polyurethane resins with different adaptabilities are manufactured by selecting materials with different functions, such as isocyanate, polyester polyol, a modified nano-silicon dioxide and the like by a high-molecular alloy technology. The aqueous polyurethane resin has the advantages of adequate raw material sources, reliable process and high solid content up to 30-40%, no organic solvent in a product, environmental protection and wide application range. The synthetic leather prepared by the aqueous polyurethane emulsion has the advantages of excellent abrasive resistance, high tear strength, high extensibility up to 400-700% and high tensile strength up to 20-45MPa and can replace PVC artificial leather, PU leather and natural leather; the synthetic material has the advantages of good hand feeling, comfort and good recoverability, as well as good water resistance, good abrasive resistance, good acid resistance, good alkali resistance, high temperature resistance and the like; and compared with the traditional synthetic leather, various technical performances of the synthetic material are obviously improved.

Description

Technical field: [0001] The invention relates to the technical field of synthetic leather materials, in particular to an aqueous polyurethane emulsion used for synthetic leather and a preparation method thereof. Background technique: [0002] Polyurethane (PU) synthetic leather has excellent wear resistance, good tear strength and elongation, and at the same time endows leather products with flat surface, full hand feel, comfort, good recovery, and moderate price. Expensive natural leather products have gradually replaced low-grade and cheap PVC artificial leather, and have become an indispensable consumer product in people's lives. Since the birth of polyurethane synthetic leather, it has gone through the development stage of profiling and simulation, and now it has entered the stage of high simulation. Now polyurethane synthetic leather is close to natural leather in terms of microstructure and physical properties, and even some mechanical properties far exceed natural le...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D06M15/568D06M13/50D06M11/79D06N3/14
Inventor 周亚民黄国任
Owner ENDIAN (GUANGDONG) LEATHER GOODS & FASHION TECH CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap