Dimer acid modified unsaturated polyester resin and synthetic method thereof

A technology of polyester resin and synthesis method, which is applied in the field of polymer materials, and can solve the problems of application limitations, unsaturated polyester resin, no patent report, and high cost.

Inactive Publication Date: 2009-12-16
HUNAN UNIV
View PDF0 Cites 21 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, some existing biomedical materials have high cost and poor performance, which limits their application.
[0003] The unsaturated polyester resin modified with dimer acid has not been reported as a patent, and no one else has set foot in it

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Dimer acid modified unsaturated polyester resin and synthetic method thereof
  • Dimer acid modified unsaturated polyester resin and synthetic method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] Embodiment 1: one of the synthetic method of unsaturated polyester resin:

[0023] Mix 2.0 moles of maleic anhydride, 2.0 moles of phthalic anhydride, 0.2 moles of dimer acid, 2.2 moles of ethylene glycol, and 2.1 moles of diethylene glycol, put them into a 250ml three-necked flask with a water separator, and place them in a silicone oil bath , electric stirring, heating up to 150°C, melt polymerization in nitrogen atmosphere for 40 minutes, then raising temperature to 180°C, melt polymerization in nitrogen atmosphere for 120 minutes, then raising temperature to 200°C, melt polymerization in nitrogen atmosphere for 30 minutes. When the distilled reaction water reaches 80% of the theoretical amount, the polymerization is stopped, the temperature is lowered to 150° C., and poured out. After cooling, a light yellow transparent viscous liquid unsaturated polyester resin is obtained.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention uses a melt phase polycondensation method, uses dimer acid as a reaction monomer for the first time, and performs copolymerization on the dimer acid and several monomers in the group consisting of ethylene glycol, propylene glycol, diethylene glycol, neopentyl glycol, polyethylene glycol, fumaric acid, maleic anhydride, adipic acid, phthalic anhydride and m-phthalic acid to obtain an unsaturated polyester resin with excellent combination properties and low cost. The resin is expected to serve as the matrix resin of medical intrabony fixing materials, tissue engineering support materials, bone tissue temporary substitutes, environment-friendly adhesives, environment-friendly fiber glass reinforced plastics, environment-friendly paints, disposable tableware, packaging materials, shopping bags, garbage bags, pharmaceutical coatings, or capsules, pharmaceutical slow-release (controlled-release) materials, agricultural mulching film and the like.

Description

technical field [0001] The invention relates to a chemical synthesis environment and biodegradable polymer materials and methods. Using several monomers such as ethylene glycol, propylene glycol, diethylene glycol, neopentyl glycol, polyethylene glycol, fumaric acid, maleic anhydride, adipic acid, phthalic anhydride, isophthalic acid, etc. One is the basic raw material, which can be co-polymerized with dimer acid to obtain unsaturated polyester resin with excellent comprehensive performance and low cost. This kind of resin can be used as medical bone internal fixation material, tissue engineering scaffold material, bone tissue temporary substitute, drug coating or capsule, drug sustained release material, UV-curable ink, UV-curable paper coating, environment-friendly FRP, Adhesives, base materials for environment-friendly UV-curable or room-temperature-curable coatings. technical background [0002] Existing light-curing coatings all need to use toxic coating additives and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08G63/676C08G63/78C08F283/01
Inventor 郭文迅孙翔月袁华彭荡何姣贺倩高鹏
Owner HUNAN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products