Production method of water-soluble hemostatic gauze
A production method and technology of hemostatic gauze, which is applied in the field of production of water-soluble hemostatic gauze, can solve the problems of unsafe products, inability to use, and insufficient strength, etc., achieve no cytotoxic reaction and side effects, prevent surgical adhesion, and facilitate acceleration The effect of rehabilitation
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0047] 1. Gauze pretreatment:
[0048] 1.1 Preparation materials: 1200 grams of cotton gauze, 4800 ml of 95% (v / v) ethanol solution.
[0049] 1.2 Pretreatment: Put the raw material of cotton gauze into a glass container, let the gauze spread out as much as possible, do not overlap, then slowly pour ethanol along the wall of the glass container, tamp it with a glass rod, so that the gauze is completely soaked, and then use a silicone plug Seal for 1 hour.
[0050] 2. Microcrystalline treatment of gauze:
[0051] 2.1 Preparation of microcrystallization reaction solution: use sodium hydroxide to analyze pure crystals and distilled water to prepare 4800ml of 40wt% sodium hydroxide solution, stir with a glass rod until it is completely dissolved and becomes clear and transparent. The liquid was cooled to 20°C and sealed for later use.
[0052] 2.2 Put the pretreated gauze raw material in a circulating rotary reactor, then add 4800ml of the prepared microcrystallization reaction ...
Embodiment 2
[0063] In the microcrystallization treatment, 50 wt% sodium hydroxide solution was selected, and other operations were the same as in Example 1. The obtained water-soluble hemostatic gauze has a mass per unit area of 95g / m 2 , 25ml per gram of water absorption, and other test results are the same as in Example 1.
Embodiment 3
[0065] In the cross-linking reaction, 60 wt% ethanol solution of chloroacetic acid was selected, and other operations were the same as in Example 1. The obtained water-soluble hemostatic gauze has a mass per unit area of 80g / m 2 , 30ml per gram of water absorption, and other test results are the same as in Example 1.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com