Plastic profiled bar decorative layer combination material with metal-like natural texture, preparation method and application thereof

A technology for profiled materials and decorative layers, applied in decorative arts and processes for producing decorative surface effects, can solve the problems of short service life and increased material consumption, and achieve long service life, green manufacturing and Use, wear-resistant and scratch-resistant effect

Inactive Publication Date: 2010-06-02
GUANGDONG SHENGHENGCHANG CHEM IND
View PDF0 Cites 106 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The short service life of the product leads to an increa...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0104] Embodiment 1, decorative layer combination material

[0105] Follow the recipe below and make trim layer composite pellets as described in Section 2. Calculated by the weight percentage of each component in the combined material.

[0106] Decorative layer combination material formula 1: PMMA: 40%; red composite pigment: 39.7%; silicon dioxide: 20%; antioxidant AOD: 0.3%. Among them, the red composite color material is made by mixing organic pigments permanent red 2BL and phthalocyanine red according to the required color chroma; the silica is pretreated with 1% coupling agent KH550.

[0107] The pellets prepared by the formula can be used for freezers, refrigerators, and microwave oven panels; it has the decorative effect of red or wine red panels, and has good heat resistance, crack resistance, high surface hardness, and scratch resistance.

[0108] Decorative layer combination material formula 2:

[0109] MS: 30%;

[0110] Green composite pigment: 37.5%;

[0111]...

Embodiment 2

[0148] Embodiment 2, application of decorative layer combination material in imitation aluminum alloy office furniture or screen

[0149] PC / ABS is selected as the resin material of the profiled material of imitation aluminum alloy office furniture or screen;

[0150] Co-extrusion decorative layer coating material is composed of: PMMA 100kg, processing aid stearic acid 1-2kg, dispersant L-1000 (Mitsubishi Rayon) 0.2-0.5kg, imitation aluminum alloy office furniture or screen decorative layer composite material 10~20kg (made by formula 6 of embodiment one).

[0151] Manufactured according to the method described in the third part above, wherein:

[0152] The processing temperature of PC / ABS is 200-230°C, the extrusion die temperature is 190-195°C, and the screw speed of the host machine is 10-20rpm.

[0153] The processing temperature of the co-extruded coating material is 200-230°C, the extrusion die temperature is 190-195°C, and the screw speed of the host machine is 5-10rpm...

Embodiment 3

[0155] Embodiment 3, the application of decorative layer combination material in the housing of colored household appliances

[0156] The material composition of the shell of colored household appliances: UPVC / ABS is selected as the resin material, 100kg of PVC-SG-5 type powder is selected, ABS 20kg, calcium carbonate 15-20kg, MBS 8-10kg, other functional additives organic tin heat stabilizer, calcium Zinc heat stabilizer, PE wax, processing aids, pigments (red, yellow, blue, green, orange, reddish brown, silver, black and other pigments) are 0.5-4kg respectively.

[0157] The co-extrusion coating composition is: PMMA 100kg, processing aid stearic acid 1~2kg, dispersant A-80 (Germany Clariant company) 0.2~0.5kg, embodiment 1 formula 3 preparation color home appliance casing decoration layer The combined material is 10-20kg.

[0158]The processing temperature of UPVC / ABS is 180-195°C, the extrusion die temperature is 190-195°C, and the screw speed of the main engine is 10-20rp...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Tensile strengthaaaaaaaaaa
Izod notched impact strengthaaaaaaaaaa
Charpy notched impact strengthaaaaaaaaaa
Login to view more

Abstract

The invention provides a plastic profiled bar decorative layer combination material with natural texture for co-extrusion molding, formed by mixing 15-80wt% of plastic substrate, 15-80wt% of composite pigment and 0-50wt% of inorganic powder, wherein the composite pigment comprises pigment or dye with natural color texture effect; inorganic pigment and inorganic powder in the composite pigment need to be respectively and actively processed by a surface conditioning agent or a coupling agent; the combination material provides the surface of the plastic profiled bar with a high-polymer material co-extrusion composite layer with stronger adhesion and endows the surface of the plastic profiled bar with the metal-like texture effects, such as the colors of gold, silver, copper or other natural metal materials. The decorative layer has a certain thickness, high hardness, strong scratch resistance and longer product service life and can be used for industries, such as electronic appliance shells, plastic color windows and doors, plastic profiled bars, furniture sheets, and the like.

Description

technical field [0001] The invention belongs to the field of macromolecular materials, and relates to the formulation and processing technology of a plastic profiled material decorative layer combination material imitating metal natural texture produced by co-extrusion technology. Background technique [0002] "Replacing wood with plastic and steel with plastic" has become a factual act of replacing natural resources with synthetic materials, but the appearance of plastic products always stays in the transformation of color and shape, and the color effect and material texture can never replace the texture of natural materials. [0003] In the past two decades, since plastic profiles are widely used in construction materials, office furniture, household appliances and other fields, the market is huge, and consumers do not want a large number of synthetic materials to flood homes, offices and public places. Therefore, surface decoration technology products on plastic profiles ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L33/12C08L25/14C08L51/00C08L69/00C08L71/12C08K13/06C08K9/06C08K3/36C08K5/3417C08K3/34C08K9/04C08K3/22C08K3/08C08K3/04C08K7/20C08K3/30C08K3/26B29B9/06B44C1/20
Inventor 罗崇远窦红荣
Owner GUANGDONG SHENGHENGCHANG CHEM IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap