Antistatic modified polyester and method for preparing same

A modified polyester and antistatic technology, applied in the field of modified polyester materials, can solve problems such as high surface resistance, poor hygroscopicity, explosion, etc., and achieve excellent mechanical properties, good thermal and temperature stability, and broad application prospects

Active Publication Date: 2010-06-23
KINGFA SCI & TECH CO LTD +1
View PDF0 Cites 23 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, because of its poor hygroscopicity, high surface resistance and serious static electricity, it affects the popularization and application of modified polyester.
Components or components produced by modified polyester used in electronic appliances and other industries are constantly rubbed or contacted with other surrounding materials during

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] Antistatic flame retardant PBT (weight percent):

[0024] PBT resin: 64%, alkali-free glass fiber: 0%, antistatic agent: 7%, ethylene-butyl methacrylate-glycidyl acrylate terpolymer and ethylene-methyl acrylate binary copolymer 5%, Brominated epoxy resin: 18%, antimony white: 4%, composite antioxidant system composed of hindered phenolic antioxidant, phosphite antioxidant, organic sulfur antioxidant: 0.3%, coloring agent: 0.5%, Processing aids: 1.2%. The weight formula of the antistatic agent is 92% of sodium dodecyl sulfate, 6% of sodium sulfate, and 2% of paraffin.

Embodiment 2

[0026] Antistatic flame retardant glass fiber reinforced PBT (weight percent):

[0027] PBT resin: 57.5%, alkali-free glass fiber: 15%, antistatic agent: 5%; ethylene-butyl methacrylate-glycidyl acrylate terpolymer 3%, brominated polycarbonate: 15%, Antimony white: 2.5%, phosphite antioxidant: 0.5%, carbon black: 0.5%, processing aid: 1%. The weight formula of the antistatic agent is 96% of sodium dodecyl sulfate and 4% of sodium sulfate.

Embodiment 3

[0029] Antistatic flame retardant glass fiber reinforced PBT (weight percent):

[0030] PBT resin: 25.6%; E-glass fiber: 50%; antistatic agent: 3%; brominated epoxy resin: 12%, antimony white: 3%, phenolic antioxidant and phosphite antioxidant: 0.4 %; ethylene-methyl acrylate binary copolymer and ethylene-vinyl acetate copolymer binary copolymer: 4.6%; iron red: 0.4%; processing aids: 1%. The weight formula of the antistatic agent is 90% of sodium dodecyl sulfate, 8% of sodium sulfate, and 2% of paraffin.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses antistatic modified polyester and a method for preparing the same. The antistatic modified polyester comprises the following components by weight percent: 30-70 percent of polyester resin, 0-50 percent of alkali-free glass fibre, 8-20 percent of brominated flame retardant, 1-5 percent of antimony trioxide, 1-8 percent of antistatic agent, 0-10 percent of toughening agent, 0.1-0.5 percent of antioxidant, 0-5 percent of coloring agent and 0.5-1 percent of processing auxiliary. The antistatic modified polyester has good thermal stability, excellent mechanical performance, can be made into a variety of colors and has broad application prospect.

Description

technical field [0001] The invention relates to the field of modified polyester materials, in particular to an antistatic modified polyester and its preparation technology. Background technique [0002] In recent years, thermoplastic polyesters, especially polybutylene terephthalate (PBT), polyethylene terephthalate (PET), etc., are in increasing demand in electronic appliances and various industrial fields. Performance characteristics include: fast crystallization speed, high-speed molding, weather resistance, chemical resistance, excellent friction and wear properties, low water absorption, high heat distortion temperature, high mechanical strength, good fatigue resistance and dimensional stability, creep Also smaller. However, because of its poor hygroscopicity, high surface resistance, and serious static electricity, it affects the popularization and application of modified polyester. Components or components produced by modified polyester used in electronic appliances...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L67/02C08K13/02C08K5/42C08K3/30C08L91/08C08K13/04B29B9/06B29C47/92B29C48/40B29C48/92
CPCB29C48/04B29C48/40
Inventor 朱文梁惠强姜苏俊陈大华
Owner KINGFA SCI & TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap