Antibacterial functionalized artificial joint with silver-loaded nanotube array surface

A nanotube array, artificial joint technology, applied in inorganic chemistry, titanium compounds, chemical instruments and methods, etc., can solve the problem of not involving the surface preparation of metal substrates, and achieve the effect of not easy to produce drug resistance and high sterilization efficiency

Inactive Publication Date: 2010-07-07
江苏广达医材集团有限公司 +1
View PDF1 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this preparation method can only prepare dispersed titanate structur

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Antibacterial functionalized artificial joint with silver-loaded nanotube array surface
  • Antibacterial functionalized artificial joint with silver-loaded nanotube array surface
  • Antibacterial functionalized artificial joint with silver-loaded nanotube array surface

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0027] Example 1

[0028] (1) First select titanium alloy to process the artificial joint;

[0029] (2) Pretreatment of the artificial joint surface: After the surface is polished, ultrasonically wash with acetone, deionized water and absolute ethanol for 10-30 minutes, and then use HF and HNO 3 The mixed solution of water and water (volume ratio is 1:4:5) is chemically polished for 20-40 seconds, and then thoroughly rinsed with deionized water, then dried for use;

[0030] (3) Preparation of aqueous organic electrolyte solution: using ethylene glycol as a solvent, other active ingredients are: water 2vol% (volume percent), phosphoric acid 4vol% (volume percent), ammonium fluoride 0.3wt% (mass percent);

[0031](4) Preparation of titanium dioxide nanotubes by two-step anodic oxidation: the artificial joint with surface pretreatment is used as the anode, and the graphite or platinum sheet is used as the cathode, and the first anodic oxidation is carried out in an aqueous organ...

Example Embodiment

[0035] Example 2

[0036] (1) First select titanium to process the artificial joint;

[0037] (2) Pretreatment of the artificial joint surface: after the surface is polished, ultrasonically wash with acetone, deionized water and absolute ethanol for 30-60 minutes in sequence, and then use HF and HNO 3 The mixed solution of water and water (volume ratio is 1:4:5) is chemically polished for 40-60 seconds, and then thoroughly rinsed with deionized water, and then dried with a hair dryer for use;

[0038] (3) Preparation of aqueous organic electrolyte solution: using ethylene glycol as solvent, other active ingredients are: water 2vol% (volume percent), phosphoric acid 4vol% (volume percent), ammonium fluoride 0.5wt% (mass percent);

[0039] (4) Preparation of titanium dioxide nanotubes by two-step anodic oxidation: the artificial joint with surface pretreatment is used as the anode, and the graphite is used as the cathode, and the first anodic oxidation is carried out in an aque...

Example Embodiment

[0043] Example 3

[0044] (1) First select titanium alloy to process the artificial joint;

[0045] (2) Pretreatment of the artificial joint surface: after the surface is polished, ultrasonically wash with acetone, deionized water and absolute ethanol for 60-90 minutes in sequence, and then use HF and HNO 3 The mixed solution of water and water (volume ratio is 1:4:5) is chemically polished for 60-80 seconds, and then thoroughly rinsed with deionized water, then dried by a hair dryer for use;

[0046] (3) Preparation of aqueous organic electrolyte solution: using ethylene glycol as a solvent, other active ingredients are: water 4vol% (volume percent), phosphoric acid 6vol% (volume percent), ammonium fluoride 0.5wt% (mass percent);

[0047] (4) Preparation of titanium dioxide nanotubes by two-step anodic oxidation: the artificial joint with surface pretreatment is used as the anode, and the graphite or platinum sheet is used as the cathode, and the first anodic oxidation is ca...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to an antibacterial functionalized artificial joint with a silver-loaded nanotube array surface. The surface of a metal substrate of the artificial joint is provided with a silver-doped sodium titanate nanotube array layer with a tubular structure. The inside of the silver-doped sodium titanate nanotube array layer is further loaded with bone morphogenetic protein (BMP). A preparation method of the antibacterial functionalized artificial joint with the silver-loaded nanotube array surface comprises the following steps: firstly selecting pure titanium or titanium alloy to process the artificial joint; then adopting the two-step anodizing technology to obtain a titanium dioxide nanotube array layer with a tubular structure on the surface of the pure titanium or titanium alloy artificial joint; adopting the alkaline hydrothermal synthesis technology to convert the titanium dioxide nanotube array layer into the sodium titanate nanotube array layer; doping trace silver in the sodium titanate nanotube array layer by solution impregnation iron exchange; and finally adopting the centrifugal load technology to load the bone morphogenetic protein in the silver-doped sodium titanate nanotube array layer.

Description

technical field [0001] The invention relates to an artificial joint with antibacterial and functionalized surface of silver-loaded nanotube arrays, in particular to an artificial joint with silver-doped sodium titanate nanotubes loaded with bone morphogenetic protein (BMP) on the surface and a preparation method thereof, belonging to Technical field of artificial joint materials. Background technique [0002] Every year, about 1.5 million patients with joint loss due to degenerative and inflammatory arthritis need artificial joint replacement. Among them, the application of metal materials in the manufacture of artificial joints is the earliest, and it is still the most widely used in clinical practice. Over time and clinical studies have shown that artificial joints made of metal materials commonly loosen, sink or break, causing bone resorption, which is one of the main complications affecting the long-term efficacy of artificial joint replacement. Modification of implant...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): A61L27/30A61L27/06A61L27/56A61L27/54C25D11/26C01G23/00
Inventor 储成林盛晓波
Owner 江苏广达医材集团有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap