Method for largely preparing superfine spherical titanium aluminium-based alloyed powder

A technology of base alloy and alloy powder, which is applied in the field of preparation of fine spherical titanium-aluminum base alloy powder, which can solve the problems of TiAl base alloy powder that have not been seen yet, and achieve the effect of fine particle size, high operation stability and strong repeatability

Inactive Publication Date: 2010-10-06
UNIV OF SCI & TECH BEIJING
View PDF1 Cites 34 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, there are no relevant reports on the preparation of TiAl-based alloy powders by the above two processes.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for largely preparing superfine spherical titanium aluminium-based alloyed powder
  • Method for largely preparing superfine spherical titanium aluminium-based alloyed powder

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0015] Example 1. Using high-purity aluminum with a purity of 99.99%, titanium sponge, Al-Nb master alloy, Ti-B alloy, tungsten powder, and yttrium scrap with a purity of 99.99% as raw materials, it is smelted by a plasma cooling bed furnace melting process Large size ingots with a nominal composition of Ti-45Al-9 (Nb, W, B, Y). The alloy ingot is coarsely crushed by low-temperature cold air chips, the temperature of the compressed nitrogen cold air is -30°C, and the particle size of the chips is about 2mm. The debris was subjected to vortex jet mill grinding, the grinding nitrogen pressure was 0.65Mpa, the rotating speed of the separator was 5800 rpm, and irregular fine alloy powder with an average particle size of 18 μm was collected. The fine alloy powder is subjected to radio frequency plasma spheroidization treatment, the plasma stable power is 35KW, the flow rate of argon working gas is 23 slpm, the flow rate of argon protective gas is 155 slpm, and the system negative p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention provides a method for largely preparing superfine spherical titanium aluminium-based alloyed powder, which belongs to the technical field of powder preparation. The method comprises the following steps: smelting high-purity aluminium and titanium sponge as main raw materials and Al-Nb intermediate alloy, Ti-B alloy, tungsten powder and high-purity yttrium scraps as auxiliary raw materials into an alloy cast ingot in a vacuum consumable electrode arc skull furnace or a vacuum induction furnace; then carrying out coarse crushing and vortex airflow milling to prepare irregular superfine alloy powder; and finally carrying out plasma spheroidization of radio frequency (RF) and the like to prepare the superfine spherical titanium aluminium-based alloyed powder. The prepared alloy powder has the advantages of high purity, fine particle size, narrow particle size distribution, good uniformity, high sphericity, good flowability and the like and can meet the demands of the technical industrial production of injection forming, gel injection molding forming, thermal spraying and the like.

Description

technical field [0001] The invention belongs to the technical field of powder preparation, and in particular provides a method for preparing fine spherical titanium-aluminum-based alloy powder. technical background [0002] TiAl-based alloys have the advantages of low specific gravity, good high-temperature strength, oxidation resistance, and excellent creep resistance. They are considered to be the most promising new generation of lightweight superalloys. Environmental protection and other technical fields have very broad application and development prospects. However, TiAl alloys generally have problems such as low ductility at room temperature, difficulty in plastic forming, and high preparation costs, which limit their development and application. Among many material preparation processes, powder metallurgy preparation technology can not only obtain uniform fine-grained structure, but also directly prepare parts with or close to the final shape, which has become one of ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B22F9/04C22C1/03
Inventor 何新波王述超路新盛艳伟朱郎平曲选辉
Owner UNIV OF SCI & TECH BEIJING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap