Composite soldering material for soldering titanium alloy and ceramic or ceramic matrix composition material and method for soldering by using same

A technology of composite brazing filler metal and composite material, applied in welding/welding/cutting items, welding/cutting medium/material, welding medium, etc., which can solve the problem of reduced wettability of base metal, low joint strength, and easy cracking of welded joints and other problems, to achieve the effect of reducing the thermal expansion coefficient, improving the strength of the joint, and improving the mechanical properties

Active Publication Date: 2010-11-24
HARBIN INST OF TECH
View PDF6 Cites 36 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The present invention aims to solve the problem that cracks are easily produced in the welded joint obtained by brazing and connecting titanium alloys and ceramics or ceramic matrix composite materials using the existing brazing material, the joint strength is low, and the introduction of the ceramic phase...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Composite soldering material for soldering titanium alloy and ceramic or ceramic matrix composition material and method for soldering by using same
  • Composite soldering material for soldering titanium alloy and ceramic or ceramic matrix composition material and method for soldering by using same
  • Composite soldering material for soldering titanium alloy and ceramic or ceramic matrix composition material and method for soldering by using same

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach 1

[0013] Specific implementation mode one: the composite solder used in this embodiment for brazing titanium alloys and ceramics or ceramic-based composite materials consists of 30% to 60% Cu powder, 30% to 60% Ni powder and 0.5% to 60% Ni powder by weight percentage. 35% reinforcement phase composition, the reinforcement phase is TiB 2 powder or SiC powder.

[0014] In the composite solder of the present embodiment, Cu and Ni can dissolve the Ti element, and it is easy to form a reaction layer on the side of the ceramic or ceramic matrix composite material, and at the same time, the reinforcing particles (TiB 2 Or SiC) reacts with Ti elements to generate reinforcing particles in situ, reduce stress, pin grain boundaries, and increase strength.

specific Embodiment approach 2

[0015] Specific embodiment two: the difference between this embodiment and specific embodiment one is that the composite solder used for brazing titanium alloys and ceramics or ceramic-based composite materials is composed of 40% to 50% Cu powder, 40% to 50% by weight. % Ni powder and 1%~10% reinforcement phase, the reinforcement phase is TiB 2 powder or SiC powder. Other parameters are the same as in the first embodiment.

[0016] The composition of the composite brazing filler metal of this embodiment is more preferable.

specific Embodiment approach 3

[0017] Specific embodiment three: the difference between this embodiment and specific embodiment one is that the composite solder used for brazing titanium alloys and ceramics or ceramic matrix composite materials is composed of 48.5% Cu powder, 48.5% Ni powder and 3% by weight. %TiB 2 powder composition. Other parameters are the same as in the first embodiment.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Thicknessaaaaaaaaaa
Shear strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a composite soldering material for soldering a titanium alloy and a ceramic or a ceramic matrix composition material and a method for soldering by using the same, and solves the problems that a welding joint obtained by soldering the titanium alloy and the ceramic or the ceramic matrix composition material through the conventional soldering material is easy to crack and has low strength, and the introduction of a ceramic phase in a method of introducing the ceramic phase into the soldering material causes reduction of wettability of a connecting layer for a base metal. The composite soldering material consists of Cu, Ni and a reinforced phase, wherein the reinforced phase is TiB2 powder or SiC powder. The method comprises the following steps of: performing ball milling on the Cu, Ni and TiB2 or SiC powder, uniformly mixing, and coating to-be-welded surfaces of the titanium alloy and the ceramic to obtain to-be-welded parts; and putting the to-be-welded parts into a vacuum brazing furnace for vacuum brazing treatment. In the soldering process, the composite soldering material has good wettability for the ceramic and ceramic materials, and the obtained welding joint has no crack, the shear strength between 16 and 45MPa, and good mechanical properties.

Description

technical field [0001] The invention relates to a composite solder and a brazing method for brazing metal and ceramics or ceramic-based composite materials. Background technique [0002] The connection between ceramics and metals can overcome the inherent brittleness of ceramic materials, difficulty in sintering, and difficulty in preparing large-scale and complex components, and can obtain composite components with both excellent performances of ceramics and metal materials. Therefore, high thrust-to-weight ratio in the future Aviation engines, satellite attitude control engines, hypersonic ramjet engines, cruise missile engines, liquid and solid rocket engines and other weapons and equipment fields have broad prospects for promotion and application. Titanium alloy materials with excellent comprehensive properties such as high specific strength, corrosion resistance, and high temperature resistance are important materials for manufacturing aeroengines and aircraft body stru...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B23K35/30B23K1/008B23K103/16
Inventor 何鹏林铁松黄超
Owner HARBIN INST OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap