Stoneware sheet and preparation method thereof

A thin plate and stoneware technology, applied in the field of building decoration materials, can solve the problems of difficult to make large-sized thin plate bricks, limit the application of building decoration, and high water absorption, achieve natural and realistic colors, reduce load-bearing, and solve the problem of brittleness. Effect

Active Publication Date: 2010-12-01
MONALISA GRP CO LTD
View PDF4 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, stoneware bricks have the disadvantages of high water absorption and poor strength, making it difficult to make large-scale thin-slab bricks, which limits their application in modern architectural decoration

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] The raw material composition of the base material is (percentage by weight): 10% of flake soil, 20% of potash sand, 18% of sodium stone powder, 8% of potassium sodium stone grain, 26% of mixed mud, and the fiber reinforcing agent added therein is acicular silica fume Stone 18%, which is a natural mineral fiber with a diameter of 5 μm and an aspect ratio of 15 to 18. The main chemical composition is SiO 2 ≥51%, CaO ≥45%. In addition, 0.1% polyvinyl alcohol and 0.1% carboxymethyl cellulose sodium are added to the raw materials.

[0025] The main chemical composition of the base material prepared by adopting the multi-element fast analyzer (DHF82 type, purchased from Xiangtan Xiangyi Instrument Co., Ltd.) above-mentioned raw material is (weight percent): SiO 2 66.8%, Al 2 o 3 18.8%, Fe 2 o 3 0.8%, TiO 2 0.4%, CaO 8.0%, MgO 0.7%, K 2 O+Na 2 O 4.5%.

[0026] Concrete preparation method is as follows:

[0027] 1) The acicular wollastonite is separately slurried by a...

Embodiment 2

[0033] The raw material of base material is composed of (percentage by weight): 10% of flake soil, 20% of potassium sand, 14% of sodium stone powder, 8% of potassium sodium stone grain, 26% of mixed mud, and the fiber reinforcing agent added therein is basalt mineral fiber ( Purchased from Qingyuan Boer Fiber Co., Ltd.) 22%, which is a natural mineral fiber with a diameter of 4 μm and an aspect ratio of 30, and its main chemical composition is SiO 2 50%, Al 2 o 3 20%, CaO+MgO 28%. In addition, 0.08% polyvinyl alcohol and 0.12% modified starch are added to the raw material.

[0034] The main chemical composition of the base material prepared by above-mentioned raw material is (percentage by weight): SiO 2 65%, Al 2 o 3 20.6%, Fe 2 o 3 1.2%, TiO 2 0.8%, CaO 3.8%, MgO 2.4%, K2 O+Na 2 O4.8%.

[0035] The specific preparation method is as follows: the basalt mineral fiber is individually pulped with a 14-ton small ball mill, and the remaining raw materials are fed into a ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Destruction strengthaaaaaaaaaa
Diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides a stoneware sheet and a preparation method thereof. The stoneware sheet comprises the following chemical components in percentage by weight: 55-68% of SiO2, 14-28% of Al2O3, 0.5-1.8% of Fe2O3, 0.2-1.5% of TiO2, 1-12% of CaO, 0.3-1% of MgO, 2-5% of K2O and Na2O and 5-30% of fiber reinforcer. The preparation method comprises the following steps: independently ball-milling and pulping the fiber reinforcer, mixing with other pulping raw materials, carrying out spray granulation, and dry-pressing to obtain the green body. The stoneware sheet has the advantages of favorable adhesiveness, high strength, favorable flatness, high resilience and flexibility, high abrasive resistance, favorable anti-fouling performance, fire resistance, high temperature resistance, long service life, no radioactive contamination, light weight and the like.

Description

technical field [0001] The invention relates to the technical field of building decoration materials, in particular to a stoneware veneer and a preparation method thereof. Background technique [0002] With the increase of product specifications, the thickness of general ceramic tiles is also increasing. Ceramic tiles consume more raw materials per unit area, which not only increases the load of the building, but also causes a large consumption of materials. Thin-slab bricks can save raw materials and reduce energy consumption in the preparation process, which has become the future development trend of the ceramic industry. [0003] Due to its certain water absorption, stoneware bricks are widely used in kitchen and bathroom floor decoration. However, stoneware bricks have the disadvantages of high water absorption and poor strength, making it difficult to make large-scale thin-slab bricks, which limits their application in modern architectural decoration. Contents of th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B35/18C04B35/622E04C2/04
Inventor 刘一军潘利敏汪庆刚杨晓峰
Owner MONALISA GRP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com