Nylon composite material special for electric wire and cable jacket and preparation method thereof

A nylon composite material, wire and cable technology, applied in the direction of insulating cables, cables, circuits, etc., can solve the problems of great human body and environmental pollution, immature research and application, etc., achieve good anti-oxidation effect, good anti-ultraviolet absorption, Excellent wear-resistant effect

Active Publication Date: 2012-05-23
辰东意普万新材料(广东)有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Anti-termite, anti-mouse, durability and corrosion resistance are long-term problems to be solved in the field of wire and cable. In the past, various additives such as dieldrin, aldrin or chlordane were used to prevent termites. However, these additives volatilized A large number of irritating and toxic gases pollute the human body and the environment greatly. Therefore, nylon materials are used internationally to prepare wire and cable sheaths to achieve the purpose of preventing rodents and ants. Nylon has high insulation and strong hardness, which can Resistant to termites, and nylon-sheathed wires and cables made of nylon are durable and corrosion-resistant
However, at present, the research and application in this area in our country is not mature.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A special nylon composite material for wire and cable sheathing. The components and the mass percentages of each component are as follows:

[0030] PA6 93.9%

[0031] Main antioxidant 0.3%

[0032] Auxiliary antioxidant 0.3%

[0033] Lubricating release agent 1.0%

[0034] Light stabilizer 0.5%

[0035] Lubricant 2.0%

[0036] Nucleating agent 1.0%,

[0037] Tackifier 1.0%

[0038] The main antioxidant is hindered phenolic antioxidant 1010, the auxiliary antioxidant is phosphite antioxidant tris[2.4-di-tert-butylphenyl] phosphite, and the lubricating mold release agent is selected From calcium stearate, the light stabilizer is selected from hindered phenol light stabilizer 770, light stabilizer 6911, light stabilizer 622, or a mixture of the above substances, and the lubricant is selected from ethylene bis stearamide, The nucleating agent is nano talc, and the tackifier is nylon 6: M1251 containing reactive groups.

[0039] The preparation method of the special nylon composite mater...

Embodiment 2

[0044] A special nylon composite material for wire and cable sheathing. The components and the mass percentages of each component are as follows:

[0045] PA6 96%

[0046] Main antioxidant 0.5%

[0047] Auxiliary antioxidant 0.5%

[0048] Lubricating release agent 0.8%

[0049] Light stabilizer 0.5%

[0050] Lubricant 1.0%

[0051] Nucleating agent 0.2%,

[0052] Tackifier 0.5%

[0053] The main antioxidant is a mixture of hindered phenolic antioxidant 1098 and antioxidant 1076, and the auxiliary antioxidant is a mixture of phosphite antioxidant tridecyl ester and tris(dodecanol) ester, The lubricating release agent is selected from calcium stearate, the light stabilizer is selected from a mixture of hindered phenolic light stabilizers 6911 and 622, the lubricant is selected from silicone powder, and the nucleating agent is selected from nano-talc , The tackifier is selected from nylon 6 containing reactive groups: maleic anhydride grafted nylon 6.

[0054] The preparation method of the sp...

Embodiment 3

[0059] A special nylon composite material for wire and cable sheathing. The components and the mass percentages of each component are as follows:

[0060] PA6 94.7%

[0061] Main antioxidant 0.3%

[0062] Auxiliary antioxidant 0.3%

[0063] Lubricating release agent 0.3%

[0064] Light stabilizer 1.5%

[0065] Lubricant 2.0%

[0066] Nucleating agent 0.1%,

[0067] Tackifier 0.8%

[0068] The main antioxidant is a hindered phenolic antioxidant 2,6-tertiary butyl-4-methylphenol, and the auxiliary antioxidant is a thiodipropionate antioxidant ditetradecyl alcohol The lubricating release agent is selected from calcium stearate, the light stabilizer is selected from light stabilizer 622, the lubricant is selected from a mixture of ethylene bis-stearamide and silicone powder, and the nucleating agent Nano talc powder is selected, and the tackifier is M1251 and maleic anhydride grafted nylon 6.

[0069] The preparation method of the special nylon composite material for wire and cable sheath incl...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a nylon composite material special for an electric wire and cable jacket, which is prepared from the following components by mass percent: 86-96% of nylon 6, 0.1-2.0% of main antioxygen, 0.1-2.0% of auxiliary antioxygen, 0.1-2.0% of lubricant release agent, 0.1-2.0% of light stabilizer, 0.1-2.0% of lubricant, 0.1-2.0% of nucleating agent and 0.3-2.0% of tackifier, wherein the main antioxygen is a hindered phenol antioxygen, the auxiliary antioxygen is thiodi-propionic acid diester or phosphite ester, the lubricant release agent is calcium stearate, the light stabilizeris a hindered amine light stabilizer, the lubricant is ethylene double hard ester amide (EBS), silicone powder or a compositor of the ethylene double hard ester amide (EBS) and silicone powder, the nucleating agent is nano talcum powder, and the tackifier is nylon 6 containing reactive groups. The nylon composite material has the advantages of simple formula and cheap, easily available components and low cost, and the electric wire and cable jacket prepared from the nylon composite material can prevent white ants and mousse, has abrasion resistance and corrosion resistance, is durable in use and is non-toxic and environment-friendly.

Description

Technical field [0001] The invention belongs to the technical field of wire and cable materials, and particularly relates to a special nylon composite material for wire and cable sheaths and a preparation method thereof. Background technique [0002] Anti-termite, anti-mouse, durability and corrosion resistance are long-standing problems that need to be solved in the field of wire and cable. In the past, various additives such as dieldrin, aldrin or chlordane were used to prevent termites, but these additives volatilize A large number of irritating and toxic gases are extremely polluting to the human body and the environment. For this reason, nylon materials are used to prepare wire and cable sheaths in the world to achieve the purpose of preventing rodents and ants. Nylon has high insulation and strong hardness. Resistant to termite erosion, and nylon sheathed wires and cables made of nylon are durable and corrosion-resistant. However, at present, my country's research and appl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L77/02C08L51/08C08K13/02C08K5/372C08K5/524C08K5/098C08K3/34C08K5/526H01B7/17
Inventor 高原梁效礼杨冬黄俊辉
Owner 辰东意普万新材料(广东)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More