High-performance epoxy resin composition for sheet molding compound (SMC)

A technology of epoxy resin and composition, applied in application, household appliances, flat products, etc., can solve the problems of high viscosity of epoxy resin, long curing time, inability to chemically thicken, etc., and achieve effective viscosity, excellent mechanical strength, The effect of shortening the curing time

Active Publication Date: 2012-02-01
北京蓝星清洗有限公司
View PDF4 Cites 24 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, epoxy resin also has disadvantages such as high viscosity, inability to ch

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0021] Example 1

[0022] 81.0g bisphenol A glycidyl ether epoxy resin E-51 (purchased from Wuxi Resin Factory of Bluestar New Chemical Materials Co., Ltd., with an epoxy value of 0.48-0.54), and 9.0g glycidylamine epoxy resin JEh-012 (purchased from Changshu Jiafa Chemical Co., Ltd., epoxy value 0.80-0.85) was mixed, and then added 18.0g dicyandiamide and 18.0g 4,4'-diaminodiphenyl sulfone (DDS) mixture , Then add 2.0g zinc stearate and 45.0g calcium carbonate in sequence, stir well, then add 18.0g toluene diisocyanate and 9.0g polyethylene glycol, continue to stir evenly to obtain the epoxy matrix resin, namely ESMC resin paste. The prepared ESMC resin paste is impregnated with 15-45mm random chopped glass fibers on the impregnating machine, and rolled by a sheet machine using an easily peelable polyethylene film as the diaphragm, and stored at 50°C for 3-4 days (thickening ) The ESMC sheet molding material is obtained. Differential scanning calorimetry (DSC method) thermal ...

Example Embodiment

[0023] Example 2

[0024] 72.0g bisphenol A glycidyl ether epoxy resin E-51 (purchased from Wuxi Resin Factory of Bluestar New Chemical Materials Co., Ltd., with an epoxy value of 0.48-0.54), 18.0g glycidylamine epoxy resin JEh-012 (purchased from Changshu Jiafa Chemical Co., Ltd., epoxy value 0.80-0.85) was mixed, and then added 18.0g dicyandiamide and 18.0g 4,4'-diaminodiphenyl sulfone (DDS) mixture , Then add 2.0g zinc stearate and 45.0g calcium carbonate in sequence, stir well, then add 18.0g toluene diisocyanate and 9.0g polyethylene glycol, continue to stir evenly to obtain the epoxy matrix resin, namely ESMC resin paste. The prepared ESMC resin paste is impregnated with 15-45mm random chopped glass fibers on the impregnating machine, and rolled by a sheet machine using an easily peelable polyethylene film as the diaphragm, and stored at 50°C for 3-4 days (thickening ) The ESMC sheet molding material is obtained. Differential scanning calorimetry (DSC method) thermal ana...

Example Embodiment

[0025] Example 3

[0026] 63.0g bisphenol A glycidyl ether epoxy resin E-51 (purchased from Wuxi Resin Factory of Bluestar New Chemical Materials Co., Ltd., with an epoxy value of 0.48-0.54), 27.0g glycidylamine epoxy resin JEh-012 (purchased from Changshu Jiafa Chemical Co., Ltd., epoxy value 0.80-0.85) was mixed, and then added 18.0g dicyandiamide and 18.0g 4,4'-diaminodiphenyl sulfone (DDS) mixture , Then add 2.0g zinc stearate and 45.0g calcium carbonate in sequence, stir well, then add 18.0g toluene diisocyanate and 9.0g polyethylene glycol, continue to stir evenly to obtain the epoxy matrix resin, namely ESMC resin paste. The prepared ESMC resin paste is impregnated with 15-45mm random chopped glass fibers on the impregnating machine, and rolled by a sheet machine using an easily peelable polyethylene film as the diaphragm, and stored at 50°C for 3-4 days (thickening ) The ESMC sheet molding material is obtained. Differential scanning calorimetry (DSC method) thermal ana...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a high-performance epoxy-based resin composition suitable for sheet molding compound (SMC) molding. The epoxy-based resin composition is prepared from the following components in parts by mass: 100 parts of mixed epoxy resin, 20-60 parts of curing agent, 10-40 parts of thickening agent, 0.5-5.0 parts of internal demolding agent and 50-120 parts of filler. The epoxy-based resin is separately selected from glycidyl ether epoxy resin and glycidyl amine epoxy resin or glycidyl ester epoxy resin, the epoxy resin composition has good wettability and bonding strength to fibers, the cured product has excellent heat resistance and mechanical strength, and the epoxy sheet molding compound prepared from the epoxy resin composition provided by the invention is suitable for the occasions with strict requirements on temperature resistance, corrosion resistance and insulation property.

Description

technical field [0001] The invention relates to an epoxy resin composition, especially a high-performance epoxy matrix resin composition suitable for SMC molding, and also relates to a preparation method of the epoxy resin composition. Background technique [0002] SMC molding technology is a closed mold molding composite material technology. It has many advantages over other open molding techniques. Especially because SMC is a closed-mold molding technology, the styrene volatilization during the molding process is significantly lower than that of open-mold molding, realizing a green and environmentally friendly molding process. Therefore, SMC molding technology has attracted more and more attention. [0003] At present, SMC is mainly based on unsaturated polyester resin. However, this kind of unsaturated polyester resin SMC has disadvantages such as temperature resistance, corrosion resistance, relatively poor insulation effect, and low structural strength, so it cannot b...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L63/02C08L63/00C08K13/02C08K5/098C08K5/29C08K3/26C08K3/22C08J5/18B29D7/01
Inventor 杨刚孟秀青胡伟陈伟明刘欣彤
Owner 北京蓝星清洗有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap