Preparation method of polystyrene/gold composite microspheres

A polystyrene microsphere and polystyrene technology, which is applied in the field of nano-functional materials, can solve the problems of time-consuming and laborious, low coverage, affecting the uniformity and controllability of gold particle distribution, etc., so as to simplify the preparation process and simplify the Operation steps, the effect of shortening the preparation time

Inactive Publication Date: 2012-02-22
WUHAN UNIV
View PDF3 Cites 29 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The above-mentioned traditional preparation methods have their own characteristics, but there are also certain shortcomings.
The layer-by-layer self-assembly method (LbL) can obtain a single-layer or multi-layer polyelectrolyte with high coverage and simple operation, but the intermediate process needs to be repeated, which is time-consuming and laborious
Reference 5 Unmodified polystyrene microsphere surface assembly of gold particles, although the steps are simplified, but it will inevitably affect the uniformity and controllability of the distribution of gold particles on polystyrene microspheres
However, the in situ reduction method has poor binding and low coverage between gold particles and polystyrene microspheres, which greatly affects the morphology, structure and characteristics of polystyrene / gold composite microspheres.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of polystyrene/gold composite microspheres
  • Preparation method of polystyrene/gold composite microspheres
  • Preparation method of polystyrene/gold composite microspheres

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] In a three-neck flask, dissolve 0.0244 g of sodium lauryl sulfate and 0.0222 g of potassium persulfate in a mixed solution of ethanol (95%) / water (50ml:20ml), and stir under the protection of argon. Add 1 ml of styrene monomer washed with 10% sodium hydroxide solution dropwise to the solution, heat to 70 ℃, and react for 8 h. After the reaction, it was centrifuged and washed with ethanol for 3 times; using 95% ethanol as a solvent, a 1 mg / ml ethanol solution of polystyrene microspheres was prepared. The particle size of the polystyrene microspheres obtained by the reaction is about 300 nm.

[0033] At room temperature, add 0.4 ml of the ethanol solution of 3-aminopropyltriethoxysilane with a volume ratio of 1:49 to 20 ml of the ethanol solution of 1 mg / ml polystyrene. Stir magnetically and react for 2 h. The aminated polystyrene microspheres were centrifuged and washed with ethanol several times, then dispersed in double-distilled water to make a 1 mg / ml aqueous solution...

Embodiment 2

[0036] The 300 nm polystyrene emulsion and the aminated polystyrene aqueous solution in Example 1 were used and allowed to stand for 13 hours to fully disperse.

[0037] At room temperature, add 0.6 ml of 1 wt% chloroauric acid aqueous solution to the aminated polystyrene aqueous solution, magnetically stir and heat to boiling, add 2.4 ml of 1 wt% trisodium citrate aqueous solution, and react for 30 min , The reaction system is dark purple. The polystyrene / gold composite microspheres were centrifuged and washed with double distilled water several times. Transmission electron microscopy showed that the product was gold nanoparticles uniformly and densely attached to the surface of polystyrene microspheres, and the average particle size of the gold nanoparticles was 8.0±2.0 nm. And the number of gold colloid particles adsorbed on the surface of a single polystyrene microsphere is about 413.

Embodiment 3

[0039] The 300 nm polystyrene emulsion and the aminated polystyrene aqueous solution in Example 1 were used and allowed to stand for 22 hours to fully disperse.

[0040] At room temperature, add 0.2 ml of 1 wt% chloroauric acid aqueous solution to the aminated polystyrene aqueous solution, magnetically stir and heat to boiling, add 0.8 ml of 1 wt% trisodium citrate aqueous solution, and react for 30 min , The reaction system is purple-red. The polystyrene / gold composite microspheres were centrifuged and washed with double distilled water several times. Transmission electron microscopy showed that the product was gold nanoparticles uniformly attached to the surface of the polystyrene microspheres, and the average particle size of the gold nanoparticles was 6.5±1.8 nm. And the number of gold colloidal particles adsorbed on the surface of a single polystyrene microsphere is about 140.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a preparation method of polystyrene / gold composite microspheres, which comprises the following steps: modifying polystyrene microspheres with a silane coupling agent, mixing with a chloroauric acid solution, and heating to carry out ionic selfassembly, wherein gold ions are fixed to the surface of the polystyrene microspheres through gold-nitrogen bonds; and after the solution is boiling, adding trisodium citrate to reduce the gold ions adsorbed onto the amino group in situ, thereby generating the core-shell structure in which a gold nanoparticle is coated on each polystyrene microsphere. The size of the gold particles and the coverage percentage of the gold particles on the polystyrene microspheres are controllable to some extent.

Description

Technical field [0001] The invention belongs to the technical field of nano functional materials, and specifically relates to a preparation method of polystyrene / gold composite microspheres. Background technique [0002] Composite nanomaterials not only have the characteristics of each constituent material, but also have new properties, which expand the application range of the material. Among them, the core-shell structure of polystyrene / gold composite microspheres have specific morphology, structure and physical and chemical properties, which are expected to be widely used in catalysis, photosensitive devices, temperature sensing, surface enhanced Raman scattering effect, immunodetection, etc. Therefore, the research on its preparation, performance and application has always been one of the subjects that materials scientists are keen on. The preparation method of polystyrene / gold composite microspheres directly affects the performance of the composite microspheres, and self-as...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08J7/12C08L25/06C08K3/08
Inventor 周娟任峰张少锋吴伟肖湘衡蒋昌忠
Owner WUHAN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com