An environmentally friendly stabilizer and high-efficiency technology, which is applied in the field of PVC processing aids and can solve problems such as thermal decomposition of PVC profiles

Active Publication Date: 2013-09-11
SHANDONG RUIFENG CHEM
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0010] The purpose of the present invention is to provide a high-efficiency environment-friendly stabilizer for PVC profiles, which not only solves the problem of thermal decomposition in the process of PVC profile processing, but also solves the problems caused by long-term sunlight and exposure to air in the daily use of PVC profiles. The resulting discoloration problem meets the needs of domestic profile development

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-efficiency environment-friendly stabilizing agent used for PVC section bars
  • High-efficiency environment-friendly stabilizing agent used for PVC section bars
  • High-efficiency environment-friendly stabilizing agent used for PVC section bars

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] (1) Accurately weigh calcium stearate and calcium zinc stearate, pentaerythritol ester, antioxidant 1010, ultraviolet absorber, magnesium aluminum hydrotalcite, stearoyl benzoyl methane, 1-methyl-2-benzene After mixing, kneading and granulating the base indole according to the conventional process, take out 4 parts, add it to the following PVC formula, put it into a small high-speed mixing mixer, raise it to 115°C to release, and cool for later use.

[0039] Table 1 PVC formula

[0040] PVC

100

Epoxidized soybean oil

1.0

CaCO 3

8

Toughening agent CPE

8

Processing aid ACR401

2

Titanium Dioxide

5

Lubricant PE wax

0.3

[0041] (2) Dynamic thermal stability

[0042] Put the mixed materials in the previous step into the double-roll plastic mill, and continue mixing at a constant roll temperature (about 190℃) and roll distance (1mm). The timing starts when the materials are added, and a sample is taken every two minutes thereafter. Take 7 samples from...

Embodiment 2～3

[0046] Except for the addition of polyol ester, the others are the same as in Example 1. See Table 2 and Table 3 for details and performance test results.

Embodiment 4～6

[0048] Except for the addition of different antioxidants, the rest are the same as in Example 1. See Table 2 and Table 3 for details and performance test results.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a high-efficiency environment-friendly stabilizing agent used for PVC section bars, which belongs to the technical field of PVC processing aids. The stabilizing agent comprises the following raw materials by weight: 20 to 30 of calcium stearate, 20 to 30 of zinc stearate, 10 to 15 of polyol ester, 1 to 3 of an anti-oxidant, 0.5 of an ultraviolet ray absorber, 10 to 30 of hydrotalcite, 3.5 of beta-diketone, 5 to 15 of alpha-phenylindole and 8 to 15 of epoxy compounds. The invention enables the problem of thermal decomposition of PVC section bars during processing to be overcome and the problem of discoloring because of long-term illumination and exposure in air during daily usage of PVC section bars to be solved, meeting developmental needs of section bars in China.

Description

Technical field [0001] The invention relates to a high-efficiency environmental protection stabilizer for PVC profiles, belonging to the technical field of PVC processing aids. Background technique [0002] As we all know, PVC resin and its products have the shortcomings of easy thermal degradation and aging due to their own structural defects. Its processing temperature (above 160°C) is higher than the decomposition temperature (120-130°C), so it is necessary to turn PVC into For products, heat stabilizers must be added during the PVC processing and molding process to delay and prevent the thermal degradation of PVC resin. Lead salt is the first heat stabilizer used, with strong stabilizing effect and low price, but it will cause certain environmental pollution during production and use. Since 2000, European countries such as Norway, Finland, Sweden, Denmark and the United Kingdom have successively taken actions to ban lead salt stabilizers. Since 2003, my country has also beg...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08L27/06C08K13/02C08K5/00C08K5/098C08K5/103C08K5/524C08K3/26C08K5/07C08K5/3417
Inventor 张振国呼建强刘春信冯健葛峰
Owner SHANDONG RUIFENG CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka