Noble metal/TiO2-C catalyst

A precious metal and catalyst technology, applied in the field of precious metal/TiO2-C catalyst and its preparation, can solve the problems of difficult hydrogenation of colored impurities, and achieve the effects of abundant mesopores, improved conversion rate, large specific surface area and pore volume

Active Publication Date: 2013-10-09
CHINA PETROLEUM & CHEM CORP +1
View PDF12 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] Pd / TiO for the crude terephthalic acid hydrorefining process in the prior art 2 Catalysts have disadvantages such as difficult hydrogenation of colored impurities. The purpose of the present invention is to provide a TiO 2 - Highly active noble metal / TiO with C as the carrier 2 -C Catalyst

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] (1) 2 g phenolic resins are added in 20 g ethanol, obtain the ethanolic solution containing phenolic resins;

[0045] (2) The specific surface area of ​​20 g is 300 m 2 / g, pore volume 0.6 cm 3 / g, anatase TiO 2 16 g of the powder was added to the ethanol solution containing phenolic resin obtained in (1), stirred evenly at room temperature, and the ethanol was evaporated under reduced pressure at 80 °C to obtain phenolic resin-modified TiO 2 Powder, crushed for later use;

[0046] (3) TiO modified with the phenolic resin obtained in (2) 2 powder and the remaining 4 g TiO 2 After the powder is mixed evenly, it is mixed with 10 g of gel containing water, binder methylcellulose, and peptizing agent nitric acid, kneaded evenly on a kneader, and extruded. The obtained molding was cured at 120 °C for 10 h, and then fired at 700 °C for 4 h under a nitrogen atmosphere to obtain TiO 2 -C composite carrier with a compressive strength of 132 N / cm and a specific surface area...

Embodiment 2

[0051] Basically the same as Example 1, but with the following changes:

[0052] A solution containing palladium acetate and platinum tetrachloride was sprayed on TiO 2 -C composite support, make palladium acetate and platinum tetrachloride supported on TiO 2 - on the composite carrier of C, obtain the catalyst precursor;

[0053] The catalyst precursor was dried at 100 °C for 2 h, and then reduced with an aqueous solution of sodium formate at 60 °C for 2 h to obtain 0.1%Pd-1.0%Pt / TiO 2 -C noble metal catalyst, the mass ratio between Pd and Pt is 0.1.

[0054] The catalyst obtained in this example was used in the hydrogenation process of 2,6-dicarboxyanthraquinone, and the conversion rate of 2,6-dicarboxyanthraquinone was 99.6%.

Embodiment 3

[0056] Basically the same as Example 1, but with the following changes:

[0057] TiO 2 -C composite support is impregnated with a solution containing palladium nitrate and platinum nitrate, so that palladium nitrate and platinum nitrate are loaded on TiO 2 - on the composite carrier of C, obtain the catalyst precursor;

[0058] The catalyst precursor was dried at 100 °C for 2 h, and then reduced with an aqueous solution of sodium formate at 60 °C for 2 h to obtain 1.0%Pd-0.1%Pt / TiO 2 -C noble metal catalyst, the mass ratio between Pd and Pt is 10.

[0059] The catalyst obtained in this example was used in the hydrogenation process of 2,6-dicarboxyanthraquinone, and the conversion rate of 2,6-dicarboxyanthraquinone was 99.7%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
pore sizeaaaaaaaaaa
specific surface areaaaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to View More

Abstract

The invention discloses a noble metal / TiO2-C catalyst for removing p-carboxybenzaldehyde, 2,6-dicarboxyl anthraquinone, 2,6-dicarboxyl fluorenone, and other colored impurities from crude p-phthalic acid. The noble metal / TiO2-C catalyst of the present invention can be used for the hydrogenation refinement process of the crude p-phthalic acid. With the noble metal / TiO2-C catalyst of the present invention, the contents of the p-carboxybenzaldehyde, the 2,6-dicarboxyl anthraquinone, the 2,6-dicarboxyl fluorenone, and other colored impurities can be significantly reduced.

Description

technical field [0001] The present invention relates to a noble metal / TiO for hydrogenation reaction 2 -C Catalyst and its preparation method, especially related to noble metal / TiO used for removing colored impurities such as p-carboxybenzaldehyde, 2,6-dicarboxyanthraquinone, 2,6-dicarboxyfluorenone, etc. in crude terephthalic acid 2 -C catalyst and preparation method. Background technique [0002] Purified terephthalic acid (PTA) is a very important organic chemical raw material, and its downstream processing products are mainly polyester fibers, polyester films, packaging bottles and PET engineering plastics. In the crude terephthalic acid (CTA) produced by the liquid-phase oxidation of p-xylene (PX), it generally contains 2000-3000 μg / g p-carboxybenzaldehyde (4-CBA) and a small amount of 2,6-dicarboxylate Anthraquinone, 2,6-dicarboxyfluorenone and other polycyclic aromatic colored impurities are more harmful, not only affecting the melting point of polyester, but also a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J23/46B01J23/44B01J23/42B01J21/18B01J35/10C07C63/26C07C51/487
Inventor 堵文斌王继元曾崇余卞伯同许建文陈韶辉柏基业朱庆奋庞焱
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com