Dye photosensitive resin composition, pattern forming method, color filter, method for making the same, and display apparatus

A technology of photosensitive resin and composition, which is applied in the direction of optical filter, photographic plate-making process of pattern surface, photosensitive material used in photomechanical equipment, etc., which can solve the problem of brightness reduction, coloring of cured film, and inability to obtain sufficient curing sensitivity and other problems, to achieve the effect of good brightness, good developability, and excellent linearity

Inactive Publication Date: 2012-05-30
FUJIFILM CORP
View PDF123 Cites 26 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] However, the conventional photosensitive resin composition containing an oxime ester compound as a photopolymerization initiator has a problem that sufficient curing sensitivity cannot be obtained when a colorant is contained in a large amount as in color filter applications.
In addition, when post-heating (post-baking) is performed on the cured film in order to further improve the curability, there is also a problem that unwanted coloring occurs in the cured film.
Undesired coloring in the cured film can cause performance degradation such as brightness reduction, especially when the cured film is applied to a colored pattern of a color filter

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Dye photosensitive resin composition, pattern forming method, color filter, method for making the same, and display apparatus
  • Dye photosensitive resin composition, pattern forming method, color filter, method for making the same, and display apparatus
  • Dye photosensitive resin composition, pattern forming method, color filter, method for making the same, and display apparatus

Examples

Experimental program
Comparison scheme
Effect test

example

[0432] Hereinafter, although an example demonstrates this invention more concretely, this invention is not limited to the following example unless the summary is exceeded. In addition, unless otherwise specified, "%" and "part" are based on weight.

Synthetic example 1

[0433] Synthesis Example 1: Synthesis of Alkali-Soluble Resin 1 Having Allyl Group

[0434] 54 g of 1-methoxy-2-propanol was added to a three-neck flask with a capacity of 200 mL equipped with a stirring bar having a stirring blade, a reflux condenser, and a thermometer, and heated to 70° C. under a nitrogen stream. Using a plunger pump, 10.07 g of allyl methacrylate and 1.93 g of methacrylate as a polymerization initiator were dissolved in 54 g of 1-methoxy-2-propanol over 2.5 hours. A solution of 0.185 g of 2,2'-azobis(2,4-dimethylvaleronitrile) was added dropwise into the three-necked flask. After completion of the dropwise addition, it was further stirred at 70° C. for 2 hours. After heating, it was poured into 1 L of water for reprecipitation. The precipitate was filtered and vacuum-dried to obtain 9 g (75% yield) of a polymer compound.

[0435] As a measurement sample of the weight average molecular weight, 0.01 g of the obtained polymer was weighed into a 10 mL...

example 1

[0453] Preparation of Green Colored Photosensitive Resin Composition

[0454] The following components were stirred and mixed to prepare a green colored photosensitive resin composition.

[0455] 32.68 parts of the dispersion liquid of the green pigment PG58

[0456] 14.56 parts of the dispersion liquid of the yellow pigment PY150

[0457] ・Binder resin: 0.65 parts of Exemplified Compound 1-1

[0458] ・Polymerizable compound: TO-2349 (carboxyl group-containing polyfunctional monomer) 5.16 parts

[0459] (Toagosei Co., Ltd., ARONIX TO-2349, acid value 67mgKOH / g)

[0460] · Specific starter A 0.9 parts

[0461] (The following structure, product name: TR-PBG-304, manufactured by Changzhou Qiangli Electronic New Material Co., Ltd.)

[0462]

[0463] · 0.2 parts of multifunctional thiol compound

[0464] (The following structure, trade name: KARENZ MTBD1, manufactured by Showa Denko Co., Ltd.)

[0465]

[0466] Solvent: 23.5 parts of 3-eth...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
acid valueaaaaaaaaaa
acid valueaaaaaaaaaa
Login to view more

Abstract

The invention provides a dye photosensitive resin composition featuring high harden sensitivity and excellent display and capable of forming dye harden film having excellent heat resistance and expected color tone, a pattern forming method employing the dye photosensitive resin composition, a method for making color filter, a color filter, and a display element having the color filter. The dye photosensitive resin composition at least comprises a colorant, bonding resin, polymerism composition, a photopolymerization starting agent shown in the general formula (I), multifunctional mercaptan composition, and a solvent. In the formula (I), R1 represents a univalent substituent group containing aromatic nucleus or heteromatic nucleus. X1, X2, X3, and X4 independently represent hydrogen atom, halogen atom, or alkyl respectively; Y represents single bond or carbonyl; and Z represents methyl or phenyl.

Description

technical field [0001] The present invention relates to a colored photosensitive resin composition, a pattern forming method, a method for producing a color filter, a color filter, and a display device including the color filter. Background technique [0002] In recent years, the development of liquid crystal display devices has expanded from personal computers or monitors with relatively small screen areas to televisions with large screens and high image quality. [0003] Liquid crystal display devices for televisions require higher image quality, that is, improvements in contrast and color purity, compared to conventional monitor applications. In order to improve contrast, the particle size of the coloring agent (organic pigment etc.) used for the colored photosensitive resin composition for forming a color filter is required to be finer. In addition, in order to improve the color purity, it is required that the content of the coloring agent (organic pigment) in the solid...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): G03F7/027G03F7/004G03F7/00G02B5/20G02F1/1335
Inventor 中村秀之长田崇一郎藤本进二
Owner FUJIFILM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap