Preparation method of nano porous high-efficiency heat insulation board

A nanoporous, heat-insulating board technology, applied in chemical instruments and methods, layered products, metal layered products, etc., can solve the problems of insufficiency of heat-insulating materials, achieve simple and feasible preparation methods, good heat-insulating performance, strong effect

Active Publication Date: 2012-06-27
SINOSTEEL LUOYANG INST OF REFRACTORIES RES
View PDF5 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, traditional thermal insulation materials are difficult to meet the higher requirements for thermal insulation materials such as civilian high-efficiency energy-saving and military equipment.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] Add 1000g of nano-alumina powder into a high-speed mixer, and add 5g of zinc oxide, 100g of dibutyl phthalate, 1g of PEG600, 5g of sodium lauryl sulfate, 50g of polyvinyl alcohol and 250g of Ethanol, stirred at high speed until uniformly mixed; put the uniformly mixed material into the prepared mold, and use a press to dry press it under a pressure of 10MPa to form it. The thickness of the formed sample is 10mm; control the drying conditions, and the temperature is controlled at 20 ℃, relative humidity controlled at 40%, after drying, cover with 0.1mm thick aluminum foil to get nanoporous high-efficiency heat insulation board.

Embodiment 2

[0025] Use a high-speed mixer to break 30g of glass fiber, then add 1000g of nano-silicon dioxide powder, and stir evenly; add 5g of potassium hexatitanate, 5g of potassium hexatitanate, and 5g of Monoethylhexyl phthalate, 50g PEG400, 30g sodium cetyl sulfate, 350g dextrin and 250g methanol, stirred at high speed until uniformly mixed; Dry press under a pressure of 10MPa to form it. The thickness of the formed sample is 10mm; control the drying conditions, the temperature is controlled at 60°C, and the relative humidity is controlled at 90%. After drying, cover it with 0.5mm thick aluminum foil to obtain nanoporous Efficient insulation panels.

Embodiment 3

[0027] Add 1000g of nano-silica powder into a high-speed mixer, and add 5g of titanium dioxide, 5g of diisodecyl phthalate, 1g of PEG500, 5g of sodium dodecylbenzenesulfonate, and 50g of epoxy Resin and 3000g water were stirred at high speed until uniformly mixed to obtain a slurry; molded by tape casting equipment, the thickness of the molded sample was 1mm; the drying conditions were controlled, the temperature was controlled at 20°C, and the relative humidity was controlled at 90%. After covering with 0.1mm thick aluminum foil, a nanoporous high-efficiency heat insulation board can be obtained.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
lengthaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention provides a preparation method of a nano porous high-efficiency heat insulation board, belonging to the field of nano porous heat insulation materials. The preparation method comprises the following processes: uniformly mixing nano powder with fiber, a bonding agent, an opacifier, a plasticizer, a drying control agent, a dispersant and a right amount of dry-and-wet degree regulating reagent in a mechanical and chemical dispersion combined method; moulding in a manner of dry pressing moulding, curtain coating moulding or extrusion moulding and the like; and controlling drying conditions, drying a moulded sample, and then coating a reflecting layer with certain thickness and material quality, thus obtaining the nano porous high-efficiency heat insulation board. The invention has the advantages that the preparation method is simple and feasible, the prepared nano porous heat insulation board has high strength, uniform hole structure and good heat insulation performance.

Description

technical field [0001] The invention relates to a preparation method of a nanoporous high-efficiency heat insulation board, belonging to the field of nanoporous heat insulation materials. technical background [0002] With the development of social economy, the global energy consumption has risen sharply, and the shortage of energy has become a worldwide problem. One of the most effective measures to save energy is to adopt new technologies and new processes to develop high-efficiency heat insulation materials. The use of good thermal insulation materials in the industry is beneficial to reduce product energy consumption, reduce production costs, reduce the volume of the insulation layer, reduce the volume of equipment and facilities, and achieve a beautiful and coordinated effect, which has great social and economic benefits. [0003] At present, traditional thermal insulation materials are difficult to meet the higher requirements for thermal insulation materials such as ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B32B15/04B32B15/20B32B33/00C04B26/02C04B14/38C04B14/42
Inventor 孙小飞李红霞王刚王冬冬孙加林
Owner SINOSTEEL LUOYANG INST OF REFRACTORIES RES
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com