Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

High-strength aluminum grinding ball with glue

A grinding ball, high-strength technology, applied in other chemical processes, chemical instruments and methods, etc., can solve the problems of single use and unsatisfactory performance, and achieve the effect of simple molding process, breaking limitations, and low water absorption

Inactive Publication Date: 2012-06-27
HENAN GOLD SOURCE NEW MATERIAL TECH
View PDF9 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The product obtained by this method has a single use and unsatisfactory performance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-strength aluminum grinding ball with glue

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] Embodiment 1: a kind of high-strength medium aluminum grinding ball with glue

[0023] 1. Composition of raw materials: expressed in weight percentage, 76% of cooked bauxite, 12% of raw bauxite, 5% of clay, 3% of feldspar, 1% of talc, 2% of calcium carbonate, 1% of barium carbonate. The slaked bauxite includes two kinds of slaked bauxite with aluminum content of 72-73% and 77-78%, and their weight ratios are 32% and 44% respectively.

[0024] 2. The preparation method includes the following steps:

[0025] (1) Grinding: Weigh cooked bauxite, raw bauxite, clay, feldspar, talc, calcium carbonate, barium carbonate, crush the bulk raw material to particles below 3mm, add it to the ball mill, press (cooked) Bauxite, raw bauxite, clay, feldspar, talc, calcium carbonate, barium carbonate) raw materials, water in a weight ratio of 5:2, add water, plus sodium tripolyphosphate, 3-5‰ of the total weight of the above-mentioned raw materials -5‰ polyvinyl alcohol solution, ground ...

Embodiment 2

[0030] Embodiment 2: It is basically the same as Embodiment 1, and the difference is:

[0031] The raw materials of the aluminum grinding ball: 70% cooked bauxite, 15% raw bauxite, 5% clay, 3% feldspar, 1% talc, 4% calcium carbonate, 2% barium carbonate, plus the total weight of raw materials 4% ‰ sodium tripolyphosphate, 4‰ polyvinyl alcohol solution. The slaked bauxite includes two kinds of slaked bauxite with aluminum content of 72-73% and 77-78%, whose weight ratios are 32% and 38% respectively.

Embodiment 3

[0032] Embodiment 3: It is basically the same as Embodiment 1, and the difference is:

[0033] Raw materials of aluminum grinding ball: 80% cooked bauxite, 10% raw bauxite, 4% clay, 2% feldspar, 2% talc, 1% calcium carbonate, 1% barium carbonate, plus the total weight of raw materials 5% ‰ of sodium tripolyphosphate, 5‰ of polyvinyl alcohol solution. The slaked bauxite includes two kinds of slaked bauxite with aluminum content of 72-73% and 77-78%, whose weight ratios are 35% and 45% respectively.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
compressive strengthaaaaaaaaaa
degree of polymerizationaaaaaaaaaa
Login to View More

Abstract

The invention relates to a grinding material, in particular to a high-strength aluminum grinding ball with glue, which has the raw materials of: 70-80 percent of mature bauxite, 10-15 percent of immature bauxite, 4-7 percent of clay, 2-5 percent of feldspar, 0.5-2 percent of talcum powder, 1-5 percent of calcium carbonate, 0.5-2 percent of barium carbonate, dispersing agent-sodium tripolyphosphate accounting for 3-5 thousandth of the total weight of the raw materials, and adhesive accounting for 3-5 thousandth of the total weight of the raw materials. A preparation method comprises the following steps of grinding, pelleting, molding, burning and the like, wherein the grinding time is 20-30h, slurry is subjected to spray drying granulation through a high tower when in pelleting, the molding pressure is 320 MPa, the burning temperature is 1255 DEG C, heat preservation is carried out for 1h, and the slurry is air cooled to be room temperature and is output from a kiln. The product provided by the invention has high strength, wear resistant, high temperature and pressure resistance, acid and alkali erosion resistance, low water absorption and stable chemical properties. The content of AL2O3 in the product is more than 68 percent, the volume density is 3.0-3.03g / cm<3>, the wear loss is less than or equal to 0.25 thousandth, the compression strength is larger than 1850 MPa, and various performances are superior to those of similar products.

Description

technical field [0001] The invention relates to a grinding material, in particular to a glue-added high-strength medium-aluminum grinding ball. Background technique [0002] Grinding media are widely used in the grinding and processing of raw materials in various industries such as minerals, ceramics, paints, and cosmetics. They are a necessity in many industries and have a wide market. At present, the performance of grinding medium balls used by domestic wall and floor tile enterprises is not satisfactory, and there are disadvantages such as poor wear resistance, fragility, and more impurities. It is necessary to improve the production process, improve product performance, and reduce equipment maintenance rates. [0003] After retrieval, the application document with the application number 201010532719.1 discloses a preparation method of grinding balls for ball mills. During the preparation, tungsten and molybdenum powders are used as the main raw materials, together with b...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09K3/14C04B35/10C04B35/622
Inventor 康荣恩
Owner HENAN GOLD SOURCE NEW MATERIAL TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com