Nanometer bi-layer film biogas digester material and preparation method thereof

A biogas tank and double-layer membrane technology, which is applied in the field of biogas tank materials, can solve problems such as affecting the tensile strength, elongation at break, weather resistance and other properties of PVC polyvinyl chloride resin, affecting the service life of biogas tank materials, etc. Physical and mechanical properties and anti-aging properties, good physical and mechanical properties, the effect of easy operation

Active Publication Date: 2014-04-23
FUJIAN SIJIA ENVIRONMENTAL PROTECTION MATERIAL TECH
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The addition of various stabilizers, antioxidants and other fillers affects the tensile strength, elongation at break, weather resistance and other properties of PVC polyvinyl chloride resin products, thus affecting the service life of biogas tank materials
At the same time, the current biogas digester material is generally a single-layer structure, and the outer surface is in contact with the atmosphere. It is required that the biogas digester material has good physical and mechanical properties and anti-aging properties; Long-term contact with gas requires that the biogas digester material has good air tightness and corrosion resistance, which puts forward high requirements for the biogas digester material, and the current single-layer biogas digester material is difficult to meet the above requirements

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0033] The preparation method of the nano double-layer biogas tank material of the present invention, the components and parts by weight of the biogas tank material are:

[0034] 100 parts of PVC polyvinyl chloride resin;

[0035] 15-25 parts of DOP dioctyl phthalate;

[0036] 20 parts of DBP dibutyl phthalate;

[0037] 3-4 parts of stabilizer;

[0038] Antioxidant 0.1-0.2 parts;

[0039] Anti-UV agent 0.4-0.6 parts;

[0040] 10-20 parts of nanometer calcium carbonate;

[0041] Modified red mud 20-30 parts;

[0042] 1-2 copies of other additives.

[0043] The preparation method of the described nano-bilayer biogas digester material comprises the following steps:

[0044] Step 1, calendering process: first PVC polyvinyl chloride resin, DOP dioctyl phthalate, DBP dibutyl phthalate, stabilizer, antioxidant, anti-UV agent, nano calcium carbonate, modified red Mud and other additives are added to the calender molding machine and calendered to obtain a laminated film;

[00...

Embodiment 1

[0049] The composition and weight of single-layer biogas digester materials are:

[0050] PVC polyvinyl chloride resin 100 kg;

[0051] DOP dioctyl phthalate 15 kg;

[0052] DBP dibutyl phthalate 20 kg;

[0053] Barium, zinc composite stabilizer 3 kg;

[0054] Antioxidant tetrakis(β-(3,5-di-tert-butyl-4-hydroxyphenyl) propionate) pentaerythritol ester 0.1 kg;

[0055] Anti-UV agent 2-hydroxy-4-n-octyloxybenzophenone 0.4 kg;

[0056] Nano calcium carbonate 10 kg;

[0057] Modified red mud 20 kg;

[0058]Pigment 1 kg.

[0059] The preparation method of the described nano-bilayer biogas digester material comprises the following steps:

[0060] Step 1, calendering process: first PVC polyvinyl chloride resin, DOP dioctyl phthalate, DBP dibutyl phthalate, stabilizer, antioxidant, anti-UV agent, nano calcium carbonate, modified red The mud and other additives were added to the calender molding machine and calendered to obtain a laminated film; the calendering temperature was ...

Embodiment 2

[0065] The composition and weight of single-layer biogas digester materials are:

[0066] PVC polyvinyl chloride resin 100 kg;

[0067] DOP dioctyl phthalate 25 kg;

[0068] DBP dibutyl phthalate 20 kg;

[0069] Barium, zinc composite stabilizer 4 kg;

[0070] Antioxidant 2,6-tertiary butyl-4-methylphenol 0.2 kg;

[0071] Anti-UV agent resorcinol monobenzoate 0.6 kg;

[0072] Nano calcium carbonate 20 kg;

[0073] Modified red mud 30 kg;

[0074] Pigment 2 kg.

[0075] The preparation method of the described nano-bilayer biogas digester material comprises the following steps:

[0076] Step 1, calendering process: first PVC polyvinyl chloride resin, DOP dioctyl phthalate, DBP dibutyl phthalate, stabilizer, antioxidant, anti-UV agent, nano calcium carbonate, modified red The mud and other additives are added to the calendering machine and calendered to obtain a laminated film; the calendering temperature is 180°C, and the pulling speed is 35m / min.

[0077] Step 2. Bondi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a nanometer bi-layer film biogas digester material, which is composed of the following components: PVC (polyvinyl chloride) resin, DOP (Dioctyl-Phthalate), DBP (dibutyl phthalate), a stabilizing agent, an antioxidant, an anti-UV (ultraviolet) agent, nano calcium carbonate, modified red mud and other accessory ingredients, wherein the components are subjected to the calendering technology, the fitting technology and the surface treatment technology, and two groups of single-surface surface-treated single-layer biogas digester materials are combined to obtain the bi-layer biogas digester material. The nanometer bi-layer film biogas digester material has the advantages that nano calcium carbonate and the modified red mud are adopted to serve as filling agents, thus the weather resistance, the aging resistance and the like of a PVC film are improved and the service life of the bi-layer film biogas digester material is prolonged; the acrylate coating is used for surface treatment, thus the weather resistance and the aging resistance of the bi-layer film biogas digester material are improved; and because of adopting the bi-layer film structure, the inner-layer film has excellent air impermeability and chemical corrosion resistance, and the outer-layer film has good physical and mechanical property and aging resistance so as to prevent the inner-layer film from being damaged by the external environment.

Description

technical field [0001] The invention relates to a biogas pit material, in particular to a nanometer double-layer biogas pit material and a preparation method thereof. Background technique [0002] The current biogas digester materials are generally made of PVC polyvinyl chloride resin as the main raw material, plus various stabilizers, antioxidants and other fillers. The addition of fillers such as various stabilizers and antioxidants affects the tensile strength, elongation at break, weather resistance and other properties of PVC polyvinyl chloride resin products, thereby affecting the service life of biogas tank materials. At the same time, the current biogas digester material is generally a single-layer structure, and the outer surface is in contact with the atmosphere. It is required that the biogas digester material has good physical and mechanical properties and anti-aging properties; Long-term exposure to gas requires good airtightness and corrosion resistance of the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L27/06C08K13/06C08K9/00C08K5/12C08K3/26C08K3/22C08J5/18C08J5/12
Inventor 林生雄张宏旺黄万能蒋石生
Owner FUJIAN SIJIA ENVIRONMENTAL PROTECTION MATERIAL TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com