Preparation method of solvent-based two-component wind turbine blade protective primer

A wind turbine blade, two-component technology, applied in the direction of polyurea/polyurethane coatings, coatings, etc., can solve the problems of limited use range, inability to carry out thick film coating, slow drying speed, etc., to achieve excellent adhesion and good protection. effect, fast drying effect

Active Publication Date: 2012-07-18
AVIC BIAM NEW MATERIALS TECH ENG
View PDF3 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The above-mentioned protective primers for wind turbine blades have very good application effects, but they have a common disadvantage, that is, the drying speed is relatively slow; thick film coating cannot be carried out; the scope of use is limited, and they can only be matched with special matching topcoats. use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of solvent-based two-component wind turbine blade protective primer

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0032] Preparation of component A: Add 0.1% to 0.5% of defoamer, 0.1% to 0.5% of defoamer, 0.1% to 0.5% of Adhesion promoter, 0.1% to 0.5% coupling agent, 0.5% to 3% wetting and dispersing agent, 0.5% to 2% thixotropic agent and 3% to 40% solvent; after stirring for 5 to 10 minutes, Add 15% to 30% of titanium dioxide and stir at high speed for 40 to 50 minutes, then add 4% to 7% of matting agent and stir evenly;

[0033] Wherein, the content of modified hydroxy acrylic resin is preferably 30% to 40%;

[0034] The content of the defoamer is preferably 0.2% to 0.4%;

[0035] The content of defoaming agent is preferably 0.2% to 0.4%;

[0036] The content of the adhesion promoter is preferably 0.3% to 0.5%;

[0037] The content of the coupling agent is preferably 0.3% to 0.5%

[0038] The content of matting agent is preferably 4% to 7%;

[0039] The content of the wetting and dispersing agent is preferably 0.5% to 2%, more preferably 1% to 2%;

[0040] The preferred content ...

Embodiment 1

[0056] The first step: preparing component A and component B;

[0057]Preparation of component A: 1 gram of polyamine block copolymer solution-based wetting and dispersing agent, 0.4 gram of carboxyl-containing adhesion promoter, 0.3 gram of silane coupling agent, 0.2 gram of acrylate polymer Foaming agent, 0.3 gram of acrylic acid copolymer defoamer, 1 gram of composite thixotropic agent (wherein, 0.4 gram of meteorological silica, 0.6 gram of modified urea thixotropic agent) are added to 30 grams of modified hydroxyacrylic resin, Then add 30 grams of solvent (including 15 grams of butyl acetate and 15 grams of propylene glycol methyl ether acetate) and stir for 5 to 10 minutes, then add 30 grams of titanium dioxide and stir at high speed for 40 to 50 minutes, and finally add 6.8 grams of meteorological silica matting powder and stir 15min.

[0058] Preparation of component B: Dissolve 65 grams of HDI trimer in 35 grams of butyl acetate and stir well to mix evenly.

[0059]...

Embodiment 2

[0061] The first step: preparing component A and component B;

[0062] Preparation of component A: 1 gram of polyamine block copolymer solution-based wetting and dispersing agent, 0.4 gram of carboxyl-containing adhesion promoter, 0.4 gram of silane coupling agent, 0.3 gram of acrylate polymer Foaming agent, 0.2 gram of acrylic acid copolymer defoamer, 0.8 gram of composite thixotropic agent (wherein meteorological silica 0.4 gram, modified urea thixotropic agent 0.4 gram) joins the inside of 46 gram of modified hydroxyacrylic resins, and then Add 19 grams of solvent (including 14 grams of butyl acetate and 5 grams of propylene glycol methyl ether acetate) and stir for 5 to 10 minutes, then add 26 grams of titanium dioxide and stir at high speed for 40 to 50 minutes, and finally add 5.9 grams of meteorological silica matting powder and stir for 15 minutes That's it.

[0063] Preparation of component B: Dissolve 74 grams of HDI trimer in 26 grams of butyl acetate and stir well...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a preparation method of solvent-based two-component wind turbine blade protective primer. The preparation method comprises the steps of preparing a component A and a component B; and mixing the components A and B at a ratio of (8-10):(1-2), and uniformly stirring to obtain the solvent-based two-component wind turbine blade protective primer. The protective primer prepared by the method provided by the invention has the advantages of excellent adhesion, rapid drying speed and good compatibility, is suitable for thick film coating, and improves work efficiency.

Description

technical field [0001] The invention belongs to the technical field of preparation of organic polymer compounds, and in particular relates to a preparation method of a solvent-based two-component wind power blade protective primer. Background technique [0002] With the rapid and sustainable development of my country's economy, the demand for energy is also growing rapidly. Wind energy, as a green renewable energy, has received more and more attention in my country. Especially in recent years, the wind power industry in my country is developing rapidly. The speed of development is developing, and already has a certain foundation. Wind power blades are one of the important components of wind turbines, and they will be exposed to harsh environments such as strong ultraviolet rays, sandstorms, high temperatures, and cold currents for a long time. The blades will face strong erosion and erosion of sand, dust, rain, and other substances during normal operation. [0003] At presen...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/04C09D7/12
Inventor 商汉章师华杨振波于一川陈立江吕化工房志安刘伟曾灵华张伟江
Owner AVIC BIAM NEW MATERIALS TECH ENG
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com