Hot-pressed veneer adhesive and preparation method thereof

An adhesive and veneer technology, applied in the direction of monocarboxylic acid ester copolymer adhesive, rosin adhesive, starch adhesive, etc., can solve the problems of harming the health of users, releasing formaldehyde, and inconvenient to use. , to achieve the effect of reducing equipment energy consumption, reducing adhesion and improving adhesive strength

Active Publication Date: 2012-07-18
顶立新材料科技股份有限公司
View PDF6 Cites 36 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This type of adhesive is inconvenient to use, the hot-pressing temperature is too high, the energy consumption is large, the hot-pressing time is long, and there is formaldehyde release during processing and later use, which pollutes the environment and seriously endangers the health of users. Therefore, the development A heat-pressed veneer veneer adhesive with one component, easy to use, low processing energy consumption, and no formaldehyde release has important economic and social benefits

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] Formula: Total amount=1000kg

[0035] Deionized water 252.8kg

[0036] PVA-1788 35kg

[0037] PVA-2099 10kg

[0038] Methacrylic acid 6.5kg

[0039] Concentration 20% N-methylolacrylamide aqueous solution 90kg

[0040] Vinyl acetate 230kg

[0041] Dibutyl phthalate 20.5kg

[0042] Tapioca starch 250kg

[0043] Concentration of 10% ammonium persulfate aqueous solution 13kg

[0044] Sodium bicarbonate 3.2kg

[0045] OP-10 3.5kg

[0046] Sodium lauryl sulfate 0.5kg

[0047] Concentration of 10% borax aqueous solution 15kg

[0048] Sodium polyacrylate 3.0kg

[0049] Defoamer F681 1.0kg

[0050] Water-based rosin 60kg

[0051] Sodium Benzoate 6.0kg

[0052] Production Process:

[0053] 1. After the equipment check is normal, put in 252.8kg of deionized water, start the reactor with condenser, add 45kg of polyvinyl alcohol, raise the temperature to 85℃~90℃ and keep it warm for about 90 minutes to fully dissolve the polyvinyl alcohol;

[0054]2. Cool down to ...

Embodiment 2

[0063] Formula: Total amount=1000kg

[0064] Deionized water 238.4 kg

[0065] PVA-2488 25.5kg

[0066] PVA-1799 20kg

[0067] Methacrylic acid 9.0kg

[0068] Concentration 32% N-methylolacrylamide aqueous solution 56kg

[0069] Vinyl acetate 200kg

[0070] Dioctyl phthalate 19kg

[0071] Tapioca starch 280kg

[0072] Concentration 20% potassium persulfate aqueous solution 8.5kg

[0073] Sodium bicarbonate 3.5kg

[0074] Sodium Lauryl Sulfate 3.2kg

[0075] Concentration 8% borax aqueous solution 75kg

[0076] Sodium polyacrylate 3.5kg

[0077] Defoamer F681 1.4kg

[0078] Water-based rosin 50kg

[0079] Sodium Benzoate 7.0kg

[0080] Production Process:

[0081] 1. After the equipment check is normal, put in 238.4kg of deionized water, start the reactor with condenser, add polyvinyl alcohol 2488 25.5kg, 1799 20kg, heat up to 85℃~90℃ and keep it warm for about 90 minutes to dissolve the polyethylene Alcohol is fully dissolved;

[0082] 2. Cool down to 55°C, a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a hot-pressed veneer adhesive and a preparation method thereof. The hot-pressed veneer adhesive mainly comprises the following components: deionized water, polyvinyl alcohol, an emulsifier, an initiator, methacrylic acid, N-methylol acrylamide, vinyl acetate, a plasticizer, a buffering agent, cassava starch, borax, a dispersing agent, aqueous rosin, a defoaming agent and a corrosion inhibitor. When the hot-pressed veneer adhesive is prepared, the preparation method comprises the following steps of: firstly synthesizing a self-crosslinked polyvinyl acetate copolymerization modified emulsion, then adding 20-35% of raw cassava starch, a crosslinking agent, waterborne tackifying resin and other auxiliaries for mixing and finally preparing the hot-pressed veneer adhesive with excellent performances. Compared with a traditional urea resin veneer adhesive, the adhesive prepared by the invention has the advantages of convenience in use, low curing temperature, short curing time and no harm to an environment and a human body.

Description

technical field [0001] The invention relates to an adhesive, in particular to a hot-pressed veneer veneer adhesive and a preparation method thereof. Background technique [0002] With the continuous improvement of people's material and cultural living standards, the requirements for furniture are getting higher and higher. In the past, furniture made of MDF, blockboard and ordinary wood can no longer meet people's requirements in terms of aesthetics and practicability. For this reason, a veneer veneer technology has appeared on the market. This technology is to laminate beech, rosewood, red sandalwood, walnut, teak, aqua, etc. on the surface of MDF, blockboard and ordinary wood. The veneer of precious natural tree species such as willow and cherry wood, the veneer maintains the natural texture and color of the precious tree species, and through the lamination of natural veneer with MDF, blockboard and ordinary wood, the added value of the product is increased, while reducing...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J131/04C09J103/02C09J129/04C09J193/04C09J11/06C09J11/04
Inventor 周闰阳章勇生徐健伏浪李小清
Owner 顶立新材料科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products