Preparation method of monodispersity micron-sized polysilicon microspheres

A polyorganosilicon and monodispersity technology, which is applied in the field of monodisperse micron-scale polyorganosilicon microspheres and its preparation, can solve the problem that the particle size of the organosilicon microspheres is difficult to be monodispersed and the coverage rate of organic functional groups is low. , the post-processing is cumbersome and other problems, to achieve the effect of good particle size uniformity, fewer types of raw materials, and easy control of the reaction

Active Publication Date: 2012-07-25
SOUTH CHINA UNIV OF TECH
View PDF5 Cites 30 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

These two methods are cumbersome, not only can not make the organic functional groups evenly covered on the silicon, but also the coverage is very low
Some of the above-mentioned preparation methods need to use emulsifiers, some need to use alcohol, the raw m

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of monodispersity micron-sized polysilicon microspheres
  • Preparation method of monodispersity micron-sized polysilicon microspheres
  • Preparation method of monodispersity micron-sized polysilicon microspheres

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0027] Example 1

[0028] (1) In a reactor equipped with a stirrer, a thermometer, a reflux condenser, and a nitrogen flow device, add 80ml of deionized water and 15ml of vinyltrimethoxysilane, and then add 0.008ml of a mass percentage concentration of 28% The reaction temperature is 30℃, the stirring speed is 300rpm, and the reaction time is 6h.

[0029] (2) Centrifuge the mixed system of step (1) on a centrifugal settling machine to filter out unreacted monomers at a speed of 5000 rpm and a time of 20 minutes.

[0030] (3) To the reaction system obtained in step (2), add 0.5 ml of an ammonia solution with a 28% mass percentage concentration, the reaction temperature is 30° C., the stirring speed is 500 pm, and the time is 1 h. The obtained product was filtered, washed with water and ethanol, and dried at 100°C for 15 hours to obtain 7.6 g of monodisperse micron-sized silicone microspheres with an average particle size of 1.6 μm, such as figure 1 Shown.

Example Embodiment

[0031] Example 2

[0032] The difference between this embodiment and Embodiment 1 is:

[0033] Step (1) Drop 0.03ml of 28% aqueous ammonia solution with a mass percentage concentration of 8 hours, and step (3) add 0.7ml of 28% aqueous ammonia solution with a mass percentage concentration of 4 hours to obtain monodisperse Micron-sized silicone microspheres are 7.4g, with an average particle size of 1.4μm.

Example Embodiment

[0034] Example 3

[0035] The difference between this embodiment and Embodiment 1 is:

[0036] Step (1) add 5ml of vinyltrimethoxysilane, the reaction temperature is 40℃, the speed of the mixed system in step (2) is 4000rpm, time 15min, step (3) add 0.3ml mass percentage A 28% ammonia aqueous solution and a reaction time of 3 hours obtain 2.5 g of monodisperse micron-sized organic silicon microspheres with an average particle size of 2 μm.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
The average particle sizeaaaaaaaaaa
The average particle sizeaaaaaaaaaa
The average particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method of monodispersity micron-sized polysilicon microspheres which comprises the following steps: (1) adding deionized water and a basic catalyst in trialkoxysilane, and stirring in a nitrogen condition for hydrolysis; (2) centrifugally separating and filtering a mixed system in step (1) to remove unreacted monomers; and (3) adding the basic catalyst in a reaction system obtained from the step (2) for polycondensation, filtering, washing and drying to obtain the monodispersity micron-sized polysilicon microspheres. According to the method, the reaction temperature is low, the reaction can be conducted at room temperature, the synthesis steps are simple; the method does not use organic solvents which pollute the environment or emulsifiers in the reaction process, is simple in post treatment, less in types of raw materials, high in yield, and low in preparation cost, and can effectively adjust the grain size range of the microspheres to realize controllable sizes; and the obtained silicon microspheres are good in grain size uniformity and high in monodispersity, and has extremely good sphericity.

Description

technical field [0001] The invention relates to a monodisperse micron-order organosilicon microsphere, in particular to a size-controllable monodisperse micron-order polyorganosilicon microsphere and a preparation method thereof. Background technique [0002] Polyorganosiloxane microspheres have excellent physical and chemical properties such as high and low temperature resistance, weather resistance, flame retardancy, abrasion resistance, hydrophobicity, electrical insulation, and physiological inertia. , coatings, cosmetics, light diffusion light guide plates and other fields, thereby improving heat resistance, flame retardancy, oxidation resistance, scratch resistance, light diffusion, etc. [0003] In the preparation of monodisperse micron-sized silicone microspheres, some people have done research. Mary et al. (US5801262) obtained the first batch of emulsions by mixing anionic surfactants, stabilizers, alkaline hydroxide aqueous solution, water, etc. together by emulsi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08G77/06C08G77/20C08G77/28
Inventor 马文石张冬桥段宇
Owner SOUTH CHINA UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap