Novel foam high-polymer composite and production method thereof

A foamed polymer and composite material technology, applied in the field of building materials, can solve the problems of consumption of large minerals and forest resources, unstable physical and chemical properties, limited bearing capacity, etc., achieving low temperature sensitivity, stable chemical properties, The effect of stable flow ratio

Inactive Publication Date: 2012-08-22
刘海福 +1
View PDF2 Cites 35 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This type of material has limited environmental tolerance, is prone to cracking, warping and deformation, corrosion, and unstable physical and chemical properties.
On the other hand, whether it is wood-plastic, calcium-plastic materials or logs will consume a lot of minerals and forest resources

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A novel foamed polymer composite material comprises the following components in parts by weight:

[0029] Thermoplastic PVC 80

[0030] Fly Ash 20

[0031] Aluminate coupling 0.4

[0032] Organotin Stabilizer 1

[0033] HL100 2.8

[0034] HL175 0.8

[0035] Acmj9 0.8

[0036] Polyethylene wax 0.5

[0037] AC blowing agent 1.6

[0038] Calcium stearate 0.5

[0039] Sodium bicarbonate 0.2

[0040] Paraffin 0.5

[0041] Epoxidized soybean oil 1

[0042] Antioxidant 168 0.15

[0043] Antioxidant 1010 0.08

[0044] Anti-ultraviolet agent UV-531 0.15

[0045] Decabromane 2

[0046] Antimony silicon trioxide 1

[0047] Just the right amount of pigment.

[0048] A preparation method of a novel foamed polymer composite material, the specific steps are:

[0049] (1) Prepare raw materials according to the above-mentioned proportioning by weight;

[0050] (2) Sieve the inorganic powder to obtain an inorganic powder with a fineness of 200-2500 mesh;

[0051] (3) P...

Embodiment 2

[0056] A novel foamed polymer composite material comprises the following components in parts by weight:

[0057] Thermoplastic PVC 60

[0058] Fly Ash 40

[0059] Aluminate coupling 0.3

[0060] Organotin stabilizer 1.2

[0061] HL100 3.1

[0062] HL175 0.9

[0063] Acmj9 0.9

[0064] Polyethylene wax 0.5

[0065] AC blowing agent 1.8

[0066] Calcium stearate 0.5

[0067] Sodium bicarbonate 0.2

[0068] Paraffin 0.5

[0069] Epoxidized soybean oil 1.3

[0070] Antioxidant 168 0.15

[0071] Antioxidant 1010 0.08

[0072] Anti-ultraviolet agent UV-531 0.15

[0073] Decabromane 2

[0074] Antimony silicon trioxide 1

[0075] Just the right amount of pigment.

[0076] The preparation method of the environment-friendly porcelain-plastic polymer composite material is the same as that in Example 1.

Embodiment 3

[0078] A novel foamed polymer composite material comprises the following components in parts by weight:

[0079] Thermoplastic PVC 40

[0080] Brick Gray 60

[0081] Aluminate coupling 0.6

[0082] Organotin stabilizer 1.5

[0083] HL100 4

[0084] HL175 1.5

[0085] Acmj9 1.5

[0086] Polyethylene wax 0.7

[0087] AC blowing agent 2

[0088] Calcium stearate 0.5

[0089] Sodium bicarbonate 0.4

[0090] Paraffin 0.5

[0091] DOP 1.5

[0092] Antioxidant 168 0.15

[0093] Antioxidant 1010 0.08

[0094] Anti-ultraviolet agent UV-531 0.15

[0095] Decabromane 2

[0096] Antimony silicon trioxide 1

[0097] Just the right amount of pigment.

[0098] The preparation method of the environment-friendly porcelain-plastic polymer composite material is the same as that in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the field of construction materials and particularly relates to novel foam high-polymer composite and a production method. The novel foam high-polymer composite comprises 10-90 parts of thermoplastic plastics, 0.5-3 parts of plasticizer, 0.5-3 parts of flexibilizer, 0.5-3 parts of tackifier, 0.3-2 parts of internal and external lubricant, 0.5-3 parts of stabilizer, 0.5-5 parts of crosslinking modifier, 0.5-12 parts of regulator, 0.5-5 parts of foaming agent, 0.5-3 parts of filler, 0-20 parts of flame retardant, 10-90 parts of inorganic powder and pigment in proper quantity. The novel foam high-polymer composite in the technical scheme is energy-saving, emission-reducing, acid-resistant and alkali-resistant, weak in temperature sensitivity and excellent in physical and chemical performance.

Description

technical field [0001] The invention belongs to the field of building materials, in particular to a novel foamed polymer composite material and a manufacturing method. Background technique [0002] With the emphasis on resource recycling and environmental protection at home and abroad, the harmless treatment and high value-added utilization of solid waste have been put on important research topics. However, the "fly ash" produced by thermal power plants around the world, and waste materials from various brick and tile factories and construction sites are piled up randomly, which not only causes serious damage to the environment, but also wastes human resources. At present, most of the profiles and panels used in municipal administration, garden construction, building materials, home furnishing, environmental decoration and related industries are wood-plastic, calcium-plastic composite materials and logs. This type of material has limited environmental tolerance, is prone to...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08K13/06C08K9/04C08K9/06C08J9/10C08J9/08B29B7/00
Inventor 刘海福宋鹤淼
Owner 刘海福
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More