Expanded type aqueous facing fireproof coating and preparation method thereof

An intumescent technology for fire-resistant coatings, applied in fire-resistant coatings, coatings, etc., can solve problems such as insufficient adhesion and poor water resistance of coatings, and achieve the effects of smooth and delicate coating films, improved fire resistance, and excellent salt spray resistance

Active Publication Date: 2012-09-19
CARPOLY CHEM GRP
View PDF3 Cites 48 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

my country's water-based decorative fire retardant coatings are developing rapidly, but some existing intumescent water-based decorative fire retardant coatings still have deficiencies, such as poor water resistance and insufficient adhesion

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Expanded type aqueous facing fireproof coating and preparation method thereof
  • Expanded type aqueous facing fireproof coating and preparation method thereof
  • Expanded type aqueous facing fireproof coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0048] The preparation method of intumescent water-based decorative fireproof coating provided by the invention may further comprise the steps:

[0049] a) Mix the following components by weight percentage: 10% to 30% of styrene-acrylic emulsion, 20% to 30% of ammonium polyphosphate, 10% to 20% of pentaerythritol, 15% to 25% of melamine, 5% to 10% titanium dioxide, 2% to 8% aluminum hydroxide, 1% to 5% zinc borate, 1% to 2% chlorinated paraffin, 0.05% to 0.2% antiseptic, 0.1% to 0.2% dispersant, 0.3% to 1.0% of film-forming aids, 0.1% to 0.5% of cellulose ether, 0.5% to 2.0% of hydroxyl silicone oil and the rest of water, wherein the cellulose ether is added after wetting with water to obtain The mixture is dispersed and stirred at a lower speed of 100rpm to 150rpm.

[0050] The weight percent components mixed can be preferably 15%-25% of styrene-acrylic emulsion, 15%-25% of ammonium polyphosphate, 15%-20% of pentaerythritol, 20%-25% of melamine, 5%-10% of titanium dioxide, h...

Embodiment 1

[0054] 20 parts of MW-161 styrene-acrylic emulsion from Shanghai Mowang Composite Material Technology Co., Ltd., 24 parts of ammonium polyphosphate, 12 parts of pentaerythritol, 15 parts of melamine, and 6 parts of R105 rutile titanium dioxide from DuPont Titanium Dioxide Technology (Shanghai) Co., Ltd. , 4 parts of aluminum hydroxide, 4 parts of zinc borate, 2 parts of 70 chlorinated paraffin, 0.1 part of isothiazolinone, XG-505 water-resistant dispersant produced by Hengshui Xinguang Chemical Co., Ltd. (hydrophobic modified polyacrylic acid ammonium salt ) 0.2 parts, 0.7 parts of dodecyl alcohol, 0.1 parts of hydroxyethyl cellulose, 1 part of hydroxy silicone oil from Qingdao Xingye Silicone New Material Co., Ltd., 1 part of antifreeze, 9.9 parts of water, dispersed at 1500-2000rpm for 10- 15 minutes, and grind in a basket sand mill for 20 minutes to make the fineness reach ≤80 μm, filter and discharge.

Embodiment 2

[0056] 25 parts of SD-800 styrene-acrylic emulsion from Nantong Shengda Chemical Co., Ltd., 20 parts of ammonium polyphosphate, 10 parts of pentaerythritol, 18 parts of melamine, 7 parts of R218 rutile titanium dioxide from Shanghai Yuejiang Titanium White Chemical Products Co., Ltd., hydrogen 2 parts of alumina, 2 parts of zinc borate, 2 parts of 70 chlorinated paraffin, 0.2 part of bromothalonil, 0.1 part of Dipas GA40 dispersant (acrylic acid copolymer ammonium salt) of Changzhou Yayuan Chemical Co., Ltd., lauryl alcohol 1 part of ester, 0.5 part of carboxymethyl cellulose, 1.4 parts of hydroxy silicone oil of Rudong Zhenfeng Yiyang Chemical Co., Ltd., 10.8 parts of water, disperse at 1500-2000rpm for 10-15 minutes, and grind in a basket sand mill Grind for 20 minutes to make the fineness ≤80μm, filter and discharge.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
decomposition temperatureaaaaaaaaaa
decomposition temperatureaaaaaaaaaa
heataaaaaaaaaa
Login to View More

Abstract

The invention provides an expanded type aqueous facing fireproof coating, which comprises the following components by weight: 10% to 30% of styrene-acrylic emulsion, 20% to 30% of ammonium polyphosphate, 10% to 20% of pentaerythritol, 15% to 25% of melamine, 5% to 10% of titanium dioxide, 2% to 8% of aluminum hydroxide, 1% to 5% of zinc borate, 1% to 2% of chlorinated paraffin, 0.05% to 0.2% of antiseptic, 0.1% to 0.2% of dispersing agent, 0.3% to 1.0% of film-forming auxiliary, 0.1% to 0.5% of cellulose ether, 0.5% to 2.0% of hydroxy silicone oil and the balance of water. The expanded type aqueous facing fireproof coating, provided by the invention, has the advantages of excellent water resistance and salt mist resistance, excellent adhesion and flexibility, good storage stability, no layering, no fineness change and no packing phenomenon, excellent waterproof resistance, smooth and fine coating film, no toxicity and pollution, and environment-friendliness.

Description

technical field [0001] The invention relates to the field of coatings, in particular to an intumescent water-based decorative fireproof coating and a preparation method thereof. Background technique [0002] With the continuous development of my country's economic construction, the development and construction of various high-rise buildings, underground projects, office buildings, and entertainment venues, the high-grade and luxurious interior decoration has further expanded the use of building decoration materials, followed by Increased fire hazard. In order to better match fire protection and decoration, people have higher and higher requirements for decorative fireproof coatings, and their applications are becoming more and more extensive. Therefore, decorative decorative fireproof coatings will have a broader application and development prospect. [0003] Fire retardant coatings, also known as flame retardant coatings, are special functional coatings. They are painted on...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D125/14C09D5/18
Inventor 陈均炽陈玉泉
Owner CARPOLY CHEM GRP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com