High-hardness wood-plastic building template and preparation method thereof

A building formwork, high hardness technology, applied in the field of high hardness wood-plastic building formwork and its preparation, can solve problems such as poor hardness and affecting use, and achieve the effect of smooth and delicate surface, high hardness and strong wood feeling

Active Publication Date: 2014-05-14
SHANDONG BODO PLASTICS CO LTD
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The wood-plastic panels in the prior art often have poor hardness, which affects its use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-hardness wood-plastic building template and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] The formula of the high-hardness wood-plastic building formwork is as follows: 50 parts by weight of polyvinyl chloride resin powder with a polymerization degree of 1000, 1 part by weight of silane coupling agent, 2 parts by weight of composite lead stabilizer, 5 parts by weight of ACR Processing modifier, the activation of ground calcium carbonate of 2 parts by weight, the polyethylene wax of 1 part by weight, the azodicarbonamide of 0.4 parts by weight, the sodium bicarbonate of 0.6 parts by weight, the chlorinated polyethylene of 1 part by weight, 30 parts by weight of 40 mesh wood flour, 7 parts by weight of nano-calcium carbonate, the total weight part is 100 parts.

[0021] The preparation method of the polyvinyl chloride wood-plastic board: first, add the above-mentioned raw materials in the formula amount into the high-speed mixer, heat through the oil jacket and self-friction to 110°C, put them into the cold mixing, and when the materials are cooled to 50 Put i...

Embodiment 2

[0024] The formula of the high-hardness wood-plastic building formwork is as follows: 30 parts by weight of polyvinyl chloride resin powder with a polymerization degree of 700, 1 part by weight of silane coupling agent, 3 parts by weight of composite lead stabilizer, and 6 parts by weight of ACR Processing modifier, the activated ground calcium carbonate of 4 parts by weight, the polyethylene wax of 2 parts by weight, the azodicarbonamide of 0.4 parts by weight, the sodium bicarbonate of 0.6 parts by weight, the chlorinated polyethylene of 5 parts by weight, 42 parts by weight of 40 mesh wood flour, 6 parts by weight of nanometer calcium carbonate, the total weight part is 100 parts.

[0025] The preparation method of the high-hardness wood-plastic building formwork is as in Example 1.

[0026] The product prepared in this embodiment is a 15mm plate with a density of 500kg / m 3 , Plate hardness (Shore hardness) D=69.

Embodiment 3

[0028] The formula of the polyvinyl chloride wood-plastic board is as follows: 33 parts by weight of polyvinyl chloride resin powder with a polymerization degree of 700, 2 parts by weight of silane coupling agent, 5 parts by weight of composite lead stabilizer, and 8 parts by weight of ACR Processing modifier, the activated ground calcium carbonate of 6 parts by weight, the polyethylene wax of 1 part by weight, the azodicarbonamide of 0.4 parts by weight, the sodium bicarbonate of 0.6 parts by weight, the chlorinated polyethylene of 6 parts by weight, 30 parts by weight of 40 mesh wood flour, 8 parts by weight of modified ultrafine silicon dioxide, the total weight part is 100 parts.

[0029] The preparation method of the high-hardness wood-plastic building formwork is as in Example 1.

[0030] The product prepared in this embodiment is a 15mm plate with a density of 510kg / m 3 , Plate hardness (Shore hardness) D=70.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to a high-hardness wood-plastic building template and a preparation method thereof, which belong to the technical field of polyvinyl chloride plates. The 100 parts by weight of high-hardness wood-plastic building template comprises the following raw materials in parts by weight: 20-50 parts of polyvinyl chloride resin powder, 1-4 parts of a coupling agent, 2-5 parts of a stabilizing agent, 1-15 parts of an acrylic alkyl ester processing modifier; 1-15 parts of a filling agent, 1-4 parts of a lubricant, 1-4 parts of a foaming agent, 1-8 parts of a toughening agent, 30-50 parts of wood flour, and 5-10 parts of a reinforcing agent. According to the invention, the plate stacking density is less than or equal to 700 kg / m<3>, so that the building template is good in flame retardancy and smoke suppression, meanwhile, the building template is high in hardness and strong in wood texture; and just like raw woods, the building template also has the properties that the template can be nailed, drilled, planed and adhered and the like, the surface of the template is smooth and fine, and the template is water-proof, corrosion-resistant, fireproof, mould-proof, moth-preventing, and pollution-free.

Description

technical field [0001] The invention relates to a high-hardness wood-plastic building template and a preparation method thereof, belonging to the technical field of polyvinyl chloride boards. Background technique [0002] Wood-plastic composite material is a new type of composite material that has been booming at home and abroad in recent years. Usually, polyvinyl chloride is used instead of the usual resin adhesive, and it is mixed with more than 30% of waste plant fibers such as wood powder, rice husk, and straw to form a new composite material. Wooden materials are processed by extrusion, molding, injection molding and other plastic processing techniques to produce panels or profiles. Wood-plastic has entered the national "Strategic Emerging Industries List" and is listed as a "new material". The state will help the green economy in terms of finance, taxation, finance, investment, etc., and at the same time increase the proportion of recycled products in government procu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L27/06C08L97/02C08K13/06C08K9/04C08K3/36C08K3/26C08J9/10C08J9/08B29C44/02B29C44/42B29C44/60
Inventor 苗伟周学卫孙锋王长明
Owner SHANDONG BODO PLASTICS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com