Mold release agent for pig-casting machine

A release agent, cast iron machine technology, applied in the direction of casting molds, casting mold components, casting molding equipment, etc., can solve problems such as poor performance, reduce production costs, improve working conditions, and stabilize chemical properties.

Inactive Publication Date: 2014-07-16
高金菊
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of the present invention is to overcome the poor performance of the release agent for cast iron machines in the prior art, and provide a release agent for cast iron machines, which is coated on the inner surface of the cast iron mold by using the release agent of the present invention , an effective isolation is formed between the molten iron and the cast iron mold, and the cast iron ingot can fall off the cast iron mold smoothly

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] A kind of demoulding agent for cast iron machine of the present embodiment, its component and content are as follows: blast furnace gas mud 20kg, sintering machine head electrostatic precipitator ash 10kg, mine trough dust removal ash 16kg in front of the furnace, soybean oil 17kg, limestone 5kg, aluminum oxide 10kg, dolomite 11kg, bentonite 17kg, iron red epoxy ester primer 7kg, zirconia 4kg, water 1000kg. It is worth noting that the gas dust removal system of the ironmaking blast furnace is composed of gravity dust removal and fine dust removal. The dry coarse dust collected by the first stage is called gravity ash; the second fine dust collector generally adopts dry type Bag filter or wet dust removal system, in which the dry fine dust obtained by dry dust removal is called gas ash; the sludge obtained by wet dust removal after precipitation treatment is called gas mud. The blast furnace used in the present invention Gas mud is the sludge obtained after the product o...

Embodiment 2

[0048] A kind of demoulding agent for cast iron machine of the present embodiment, its component and content are as follows: blast furnace gas mud 23kg, sintering machine head electrostatic precipitator ash 11kg, mine trough dust removal ash 19kg in front of the furnace, soybean oil 16kg, limestone 6kg, aluminum oxide 9kg, dolomite 13kg, bentonite 18kg, iron red epoxy ester primer 8kg, zirconia 5kg, water 900kg.

[0049] The preparation method of the release agent of the present embodiment, its steps are as follows:

[0050] (1) Weigh 16kg of soybean oil and 18kg of bentonite, mix and stir the above soybean oil and bentonite in a mixer for 28 minutes at a stirring speed of 150 r / min, and mix well to obtain mixture A;

[0051] (2) Weigh 23kg of blast furnace gas mud according to the mass ratio, 11kg of dust removal dust from the sintering machine head, and 19kg of dust removal dust from the mine trough in front of the furnace. The particle size can be 38-74 microns, and the ab...

Embodiment 3

[0056] A kind of demoulding agent for cast iron machine of the present embodiment, its component and content are as follows: blast furnace gas mud 25kg, sintering machine head electrostatic precipitator ash 13kg, mine trough dust removal ash 23kg in front of the furnace, soybean oil 15kg, limestone 7kg, aluminum oxide 9.5kg, dolomite 15kg, bentonite 19kg, iron red epoxy ester primer 7.5kg, zirconia 3kg, water 800kg.

[0057] The preparation method of the release agent of the present embodiment, its steps are as follows:

[0058] (1) Weigh 15kg of soybean oil and 19kg of bentonite, mix and stir the above soybean oil and bentonite in a mixer for 30 minutes at a stirring speed of 100 r / min, and mix well to obtain mixture A;

[0059] (2) Weigh 25kg of blast furnace gas mud according to the mass ratio, 13kg of dust removal dust from the sintering machine head, and 23kg of dust removal dust from the mine trough in front of the furnace. The particle size can be 38-74 microns, and th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a release agent for cast iron machines, which belongs to the technical field of release agents for metallurgical casting. Each component of the present invention is composed of the following parts by mass: 20-25 parts of blast furnace gas mud, 10-13 parts of electrostatic precipitator ash for sintering head, 16-23 parts of dedusting ash for mine trough in front of furnace, 15-17 parts of soybean oil, limestone 5~7 parts, 9~10 parts of alumina, 11~15 parts of dolomite, 17~19 parts of bentonite, 7~8 parts of iron red epoxy ester primer, 3~5 parts of zirconia, 800~1000 parts of water. In the present invention, wastes that are difficult to comprehensively utilize, such as blast furnace gas mud, sintering machine head electric dust, and furnace front mine trough dust, are used as some components of the release agent, so that these dusts can be recycled and utilized, which greatly improves The production cost of the steel plant is reduced, and the release agent can effectively adhere to the inner surface of the casting mold, forming an effective isolation layer between the molten iron and the cast iron mold, and the cast iron machine can be demolded without additional knocking, The cast iron ingot has a smooth surface.

Description

technical field [0001] The invention relates to the technical field of mold release agents for metallurgical casting, and more specifically, to a mold release agent for cast iron machines. Background technique [0002] The iron casting machine is a device for continuously casting molten iron into iron blocks. It is a circular chain belt with many iron molds and chain plates tilted upwards. It revolves around the star-shaped large gears at the upper and lower ends. The gear is a transmission wheel driven by a motor, and the star-shaped large gear at the lower end is a guide wheel, and its bearing position can be moved to adjust the tightness of the chain belt. According to the fixed situation of the roller, the cast iron machine is divided into a fixed roller cast iron machine and a movable roller cast iron machine. The process of cast iron machine is that the locomotive transports the molten iron tank car or mixed iron car loaded with molten iron from the blast furnace to t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B22C3/00
Inventor 郭玉杰胡睿沈续雨张文英包贤强丁丹丹陈子亮杨智明胡绪照左佳高金菊
Owner 高金菊
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com