Preparation method of ion induction patch

A technology of ion induction and ion accumulation, applied in the field of medical devices, to increase blood supply, promote blood circulation, and reduce nerve root inflammatory edema

Active Publication Date: 2013-04-03
GUANGDONG TAIBAO MEDICAL SCI TECH
View PDF4 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Existing plasters for pain relief, detumescence, and anti-inflammation for the treatment of hyperosteogeny or rheumatoid arthritis all contain various drugs, and their main function is to produce effects through the absorption of drugs by the affected part of the human body, and sometimes unavoidable side effects

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of ion induction patch
  • Preparation method of ion induction patch

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] Embodiment 1, Blend and stir 94wt% polytetrafluoroethylene micropowder and 6wt% nanometer far-infrared powder, and then form a film through pressing, drying and other processes. : The molding pressure is 20~30MPa, the sintering temperature is 350~390℃, the holding time is 3~5h, and it is cooled with the furnace; then, it is cut into 145mm*95mm squares; the ion conversion accumulation micro-processing is carried out on the membrane, and the dielectric breakdown is adopted The device is charged, the charging time is 100s, and the charging voltage is 100,000 SEV to form an ion accumulation layer; then place aluminum foil on both sides of the ion accumulation layer, the length and width of the aluminum foil are respectively 90% of the length and width of the ion accumulation layer, and the aluminum foil is obtained Ion stacking layer; then paste one side of the aluminum foil ion stacking layer on the self-adhesive non-woven fabric pasting base layer, and cover the other si...

Embodiment 2

[0022] Embodiment 2, Blend and stir 90wt% of polyimide micropowder and 10wt% of nanometer far-infrared powder, and then form a film through film pressing and drying. : The molding pressure is 20~30MPa, the sintering temperature is 350~390℃, the holding time is 3~5h, and it is cooled with the furnace; then, it is cut into 155mm*105mm squares; the ion conversion stacking micro-treatment is carried out on the membrane, and the dielectric breakdown is adopted The device is charged, the charging time is 120s, and the charging voltage is 80,000 SEV to form an ion accumulation layer; then place silver foil on both sides of the ion accumulation layer, and the length and width of the silver foil are 85% of the length and width of the ion accumulation layer. The silver foil ion accumulation layer is obtained; then, one side of the silver foil ion accumulation layer is pasted on the self-adhesive non-woven fabric pasting base layer, and the other side is covered with a glossy support pa...

Embodiment 3

[0023] Embodiment 3, Blend and stir 86wt% fluorinated polyarylether and 14wt% nano far-infrared powder, and then form a film through lamination, drying and other processes; Process: The forming pressure is 20~30MPa, the sintering temperature is 350~390℃, the holding time is 3~5h, and it is cooled with the furnace; then, it is cut into 145mm*95mm squares; the ion conversion accumulation micro-treatment is carried out on the membrane, and the medium shock is used Wear the device to charge, the charging time is 80s, the charging voltage is 120,000 SEV, and the ion accumulation layer is formed; then aluminum foil is placed on both sides of the ion accumulation layer, and the length and width of the aluminum foil are 95% of the length and width of the ion accumulation layer, respectively. Aluminum foil ion accumulation layer; then paste one side of the aluminum foil ion accumulation layer on the self-adhesive non-woven fabric pasting base layer, and cover the other side with a glo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Peel strengthaaaaaaaaaa
Holding poweraaaaaaaaaa
Peel strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to a preparation method of an ion induction patch. The method comprises the following steps of: blending and mixing organic high polymer fine powder with nanometer far infrared powder, pressing a film, drying and sizing to obtain a film; performing ion transformation deposition micro-treatment on the film to form an ion deposition layer; placing metal foils onto both sides of the ion deposition layer respectively to obtain a metal foil ion deposition layer; and sticking one side of the metal foil ion deposition layer to a sticking base layer and covering a surface gloss paper support layer on the other side of the metal foil ion deposition layer to obtain an ion induction patch. According to a prepared product, the principle of the biological stimulation effects of a high-voltage electrostatic field, far infrared rays and microcurrent on human bodies is utilized comprehensively, and electrostatic ion induction directly acts on afflicted parts, so that the proliferation of abnormal cells is suppressed effectively, normal growth of benign cells is activated, local blood circulation is facilitated in combination with far infrared rays, blood acidity is lowered, metabolism is facilitated, and the immunity is enhanced; and the product has the effects of rapidly relieving pain, diminishing inflammation and subsiding swelling.

Description

technical field [0001] The invention belongs to the field of medical devices and relates to a preparation method of an ion induction sticker. Background technique [0002] Cervical, lumbar and other joint pain is due to the degeneration of intervertebral disc tissue, resulting in the degeneration, hyperplasia, calcification, and ossification of the bony structure and its subsidiary soft tissue, resulting in compression of the spinal cord, nerves, and vascular tissue, resulting in a series of pathological changes and clinical manifestations , is a common and frequently-occurring disease in middle-aged and elderly people. [0003] Existing medicated plasters for treating hyperosteogeny or rheumatoid arthritis etc. for relieving pain, detumescence, and anti-inflammation all contain various medicines. Contents of the invention [0004] The object of the present invention is to provide a preparation method of an ion-inductive patch that does not contain drugs and has analgesic...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): A61F13/02A61N5/06A61N1/00
Inventor 卢亢陈锦涛黄建伟
Owner GUANGDONG TAIBAO MEDICAL SCI TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com