A titanium-based lead dioxide electrode co-doped with lanthanum and gadolinium and its preparation method and application

A technology of lead dioxide and co-doping, applied in chemical instruments and methods, plating of superimposed layers, electrolytic inorganic material plating, etc., can solve problems such as poor treatment effect, electrical poisoning, and difficulty in degrading pollutants , to achieve the effect of saving daily maintenance, mild conditions, and saving equipment investment costs

Active Publication Date: 2015-10-07
ZHEJIANG UNIV OF TECH
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the 1940s, due to technical constraints such as electricity and materials, traditional industrial wastewater was often treated with physical and chemical methods, biochemical methods, etc., and it was difficult to truly achieve the purpose of degrading such pollutants.
Although new lead dioxide electrodes based on Ti such as RuO 2 、Ir 2 o 5 , SnO 2 etc., to a certain extent, the energy efficiency and treatment effect have been improved, but when dealing with high-concentration organic wastewater, the electrode is prone to "poisoning" and the treatment effect is not good.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A titanium-based lead dioxide electrode co-doped with lanthanum and gadolinium and its preparation method and application
  • A titanium-based lead dioxide electrode co-doped with lanthanum and gadolinium and its preparation method and application
  • A titanium-based lead dioxide electrode co-doped with lanthanum and gadolinium and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] The electrode preparation method is as follows:

[0043] (1) Coarsening treatment of Ti substrate: Ti sheet (3*7.5cm 2 ) was sanded and rounded with sandpaper, soaked in NaOH solution (mass fraction 40%) for 30min, washed with water, and then kept at 60°C for H 2 SO 4 Soak in solution (mass fraction: 20%) for 20min, wash with water, and finally treat in oxalic acid solution (mass fraction: 15%) at 80°C for 3h. After washing with water, the coarsened titanium sheet was obtained, which was gray and pitted, and placed in 1wt% oxalic acid for later use.

[0044] (2) Thermally decompose the bottom layer of tin antimony oxide: evenly coat the PPM precursor coating solution on the surface of the roughened Ti base, first bake it in a tubular electric furnace at a constant temperature of 130°C for 25 minutes, and then raise the temperature of the electric furnace to Bake at 500°C for 15 minutes at a constant temperature to complete one cycle, and repeat the aforementioned cyc...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
quality scoreaaaaaaaaaa
quality scoreaaaaaaaaaa
Login to View More

Abstract

The invention provides a preparation method of a lanthanum-gadolinium co-doping titanium-based lead dioxide electrode. Rough processing is carried out on the surface of a titanium-based body, a tin antimony oxide bottom layer is prepared in a plating mode through a thermal decomposition method, then an alpha-PbO2 layer is electroplated in an alkalinity mode, finally a beta-PbO2 layer containing rare-earth metal oxide is electroplated in an acidity mode, and the lanthanum-gadolinium co-doping titanium-based lead dioxide electrode is prepared. Through the co-doping of the lanthanum and the gadolinium, a certain synergistic effect is achieved, the provided electrode can process and degrade organic matters under the normal temperature and the normal pressure, processing effect is good, cost is low, and good application value is achieved.

Description

(1) Technical field [0001] The invention relates to a novel titanium-based lead dioxide electrode co-doped with lanthanum and gadolinium, a preparation method and application thereof. (2) Background technology [0002] With the development of the economy, the number and types of refractory organic compounds in industrial wastewater are increasing day by day. These toxic and harmful high-concentration refractory organic wastewater has always restricted the sustainable development of my country's chemical, pharmaceutical, printing and dyeing, papermaking and other industries. It also affects the normal life and physical and mental health of the people. A large amount of industrial wastewater discharged by these industries has the characteristics of complex components, various types, difficult biochemical degradation, high chemical oxygen demand, toxic and harmful, and some are even teratogenic, carcinogenic, and mutagenic "three-cause" pollutants. Without effective control and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C23C28/04C23C18/12C25D9/04C25D9/06C02F1/461
Inventor 戴启洲陈建孟王家德沈宏夏伊静
Owner ZHEJIANG UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products