Metal rust-preventative oil containing trimerization glycerol monostearate

A technology of monostearate and tripolyglycerol, used in anti-corrosion coatings, coatings, etc., can solve the problem of insufficient anti-rust effect, and achieve excellent contact anti-rust performance, good gas-phase anti-rust effect, and good contact anti-rust effect. The effect of the rust effect

Inactive Publication Date: 2013-06-12
HUATAI LIGHT STEEL STRUCTURE SHANTOU
View PDF6 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the anti-rust effect of simple amines in mineral oil is not good enough, and amine salts or other compounds

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Metal rust-preventative oil containing trimerization glycerol monostearate
  • Metal rust-preventative oil containing trimerization glycerol monostearate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0015] A kind of metal antirust oil that contains tripolyglycerol monostearate, it is made by the raw material of following parts by weight (kg):

[0016] Zinc naphthenate 0.3, benzotriazole 0.6, 2-aminoethyl heptadecenyl imidazoline 1.6, No. 120 solvent oil 115, isobutyl methacrylate 2, silane coupling agent KH540 2.4, lanolin magnesium Soap 2.7, barium petroleum sulfonate 0.7, antioxidant BHT 0.7, alcohol ether glycoside 0.8, oleic acid triethanolamine 0.6, tripolyglycerol monostearate 1.4, methanol 0.5, silane coupling agent KH550 0.4, composite film-forming material 6. Modified nano potassium feldspar powder 0.5, antioxidant 626 0.2;

[0017] The composite film-forming material is prepared from the following raw materials in parts by weight: 145 rosin resin 38, fatty alcohol polyoxyethylene ether 10, methyl acetate 4, ethyl acetate 1, No. 120 solvent naphtha 72, butyl acrylate 3 , Dimethicone 2;

[0018] The preparation method of the modified nano-potassium feldspar powd...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses metal rust-preventative oil containing trimerization glycerol monostearate. The metal rust-preventative oil containing the trimerization glycerol monostearate comprises the following raw materials, by weight, 0.2 part-0.3 part of zinc naphthenate, 0.4 part-0.6 part of benzotriazole, 1.3 parts-1.6 parts of 2-aminoethyl-heptadecenyl-imidazoline, 105 parts-115 parts of number 120 solvent oil, 1 part-2 parts of methacrylic acid isobutyl ester, 1.2 parts-2.4 parts of a silane coupling agent KH540, 1.5 parts-2.7 parts of lanolin magnesium soap, 0.5 part-0.7 part of petroleum barium sulfonate, 0.5 part-0.7 part of antioxidant BHT, 0.6 part-0.8 part of alcohol ether glucoside, 0.4 part-0.6 part of oleic acid triethanolamine, 1.1 parts-1.4 parts of the trimerization glycerol monostearate, 0.4 part-0.5 part of carbinol, 0.2 part-0.4 part of a silane coupling agent KH550, 6 parts-8 parts of composite film-forming materials, 0.3 part-0.5 part of modified nanometer potassium feldspar powder, and 0.1 part-0.2 part of antioxidant 626. The metal rust-preventative oil containing the trimerization glycerol monostearate has good contact rust-preventative performance and a good gaseous phase rust-preventative effect. The metal rust-preventative oil containing the trimerization glycerol monostearate has the good gaseous phase rust-preventative effect and a contact rust-preventative effect to steel and brass.

Description

technical field [0001] The invention relates to the field of metal surface treatment agents, in particular to a metal antirust oil containing tripolyglycerol monostearate. Background technique [0002] Metal surface treatment agent refers to the general term for various chemical agents for metal surface treatment. Metal surface treatment includes degreasing, rust removal, phosphating, antirust and other substrate pretreatments, which are prepared for metal coating technology and metal protection technology. The quality of substrate pretreatment has a great influence on subsequent coating preparation and metal use. big impact. [0003] Oil-soluble rust inhibitors are also called oil-soluble corrosion inhibitors. Most are long carbon chain organic compounds with polar groups. The polar groups in the molecule are tightly adsorbed on the metal surface by the action of charge; the non-polar group long carbon chain hydrocarbons are facing the outside of the metal surface, and c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D4/02C09D4/06C09D7/12C09D5/08
Inventor 沈升好
Owner HUATAI LIGHT STEEL STRUCTURE SHANTOU
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap