Method for preparing environment-friendly water permeable bricks by using iron tailings
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of permeable bricks and iron tailings, applied in the field of using iron tailings to prepare environmentally friendly permeable bricks, can solve the problems of low utilization of tailings resources, improve mechanical strength and wear resistance, improve product strength, and improve production technology simple effect
Inactive Publication Date: 2014-05-14
UNIV OF SCI & TECH BEIJING +2
View PDF2 Cites 3 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0006] The purpose of the present invention is to provide a method for applying iron tailings to environment-friendly permeable bricks, and successfully develop green environment-friendly permeable bricks with iron tailings as the main raw material. The bricks have good water permeability, high strength, and can be fired The temperature is appropriate, the cost is low, and the structure is excellent. It is an environmentally friendly green building material suitable for urban square pavements and sidewalks. It not only solves the problem of low utilization of tailings resources, but also provides a new type of permeable material for building environmental protection. Realized turning waste into treasure, turning harm into profit
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0021] According to the weight percentage composition in the table below, the environmentally friendly permeable bricks are prepared according to the technological process of raw material crushing, ball milling, batching, mixing, drying, molding and firing
[0022]
[0023] Some of the process parameters are: wet grinding time: 16 hours, pass through a 200-mesh sieve; dry pressing molding, molding pressure is 30MPa; firing temperature: 1150°C, heat preservation for 40 minutes.
[0024] The prepared foamed ceramic material has a uniform pore size distribution, a porosity of 30%, and a bulk density of 12g / cm 3 , water permeability 0.013cm / s, compressive strength 50MPa.
Embodiment 2
[0026] According to the weight percentage composition in the following table, the environmentally friendly permeable bricks are prepared according to the technological process of raw material crushing, ball milling, batching, mixing, drying, firing and molding, and mechanical processing
[0027]
[0028] Some of the process parameters are: ball milling time: 12 hours, passing through a 200-mesh sieve; the dried powder is directly put into the baffle for firing without molding; firing temperature: 1200°C, and kept for 40 minutes.
[0029] The prepared foamed ceramic material has a uniform pore size distribution, a porosity of 46%, and a bulk density of 0.9g / cm 3 , the water permeability is 0.024cm / s, and the compressive strength is 36MPa.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
particle size
aaaaa
aaaaa
compressive strength
aaaaa
aaaaa
density
aaaaa
aaaaa
Login to view more
Abstract
The invention discloses a method for preparing environment-friendly water permeable bricks by using iron tailings, belonging to the field of comprehensive utilization of iron tailing resources and construction ceramic materials. The method is characterized in that through taking iron tailings as basic aggregates and introducing a certain amount of waste broken glass, an environment-friendly water permeable brick with excellent performance is prepared. The method comprises the following process steps of raw material crushing, ball milling, material dispensing, mixing, drying, molding, sintering, cutting and grinding. The dispensed material comprises the following ingredients in percentage by weight: 30-60% of iron tailings powder, 5-15% waste glass powder, 15-30% of clay, 15-24% of quartz, 5-15% of potash feldspar, and 0.25-1.5% of silicon carbide. The prepared water permeable brick is high in compressive strength, good in abrasion resistance and excellent in water permeability, and accords with national related standards of water permeable bricks, therefore, the method creates a new way for the high-technology and high value-added application of iron tailing resources.
Description
technical field [0001] The invention belongs to the field of comprehensive utilization of iron tailings resources and building ceramic materials, and in particular relates to a method for preparing environment-friendly permeable bricks by using iron tailings. technical background [0002] With the development of the economy and the process of modernization, many towns are gradually covered by reinforced concrete houses, large-scale infrastructure and various impermeable sites and roads. While providing convenience for people, these impervious surfaces also bring many negative impacts to the ecological environment of the city. The hardening of the surface makes it difficult for atmospheric precipitation to infiltrate into the ground in a timely manner, increasing surface runoff, forming a heat island effect and insufficient drainage, causing environmental problems such as waterlogging and urban surface settlement. Permeable bricks have many characteristics that other bricks d...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more