Polyphenyl ether resin alloy material, and preparation method and application thereof

A polyphenylene ether resin and alloy material technology, applied in the field of polyphenylene ether resin alloy materials, can solve problems such as stress cracking, poor oil resistance, and high fluidity, and achieve the effects of poor fluidity, low cost, and high fluidity

Active Publication Date: 2014-01-08
江苏沃特新材料科技有限公司
View PDF5 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although polyphenylene ether alloy materials have excellent heat resistance and mechanical strength, they also have some fatal defects, such as poor fluidity, poor oil resistance, and severe stress cracki

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polyphenyl ether resin alloy material, and preparation method and application thereof
  • Polyphenyl ether resin alloy material, and preparation method and application thereof
  • Polyphenyl ether resin alloy material, and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0026] Example 1

[0027] The raw materials and dosages used in this example are shown in Table 1, where:

[0028] Polyphenylene ether resin: a polymer selected from 2,6-dimethylphenol with an intrinsic viscosity of 0.4dl / g;

[0029] Polystyrene resin: composed of polystyrene and high-impact polystyrene in a weight ratio of 1:3;

[0030] Polyolefin: It is composed of polypropylene, ethylene propylene copolymer and polybutene in a weight ratio of 3:1:1;

[0031] Elastomer: It is composed of styrene butadiene rubber, hydrogenated styrene butadiene rubber, polyacrylate rubber, 1,2 polybutadiene elastomer in a weight ratio of 4:4:1:1;

[0032] Flame retardant: It is composed of phosphorus flame retardant and nitrogen flame retardant in a weight ratio of 3:1, wherein the phosphorus flame retardant is a phosphate flame retardant, and the nitrogen flame retardant is melamine;

[0033] Lubricant: It is composed of calcium stearate, zinc stearate and stearic acid in a weight ratio of 1:1:1;

[0034...

Example Embodiment

[0039] Example 2

[0040] The raw materials and dosages used in this embodiment are shown in Table 1. The raw materials other than polyphenylene ether resin, polystyrene resin, and graft are the same as those in Embodiment 1.

[0041] In this example, polyphenylene ether resin: a polymer of 2,6-dimethylphenol, a copolymer of 2,6-dimethylphenol and 2,3,6-trimethylphenol in a weight ratio of 2: 1 composition of the mixture, its intrinsic viscosity is 0.5dl / g;

[0042] In this example, polystyrene resin: selected from polystyrene;

[0043] In this example, the graft: styrene-butadiene rubber as the base material, and the graft is a mixture of acetic anhydride, succinic anhydride, and benzoic anhydride in a weight ratio of 3:1:1

[0044] In this example, the preparation method of the polyphenylene ether resin alloy material is the same as in Example 1, and will not be repeated here.

Example Embodiment

[0045] Example 3

[0046] The raw materials and dosages used in this embodiment are shown in Table 1. The raw materials other than polyolefin, elastomer, and antioxidant are the same as in Embodiment 1.

[0047] In this example, polyolefin: selected from polyethylene;

[0048] In this example, elastomer: a mixture of hydrogenated styrene butadiene rubber and binary ethylene propylene rubber in a weight ratio of 1:1;

[0049] In this example, antioxidant: It is composed of main antioxidant and auxiliary antioxidant in a weight ratio of 3:1, among which, the main antioxidant is 3,5-di-tert-butyl-4-hydroxyphenylpropionic acid Stearyl alcohol ester, 2,2-methylene bis(4-methyl-6-tert-butylphenol) is a mixture of 1:1 by weight, and the auxiliary antioxidant is bis(2,4-di-tert-butyl (Phenyl) pentaerythritol diphosphate and bis(octadecyl) pentaerythritol diphosphate in a weight ratio of 1:1;

[0050] In this example, the preparation method of the polyphenylene ether resin alloy material is th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Intrinsic viscosityaaaaaaaaaa
Intrinsic viscosityaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the field of high-polymer alloy materials, and particularly relates to a polyphenyl ether resin alloy material used for processing automobile spare tire covers and a preparation method of the polyphenyl ether resin alloy material. The polyphenyl ether resin alloy material is prepared by, by weight, 20-40 parts of polyphenyl ether resin, 50-80 parts of polystyrene resin, 1-3 parts of polyolefin, 1-8 parts of elastomer, 1-15 parts of flame retardant, 0.05-0.30 part of lubricant, 1-3 parts of inorganic filler, 3-8 parts of grafting bodies, and 0.10-0.50 part of antioxidant. By adjusting formula composition and selecting proper process and extruding conditions, the problem about mobility of the polyphenyl ether resin alloy material is solved. The polyphenyl ether resin alloy material has high mobility and no stress cracking after spraying, is capable of sufficiently meeting operating requirements of the application field of automobile parts and quite applicable to raw materials for automobile spare tire covers.

Description

Technical field [0001] The invention belongs to the field of polymer alloy materials, and specifically relates to a polyphenylene ether resin alloy material, a preparation method and application thereof. Background technique [0002] Polyphenylene ether resin has many excellent properties, such as mechanical properties, hydrolysis resistance, acid and alkali corrosion resistance, heat resistance, dimensional stability, etc. Its products are widely used in electronic appliances, auto parts, water treatment equipment, Chemical industry and other fields. Although polyphenylene ether alloy materials have excellent heat resistance and mechanical strength, they also have some fatal defects, such as poor fluidity, poor oil resistance, and severe stress cracking. For the relatively large parts of automobiles, high fluidity is required, and no stress cracking occurs after spraying. This has always been a major challenge in the application of polyphenylene ether resin. Summary of the inv...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L25/06C08L71/12C08L23/00C08L23/06C08L23/12C08L23/08C08L23/20C08L9/06C08L15/00C08L23/16C08L33/04C08L9/00C08L51/04
Inventor 李海涛何征吴宪孙伟张宝军张国军廖峻峰于强
Owner 江苏沃特新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap