Environment-friendly cold-resistant polyvinyl chloride cable material

A polyvinyl chloride cable and polyvinyl chloride technology are applied in the field of cable materials, which can solve the problem of low impact strength, achieve good impact resistance and solve the effect of poor impact resistance.

Inactive Publication Date: 2014-01-15
东莞虎塑塑胶科技有限公司
View PDF5 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Wire and cable are indispensable and important materials in industrial and agricultural production and modern life. my country is the world's largest producer of wire and cable. The wire and cable industry occupies a very important position in my coun

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Environment-friendly cold-resistant polyvinyl chloride cable material
  • Environment-friendly cold-resistant polyvinyl chloride cable material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0017] An environment-friendly cold-resistant polyvinyl chloride cable material, which is prepared from the following weight (kg) component raw materials:

[0018] Polyvinyl chloride 65, polysiloxane 14, silicone rubber 9, dioctyl terephthalate 13, triethylene glycol diisocaprylate 9, epoxidized triglyceride 5, acetyl tributyl citrate Ester 8, Cobalt Naphthenate 1, Ethyl Silicone Oil 0.2, Chlorinated Polyethylene 4, Aluminum Hydroxide 14, Triphenyl Phosphate 6, Decabromodiphenyl Ether 5, Light Active Calcium Carbonate 9, Bentonite 6, Zinc Oxide 1. Titanium dioxide 2, volcanic ash 5, high wear-resistant carbon black 7, Ca-Zn composite stabilizer 2, antioxidant 1076 0.5, dicumyl peroxide DCP 0.2, butyl stearate 0.3, barium stearate 2 , zinc stearate 0.4, modified filler 9,

[0019] Among them, the modified filler is prepared by the following method: a. Take the following raw materials in parts by weight: kaolin 205, diatomite 125, sepiolite 11, nano-carbon 2, zirconium fluoride...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides an environment-friendly cold-resistant polyvinyl chloride cable material. The polyvinyl chloride cable material is prepared with the following components and raw materials by weight: 60-70 parts of polyvinyl chloride, 10-15 parts of polysiloxane, 8-10 parts of silicon rubber, 12-15 parts of dioctyl terephthalate, 5-10 parts of triethylene glycol di-2-ethylhexoate (triglycol dioctate), 3-5 parts of epoxy triglyceride, 8-10 parts of tributyl acetocitrate, 1-2 parts of cobalt naphthenate, 0.2-0.3 part of ethyl silicon oil, 2-5 parts of chlorinated polyethylene, 10-15 parts of aluminum hydroxide, 5-6 parts of triphenyl phosphate, 4-6 parts of decabromodiphenyl ether, 8-10 parts of light activated calcium carbonate, 5-8 parts of bentonite, 1-2 parts of zinc oxide, 1-2 parts of titanium dioxide, 5-6 parts of cinerite, 6-8 parts of highly wear-resistant carbon black, 2-3 parts of Ca-Zn compound stabilizer, 0.1-1 part of antioxidant 1076, 0.1-0.3 part of dicumyl peroxide (DCP), 0.2-0.3 part of butyl stearate, 1-2 parts of barium stearate, 0.1-0.5 part of zinc stearate, and 8-10 parts of modified filler. The cable material is of good shock resistance at low temperature and environment-protection property, thereby solving the problem that the existing polyvinyl chloride cable material is not environment-friendly, and bad in the shock resistance at low temperature.

Description

technical field [0001] The invention relates to the field of cable materials, in particular to an environment-friendly cold-resistant polyvinyl chloride cable material. Background technique [0002] Wire and cable are indispensable and important materials in industrial and agricultural production and modern life. my country is the world's largest producer of wire and cable. The wire and cable industry occupies a very important position in my country's national economy. However, at present, the market The cable material has low impact strength under low temperature conditions, and the invention provides an environment-friendly cable material with good impact strength at low temperature. Contents of the invention [0003] The invention provides an environment-friendly cold-resistant polyvinyl chloride cable material. The cable wire processed from the cable material of the invention has the characteristics of good impact resistance under low temperature conditions. [0004] ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L27/06C08L83/04C08K13/06C08K9/02C08K3/34C08K3/36C08K5/1545C08K5/1539C08K3/22
Inventor 谢华
Owner 东莞虎塑塑胶科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap