Fluororesin modified high-chlorinated polyethylene fireproof anticorrosion composite coating

A technology of high chlorinated polyethylene and composite coatings, which is applied in the direction of anti-corrosion coatings, fireproof coatings, coatings, etc., and can solve problems such as composite coating peeling off

Active Publication Date: 2014-02-05
ZHEJIANG YONGGUWEIHUA COATING
View PDF8 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Overcome the disadvantages of the composite coating falling off during use due to the use of different manufacturers and different coatings in the past

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] 1. The preparation method of component A of fluororesin modified high-chlorinated polyethylene fireproof and anticorrosion composite coating is: put 200# solvent oil with a weight ratio of 7.0-80 parts into the reaction kettle, and stir at a stirring speed of 80-120 rpm Put in 11.0-13.0 parts of butyl acetate, raise the temperature of the material to 60±5°C, slowly add 8.0-9.0 parts of modified high-chlorinated polyethylene resin, continue stirring until the material is completely dissolved, then add 6.0-7.0 parts of fluorocarbon resin, 4.0-5.0 parts of chlorinated paraffin and 10.5-12.0 parts of prepared polyvinylidene fluoride glue, stir well to dissolve the material completely and form a transparent clear material, then add 0.7-0.9 parts of polyacid polymer dispersant, 0.8-1.0 parts Nano silicon dioxide, then increase the stirring speed from the original 80-120 rpm to 400 rpm, then add 4.0-6.0 parts of titanium dioxide, 1.0-3.0 parts of zinc oxide, 16.0-17.0 parts of ...

Embodiment 2

[0018] 1. Preparation of group A of fluororesin modified high-chlorinated polyethylene fireproof and anticorrosion composite coating: put 8.0 parts of 200# solvent oil into the reaction kettle, put 12.0 parts of butyl acetate at a stirring speed of 80-120 rpm, and put Raise the temperature of the material to 60±5°C, and slowly add 8.0 parts of modified high-chlorinated polyethylene resin, continue to stir until the resin is completely dissolved, then add 7.0 parts of fluorocarbon resin, 5.0 parts of chlorinated paraffin and 11.0 parts of polyvinylidene fluoride Liquid, fully stirred to dissolve the material completely and form a transparent clear material, then add 0.8 parts of polycarboxylate polymer dispersant, 0.9 parts of nano-silica, and increase the stirring speed from the original 80-120 rpm to 400 rpm Add 4.0 parts of titanium dioxide, 2.0 parts of zinc oxide, 16.0 parts of ammonium polyphosphate, 14.0 parts of pentaerythritol, 6.0 parts of melamine, and 5.0 parts of fl...

Embodiment 3

[0022] 1. Preparation of Component A of fluororesin modified high chlorinated polyethylene fireproof and anticorrosion composite coating: same as Example 1;

[0023] 2. The amount of component B in the fluororesin modified high-chlorinated polyethylene fireproof and anticorrosion composite coating: the same as in Example 2;

[0024] 3. Preparation of fluororesin-modified high-chlorinated polyethylene fire-proof and anti-corrosion composite coating: the same as in Example 2.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
flame retardantaaaaaaaaaa
flame retardantaaaaaaaaaa
Login to View More

Abstract

The invention discloses a fluororesin modified high-chlorinated polyethylene fireproof anticorrosion composite coating, which is composed of two components A and B, wherein the component A is prepared from polyvinylidene fluoride glue solution, ammonium polyphosphate, modified high-chlorinated polyethylene resin, pentaerythritol, melamine, titanium dioxide, zinc oxide, fluoroferrophosphorus, nanosilicon dioxide, carboxylic polymer, fluorocarbon modified polysiloxane, miscella, butyl acetate, chlorcosane and the like; and the component B is prepared from isocyanate and ethyl acetate; the fluororesin modified high-chlorinated polyethylene fireproof anticorrosion composite coating is prepared from the component A and the component B in the weight ratio of 100.0:(9.0-11.0); the fluororesin modified high-chlorinated polyethylene fireproof anticorrosion composite coating is called as FFFH fireproof anticorrosion coating for short; the coating has the characteristics of high strength, low specific weight, outstanding corrosion resistance and fire resistance, and the like. The fluororesin modified high-chlorinated polyethylene fireproof anticorrosion composite coating can be widely applied to industries such as chemical industry and food, and has excellent economic and social benefits.

Description

1. Technical field [0001] The invention belongs to the field of industrial anti-corrosion, and is a two-component solvent-based fluororesin modified high-chlorinated polyethylene coating, which has dual functions of anti-corrosion and fire prevention, referred to as FVC fire-proof and anti-corrosion composite coating. 2. Technical background [0002] At present, there are many kinds of corrosion-resistant coatings on the market in our country, each with its own characteristics, but the anti-corrosion ability of fire-resistant coatings is poor, and corrosion-resistant coatings do not have fire-proof functions, so that projects that require dual functions of fire protection and corrosion protection must sometimes choose both anti-corrosion and fire protection. The combination of the two coatings will lead to an increase in the construction period and an increase in the project cost. Sometimes the combination of the two coatings is not ideal and the service life of the coating w...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D123/28C09D127/16C09D127/12C09D5/08C09D5/18C09D7/12
Inventor 金辉杨华福金如朋
Owner ZHEJIANG YONGGUWEIHUA COATING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com