Flame-retardant foamed sheet

A technology of foamed boards and raw materials, applied in the field of boards, can solve problems such as unsatisfactory flame retardant properties, and achieve the effects of low density, convenient and simple raw materials, and excellent flame retardant effects

Inactive Publication Date: 2014-02-12
安徽玉龙新型建材有限公司
View PDF4 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the flame retardant properties of the existing flame retardant foaming materials are still not ideal, and cannot meet some occasions with high fire protection requirements, and are still subject to some limitations in use.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0014] specific implementation plan

[0015] The present invention will be described in detail below through specific examples.

[0016] A flame-retardant foamed board made of the following raw materials in parts by weight (kg): SG-3PVC resin 100, light calcium carbonate 5, titanium dioxide 10, azodicarbonamide 4, hexamethylenetetramine 1.4 , Nano titanium dioxide 2.8, Precipitated barium sulfate 4, Sodium dodecylbenzene sulfonate 1, Dibutyltin dilaurate 1, Diethylene glycol dibenzoate 4, Zinc oxide 2, Dicumyl peroxide 1. Modified filler 6;

[0017] The modified filler is prepared by the following method: Weigh the following raw materials in parts by weight (kg): attapulgite 90, diatomite 20, straw ash 50, sodium dodecylbenzenesulfonate 2, ammonium bicarbonate 2, Mica 3, 2-amino-2-methyl-1-propanol 3, actinolite 5, magnesium sulfate 2, nano silicon dioxide 1, epoxy soybean oil 2, sodium metasilicate 2, sodium selenite 4 The preparation method is to put attapulgite, diatomac...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to View More

Abstract

The invention discloses a flame-retardant foamed sheet which is characterized by being prepared from the following raw materials in parts by weight: 100 parts of SG-3PVC, 5-7 parts of light calcium carbonate, 10-14 parts of titanium dioxide, 4-5 parts of azodicarbonamide, 1.4-1.6 parts of hexamine, 2.8-3.2 parts of nanometer titania, 4-6 parts of precipitated barium sulphate, 1-2 parts of sodium dodecyl benzene sulfonate, 1-2 parts of dibutyltin dilaurate, 4-5 parts of diethylene glycol dibenzoate, 2-3 parts of zinc oxide, 1-2 parts of dicumyl peroxide and 6-8 parts of modified packing. The foamed sheet has an uncommon excellent flame-retardant effect, is low in density, light in weight, sound-insulated, heat-insulated, attractive in appearance and suitable for serving as a building material and is convenient and simple in raw material source, low in production cost and suitable for large-area popularization.

Description

technical field [0001] The invention relates to a board, in particular to a flame-retardant foamed board. Background technique [0002] The foamed board made of polyvinyl chloride is mainly used in the manufacture of advertising cabinets and bathroom cabinets. It was the first to introduce equipment and technology from Europe, and the quoted product standards also refer to European standards. The density of the board is relatively high. In recent years, with the development of domestic equipment, especially the development of additives, the density of the board has been greatly reduced, which can reach 0.4~0.45g / cm3, thus greatly improving the application space of the board and reducing the cost of use , but how to further reduce the density of the board and still achieve better performance is a bottleneck in the research of lightweight boards. [0003] Flame-retardant foaming materials are widely used in various occasions that require fire protection because of their light...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08K13/06C08K3/26C08K3/22C08K5/17C08K3/30C08K5/42C08J9/10
Inventor 丁继军陈志刚张兴民
Owner 安徽玉龙新型建材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com