High-temperature resistant and wear-resistant alloy steel lining plate material and preparation method thereof

A technology of alloy steel and high temperature resistance, which is applied in the field of high temperature and wear-resistant alloy steel liner materials and its preparation, can solve the problems of brittleness and corrosion resistance of medium and low alloy steels, unsatisfactory wear resistance and corrosion resistance, Poor toughness and other problems, to achieve good wear resistance, improve yield, and good plasticity

Inactive Publication Date: 2014-02-26
CHUZHOU UNIV
View PDF1 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, in domestic practical applications, high manganese steel is still dominant. Among several mainstream materials, high manganese steel has good toughness, but its wear resistance and corrosion resistance are not ideal; high chromium cast iron has good wear resistance, but its toughness is low. Poor; the brittleness and corrosion resistance of medium and low alloy steels are not up to standard

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0013] A high-temperature and wear-resistant alloy steel liner material, which contains chemical element components and mass percentages: carbon 0.2-0.4, silicon 0.2-0.4, manganese 3.5-3.7, chromium 0.7-0.9, molybdenum 0.8-1.1, vanadium 1.2-1.4, Lanthanum 0.1-0.15, Nb0.04-0.07, S≤0.04, P≤0.04, the balance is iron.

[0014] The production method of the high-temperature and wear-resistant alloy steel liner material is as follows:

[0015] (1) Prepare pig iron and scrap iron in a ratio of 1:1.6 as the source of iron matrix, put pig iron into the furnace for melting, perform desulfurization, deoxidation, use refining agent for one-time refining, add alloy components for alloying, and then add scrap iron to melt , adding refining agent for secondary refining, testing and adjusting the content of chemical elements to pass, casting, post-casting heat treatment, etc.;

[0016] (2) The order of batches of alloying elements put into the furnace during the alloying process is: (1) chrom...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
yield strengthaaaaaaaaaa
impact absorption energyaaaaaaaaaa
Login to view more

Abstract

The invention discloses a high-temperature resistant and wear-resistant alloy steel lining plate material which comprises the following chemical elements in percentage by mass: 0.2-0.4% of carbon, 0.2-0.4% of silicon, 3.5-3.7% of manganese, 0.7-0.9% of chromium, 0.8-1.1% of molybdenum, 1.2-1.4% of vanadium, 0.1-0.15% of lanthanum, 0.04-0.07% of Nb, less than or equal to 0.04% of S, less than or equal to 0.04% of P and the balance of iron. In the lining plate provided by the invention, the alloy steel obtained by adding the elements such as lanthanum, molybdenum and niobium into low-carbon steel has the advantages of high hardness, high strength, good wear resistance, high-temperature resistance, good toughness, good plasticity, corrosion resistance and high cost performance. In the lining plate material disclosed by the invention, the waste iron is partially used as the raw material, secondary refining is performed, the thermal treatment temperature after casting is reasonably controlled, the raw material is fed in batches, and the comprehensive mechanical properties are improved. A refining agent is applied to the casting production; and in a casting, the porosity is reduced by 1-2 degrees, and the oxide inclusion is at about level 2.

Description

technical field [0001] The invention relates to the field of metal materials, in particular to a high-temperature-resistant and wear-resistant alloy steel lining material and a preparation method thereof. Background technique [0002] After more than 30 years of development, the liner material has experienced the development of high manganese steel, ordinary white cast steel, nickel hard cast iron, high chromium white iron, modified high manganese steel and medium and low alloy steel with various quenching and tempering processes stage. At present, in domestic practical applications, high manganese steel is still dominant. Among several mainstream materials, high manganese steel has good toughness, but its wear resistance and corrosion resistance are not ideal; high chromium cast iron has good wear resistance, but its toughness is low. Poor; the brittleness and corrosion resistance of medium and low alloy steels are not up to standard. It is necessary to research and devel...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/38C22C33/04C21D6/00
Inventor 丁健葛浩汪俊夏岩磊杨玭刘克忠
Owner CHUZHOU UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap