A kind of functionalized graphene-doped epoxy resin conductive adhesive and preparation method thereof

A technology of epoxy resin and graphene, which is applied in the field of conductive adhesives, can solve problems such as the decline of electrical conductivity, and achieve the effects of not easy to fall off and migrate, improve utilization rate, and high uniformity and stability

Active Publication Date: 2016-11-02
道尔化成电子材料(上海)有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] The present invention aims at the disadvantages of the existing epoxy resin conductive adhesives that rely solely on filling flake silver powder to obtain electrical conductivity, and the silver powder is easily oxidized during the curing process, resulting in a decrease in electrical conductivity, and provides a simple method for preparing graphene-silver nanowires. Conductive filler and applied to epoxy resin conductive adhesive
Utilizing the high conductivity produced by the synergistic effect of graphene and silver nanowires, the technical problem of the drop in conductivity caused by easy oxidation during the curing process caused by the simple use of silver powder is improved, thereby obtaining extremely stable high conductivity and preparing a A high-conductivity silver nanowire functionalized graphene-doped epoxy conductive adhesive

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of functionalized graphene-doped epoxy resin conductive adhesive and preparation method thereof
  • A kind of functionalized graphene-doped epoxy resin conductive adhesive and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] (1) Prepare 1ml of 0.1M silver nitrate aqueous solution and 1ml of 0.1M sodium citrate aqueous solution respectively, then mix and shake well. Add 10ml of deionized water and sonicate for 30 minutes. It was then dropped into 20ml of graphene oxide aqueous solution with a concentration of 1.08mg / ml, ultrasonicated for 30 minutes, poured into a 250ml single-necked flask, and then magnetically stirred for 12 hours at normal temperature with an aluminum film.

[0030] (2) Then heat in an oil bath to 130°C for 3 hours. Afterwards, 0.216 g of sodium citrate was added and the temperature was maintained at 90° C. for 10 hours. Move the product to the platform to cool down to room temperature, and then centrifuge and wash thoroughly with deionized water and ethanol solution. Prepared into 2mg / ml ethanol solution.

[0031] (3) Put 28.8021g of bisphenol A type E-51 epoxy resin, 1.089g of curing agent dicyandiamide and 0.1089g of curing accelerator 2,4,6-tris(dimethylaminomethyl...

Embodiment 2

[0033] (1) Prepare 1ml of silver nitrate aqueous solution with concentration of 0.1M and 1ml of sodium citrate aqueous solution with concentration of 0.05M respectively, then mix and shake well. Add 10ml of deionized water and sonicate for 30 minutes. It was then dropped into 50ml of graphene oxide aqueous solution with a concentration of 1.08mg / ml, ultrasonicated for 30 minutes, poured into a 250ml single-necked flask, and then magnetically stirred for 15 hours at normal temperature with an aluminum film.

[0034] (2) Then heat in an oil bath to 130°C for 3 hours. Afterwards, 1.08 g of sodium citrate was added and the temperature was maintained at 90° C. for 10 hours. Move the product to the platform to cool down to room temperature, and then centrifuge and wash thoroughly with deionized water and ethanol solution. Prepared into 5mg / ml ethanol solution.

[0035] (3) Put 29.1g of bisphenol F type epoxy resin, 0.816g of curing agent dicyandiamide and 0.084g of curing acceler...

Embodiment 3

[0037] (1) Prepare 1ml of 0.1M silver nitrate aqueous solution and 1ml of 0.1M sodium citrate aqueous solution respectively, then mix and shake well. Add 10ml of deionized water and sonicate for 30 minutes. It was then dropped into 50ml of graphene oxide aqueous solution with a concentration of 1.08mg / ml, ultrasonicated for 30 minutes, poured into a 250ml single-necked flask, and then magnetically stirred for 14 hours at normal temperature with an aluminum film.

[0038] (2) Then heat in an oil bath to 130°C for 3 hours. Afterwards, 1.08 g of sodium citrate was added to maintain 90° C. for 10 hours. Move the product to the platform to cool down to room temperature, and then centrifuge and wash thoroughly with deionized water and ethanol solution. Prepared into 5mg / ml ethanol solution.

[0039] (3) 30.3125g of bisphenol A type E-51 epoxy resin, 0.8525g of curing agent dicyandiamide and 0.085g of curing accelerator 2,4,6-tris(dimethylaminomethyl)phenol are placed in the The ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
electron mobilityaaaaaaaaaa
Login to View More

Abstract

The invention relates to a functionalized graphene-doped epoxy resin conductive adhesive and a preparation method thereof, belonging to the technical field of conductive adhesives. Firstly, graphene oxide colloids (GO) with stable dispersion were prepared by Hummers method, and then silver nanowires were induced to grow in situ on GO sheets to prepare silver nanowires / graphene nanohybrid materials. The in situ assembly of silver nanowires and graphene produces a synergistic effect, and the prepared nanocomposite material has extremely high conductivity and processing stability, avoids the agglomeration of graphene in epoxy resin, and can be used as a filler to uniformly disperse Conductive adhesives with excellent electrical conductivity were prepared in epoxy resins. The epoxy resin conductive adhesive in the present invention is based on the high conductivity of graphene and silver nanowires. Under the given process conditions, the conductivity and bonding strength of the adhesive are improved, and it is especially suitable for high-end refined electronic and electrical components. Conductive packaging and bonding, has a wide range of application prospects.

Description

technical field [0001] The invention relates to a preparation method of high-conductivity silver nanowire functionalized graphene-doped epoxy resin conductive adhesive, belongs to the technical field of conductive adhesive, is an improvement on the prior art, and specifically relates to the raw material of graphene-silver nanowire Bit preparation and its application in epoxy resin. Background technique [0002] Low electrical and thermal conductivity, poor reliability and high price are the bottlenecks restricting the development of conductive adhesives. Graphene, which has attracted much attention internationally, has ultra-high and unusually stable electrical and thermal conductivity and mechanical strength, and is one of the most promising conductive filling materials. However, the application of graphene in conductive adhesives faces the problem that it is difficult to Large-scale preparation of defect-free single-layer graphene, graphene is easy to aggregate, and lacks...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J9/02C09J163/00C09J11/04C09J11/06
Inventor 王标兵王玉鹏
Owner 道尔化成电子材料(上海)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com