Preparation method of polystyrene-acrylate core-shell composite emulsion

An acrylate and polystyrene technology, applied in the field of emulsion preparation, can solve the problems of anti-blocking, poor heat resistance, etc., and achieve the effects of transparent film formation, improved cohesive strength, and optimized construction process

Inactive Publication Date: 2016-05-11
NORTHEAST FORESTRY UNIVERSITY
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The present invention aims to solve the problems that existing thermoplastic polystyrene-acrylate random copolymers often cannot have the advantages of both at the same time, and still have problems such as anti-blocking and poor heat resistance; thereby providing polystyrene-acrylate core-shell composite Preparation method of emulsion

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of polystyrene-acrylate core-shell composite emulsion
  • Preparation method of polystyrene-acrylate core-shell composite emulsion
  • Preparation method of polystyrene-acrylate core-shell composite emulsion

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach 1

[0022] Embodiment 1: In this embodiment, the polystyrene-acrylate core-shell composite emulsion is prepared as follows:

[0023] Step 1. Weighing by weight percentage: 72% distilled water, 17.7% vinyl mixed monomer, 8.8% acrylate mixed monomer, 1.0% composite emulsifier, 0.38% pH buffer and 0.12% initiator;

[0024] Among them, the vinyl mixed monomer is composed of 80% styrene and 20% butyl acrylate by weight; the acrylate mixed monomer is composed of 50% butyl acrylate, 46% methyl methacrylate and 4% methacrylic acid It is mixed; the compound emulsifier is a mixture of alkylphenol polyoxyethylene ether and sodium lauryl sulfate at a mass ratio of 2:1; the initiator is ammonium persulfate; the pH buffer is sodium carbonate.

[0025] Step 2. Add the distilled water weighed in step 1 into a four-necked bottle, raise the temperature to 55°C, add compound emulsifier and pH buffer, then add 20% of the vinyl mixed monomer weighed in step 1, stir and emulsify for 30 minutes , add 3...

specific Embodiment approach 2

[0028] Specific embodiment two: In this embodiment, polystyrene-acrylate core-shell composite emulsion is prepared according to the following method:

[0029] Step 1. Weigh respectively by weight percentage: 61.2% distilled water, 13.3% vinyl mixed monomer, 23.7% acrylic acid mixed monomer, 1.4% composite emulsifier, 0.32% pH buffer and 0.08% initiator;

[0030] Among them, the vinyl mixed monomer is mixed by 85.7% styrene and 14.3% butyl acrylate by weight percentage; the acrylate mixed monomer is mixed by 54% butyl acrylate, 44% methyl methacrylate and 2% acrylic acid The composite emulsifier is a mixture of alkylphenol polyoxyethylene ether and sodium dodecylsulfonate in a mass ratio of 1:4; the initiator is potassium persulfate; the pH buffer is sodium bicarbonate.

[0031] Step 2. Add the distilled water weighed in step 1 into a four-necked bottle, raise the temperature to 50°C, add compound emulsifier and pH buffer, then add 15% of the vinyl mixed monomer weighed in step...

specific Embodiment approach 3

[0034] Specific embodiment three: In this embodiment, polystyrene-acrylate core-shell composite emulsion is prepared according to the following method:

[0035] Step 1. Weigh respectively by weight percentage: 61% distilled water, 9.1% vinyl mixed monomer, 28% acrylate mixed monomer, 1.5% composite emulsifier, 0.25% pH buffer and 0.15% initiator;

[0036] Among them, the vinyl mixed monomer is composed of 70.6% styrene and 29.4% butyl acrylate by weight; the acrylate mixed monomer is composed of 50% butyl acrylate, 46% ethyl methacrylate and 4% methacrylic acid It is made by mixing; the compound emulsifier is a mixture of alkylphenol polyoxyethylene ether and sodium lauryl sulfate at a mass ratio of 2:3; the initiator is ammonium persulfate; the pH buffer is dipotassium hydrogen phosphate.

[0037] Step 2. Add the distilled water weighed in step 1 into a four-necked bottle, raise the temperature to 58°C, add compound emulsifier and pH buffer, then add 20% of the vinyl mixed mo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of a polystyrene-acrylate core-shell composite emulsion, belongs to the emulsion preparation field, and solves the problems of adhesion resistance, poor heat resistance and the like of a thermoplastic polystyrene-acrylate random copolymer in the prior art. The preparation method is as follows: 1, weighing raw materials; 2, adding distilled water into a reactor, heating up, adding a compound emulsifier, a pH buffer and then part of a mixed vinyl monomer for emulsifying, adding part of an initiator, heating up to react until no reflux exists to obtain a seed emulsion; 3, continuing heating up, dripping off the rest of the mixed vinyl monomer, synchronously adding part of the initiator, after the dripping of the part of the initiator, keeping warm to obtain a core structure emulsion; 4, dripping a mixed acrylate monomer to the core structure emulsion, in the mixed monomer dripping process, adding part of the initiator, after dripping of the part of the initiator, adding the rest of the initiator, keeping warm, then cooling, adding ammonia water, stirring, further cooling, and filtering. The preparation method is applied in the fields of wood veneering, interior decoration, textiles and the like.

Description

technical field [0001] The invention belongs to the field of emulsion preparation; in particular, it relates to a preparation method of polystyrene-acrylate core-shell composite emulsion. Background technique [0002] Polymer emulsion is a synthetic resin product with aqueous solution as the dispersion medium. Because of its simple synthesis, easy operation, and no volatilization of organic components during synthesis and use, it is non-toxic and harmless, and is a green and environmentally friendly industrial product. Therefore, it is widely used in plastic impact modifiers, adhesives, coatings, and flocculants. And fabric sizing agents and finishing agents and other fields. Polyacrylate emulsion (pure acrylic emulsion) is an important type of environment-friendly emulsion. Because of its good physical and chemical properties, film-forming properties, aging resistance, and excellent processing performance, it is widely used in automobiles, furniture, home appliances, and i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08F212/08C08F220/18C08F220/14C08F220/06C08F2/26C08F2/30
Inventor 李志国白龙顾继友
Owner NORTHEAST FORESTRY UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com